Objectives: This study analyzed the physical-chemical behavior of 2 bulk fill resin composites (BFCs; Filtek Bulk Fill [FBF], and Tetric-N-Ceram Bulk Fill [TBF]) used in 2- and 4-mm increments and compared them with a conventional resin composite (Filtek Z250). Materials and Methods: Flexural strength and elastic modulus were evaluated by using a 3-point bending test. Knoop hardness was measured at depth areas 0–1, 1–2, 2–3, and 3–4 mm. The translucency parameter was measured using an optical spectrophotometer. Real-time polymerization kinetics was analyzed using Fourier transform infrared spectroscopy. Results: Flexural strength was similar among the materials, while TBF showed lower elastic modulus (Z250: 6.6 ± 1.3, FBF: 6.4 ± 0.9, TBF: 4.3 ± 1.3). The hardness of Z250 was similar only between 0–1 mm and 1–2 mm. Both BFCs had similar hardness until 2–3 mm, and showed significant decreases at 3–4 mm (FBF: 33.45 ± 1.95 at 0–1 mm to 23.19 ± 4.32 at 3–4 mm, TBF: 23.17 ± 2.51 at 0–1 mm to 15.11 ± 1.94 at 3–4 mm). The BFCs showed higher translucency than Z250. The polymerization kinetics of all the materials were similar at 2-mm increments. At 4-mm, only TBF had a similar degree of conversion compared with 2 mm. Conclusions: The BFCs tested had similar performance compared to the conventional composite when used in up to 2-mm increments. When the increment was thicker, the BFCs were properly polymerized only up to 3 mm.
Abstract
Objectives: This study analyzed the physical-chemical behavior of 2 bulk fill resin composites (BFCs; Filtek Bulk Fill [FBF], and Tetric-N-Ceram Bulk Fill [TBF]) used in 2- and 4-mm increments and compared them with a conventional resin composite (Filtek Z250). Materials and Methods: Flexural strength and elastic modulus were evaluated by using a 3-point bending test. Knoop hardness was measured at depth areas 0–1, 1–2, 2–3, and 3–4 mm. The translucency parameter was measured using an optical spectrophotometer. Real-time polymerization kinetics was analyzed using Fourier transform infrared spectroscopy. Results: Flexural strength was similar among the materials, while TBF showed lower elastic modulus (Z250: 6.6 ± 1.3, FBF: 6.4 ± 0.9, TBF: 4.3 ± 1.3). The hardness of Z250 was similar only between 0–1 mm and 1–2 mm. Both BFCs had similar hardness until 2–3 mm, and showed significant decreases at 3–4 mm (FBF: 33.45 ± 1.95 at 0–1 mm to 23.19 ± 4.32 at 3–4 mm, TBF: 23.17 ± 2.51 at 0–1 mm to 15.11 ± 1.94 at 3–4 mm). The BFCs showed higher translucency than Z250. The polymerization kinetics of all the materials were similar at 2-mm increments. At 4-mm, only TBF had a similar degree of conversion compared with 2 mm. Conclusions: The BFCs tested had similar performance compared to the conventional composite when used in up to 2-mm increments. When the increment was thicker, the BFCs were properly polymerized only up to 3 mm.
참고문헌 (49)
- Garcia D, "Polymerization shrinkage and depth of cure of bulk fill flowable composite resins", Oper Dent, 39, pp.441~448 (2014)
- Orłowski M, "Evaluation of marginal integrity of four bulk-fill dental composite materials: in vitro study", Sci World J, 2015, pp.701262~ (2015)
- Ferracane JL, "Resin composite--state of the art", Dent Mater, 27, pp.29~38 (2011)
- Benetti AR, "Bulk-fill resin composites: polymerization contraction, depth of cure, and gap formation", Oper Dent, 40, pp.190~200 (2015)
- Krämer N, "Light curing of resin-based composites in the LED era", Am J Dent, 21, pp.135~142 (2008)
- Corral Núñez C, "Revisión del estado actual de resinas compuestas bulk-fill", Rev Fac Odontol Univ Antioq, 27, pp.177~196 (2015)
- Ferracane JL, "Academy of dental materials guidance-resin composites: part II-technique sensitivity (handling, polymerization, dimensional changes)", Dent Mater, 33, pp.1171~1191 (2017)
- Nascimento AS, "Marginal microleakage in Bulk Fill resins", Rev Odontol UNESP, 45, pp.327~331 (2016)
- Al-Harbi F, "Marginal integrity of bulk versus incremental fill class II composite restorations", Oper Dent, 41, pp.146~156 (2016)
- El-Damanhoury H, "Polymerization shrinkage stress kinetics and related properties of bulk-fill resin composites", Oper Dent, 39, pp.374~382 (2014)
- Rengo C, "Marginal leakage of bulk fill composites in class II restorations: a microCT and digital microscope analysis", Int J Adhes Adhes, 60, pp.123~129 (2015)
- Ilie N, "Bulk-fill resin-based composites: an in vitro assessment of their mechanical performance", Oper Dent, 38, pp.618~625 (2013)
- Swift EJ Jr, "Critical appraisal: bulk-fill composites, part I", J Esthet Restor Dent, 27, pp.176~179 (2015)
- Khamverdi Z, "Comparative evaluation of microleakage in class V composite resin restorations using two bulk filled resin composites and one conventional composite (grandio)", Ann Dent Spec, 6, pp.17~22 (2018)
- Ilie N, "Curing behaviour of high-viscosity bulk-fill composites", J Dent, 42, pp.977~985 (2014)
- Czasch P, "In vitro comparison of mechanical properties and degree of cure of bulk fill composites", Clin Oral Investig, 17, pp.227~235 (2013)
- Li X, "Curing profile of bulk-fill resin-based composites", J Dent, 43, pp.664~672 (2015)
- International Organization for Standardization, "ISO 4049:2009 Dentistry — Polymer based restorative materials", International Organization for Standardization, ~ (2009)
- de Araújo CS, "Composite resin microhardness: the influence of light curing method, composite shade, and depth of cure", J Contemp Dent Pract, 9, pp.43~50 (2008)
- Sharma G, "The CIEDE2000 color-difference formula: implementation notes, supplementary test data, and mathematical observations", Color Res Appl, 30, pp.21~30 (2005)
- Herrera-González AM, "Analysis of double bond conversion of photopolymerizable monomers by FTIR-ATR spectroscopy", J Chem Educ, 96, pp.1786~1789 (2019)
- Moraes RR, "Impact of immediate and delayed light activation on self-polymerization of dual-cured dental resin luting agents", Acta Biomater, 5, pp.2095~2100 (2009)
- Flury S, "Depth of cure of resin composites: Is the ISO 4049 method suitable for bulk fill materials?", Dent Mater, 28, pp.521~528 (2012)
- Masouras K, "Correlation of filler content and elastic properties of resin-composites", Dent Mater, 24, pp.932~939 (2008)
- Son SA, "How light attenuation and filler content affect the microhardness and polymerization shrinkage and translucency of bulk-fill composites?", Clin Oral Investig, 21, pp.559~565 (2017)
- Marovic D, "Monomer conversion and shrinkage force kinetics of low-viscosity bulk-fill resin composites", Acta Odontol Scand, 73, pp.474~480 (2015)
- Leprince JG, "Physico-mechanical characteristics of commercially available bulk-fill composites", J Dent, 42, pp.993~1000 (2014)
- Cuevas-Suárez CE, "Examining the effect of radiant exposure on commercial photopolimerizable dental resin composites", Dent J (Basel), 6, pp.55~ (2018)
- Abed YA, "Degree of conversion and surface hardness of bulk-fill composite versus incremental-fill composite", Tanta Dent J, 12, pp.71~80 (2015)
- Camassari JR, "Physical-mechanical properties of bulk fill composites submitted to biodegradation by Streptococcus mutans", Braz Dent J, 31, pp.431~439 (2020)
- Vojdani M, "Effects of aluminum oxide addition on the flexural strength, surface hardness, and roughness of heat-polymerized acrylic resin", J Dent Sci, 7, pp.238~244 (2012)
- Tchorz JP, "Microhardness of composite materials with different organic phases in deep class II cavities: an in vitro study", Oper Dent, 36, pp.502~511 (2011)
- Van Ende A, "Bulk-fill composites: a review of the current literature", J Adhes Dent, 19, pp.95~109 (2017)
- Cidreira Boaro LC, "Clinical performance and chemical-physical properties of bulk fill composites resin -a systematic review and meta-analysis", Dent Mater, 35, pp.e249~e264 (2019)
- Tomaszewska IM, "Bulk fill restoratives: to cap or not to cap--That is the question?", J Dent, 43, pp.309~316 (2015)
- Bucuta S, "Light transmittance and micro-mechanical properties of bulk fill vs. conventional resin based composites", Clin Oral Investig, 18, pp.1991~2000 (2014)
- Lee YK, "Influence of filler on the difference between the transmitted and reflected colors of experimental resin composites", Dent Mater, 24, pp.1243~1247 (2008)
- Shortall AC, Palin WM, Burtscher P, "Refractive index mismatch and monomer reactivity influence composite curing depth", J Dent Res, 87, pp.84~88 (2008)
- Fujita K, "Effect of base monomer's refractive index on curing depth and polymerization conversion of photo-cured resin composites", Dent Mater J, 24, pp.403~408 (2005)
- Garoushi S, "Influence of increment thickness on light transmission, degree of conversion and micro hardness of bulk fill composites", Odontology, 104, pp.291~297 (2016)
- Leprince JG, "Progress in dimethacrylate-based dental composite technology and curing efficiency", Dent Mater, 29, pp.139~156 (2013)
- Fronza BM, "Monomer conversion, microhardness, internal marginal adaptation, and shrinkage stress of bulk-fill resin composites", Dent Mater, 31, pp.1542~1551 (2015)
- Radebner J, "Tetraacylgermanes: highly efficient photoinitiators for visible-light-induced free-radical polymerization", Angew Chem Int Ed Engl, 56, pp.3103~3107 (2017)
- Al-Ahdal K, "Polymerization kinetics and impact of post polymerization on the degree of conversion of bulk-fill resin-composite at clinically relevant depth", Dent Mater, 31, pp.1207~1213 (2015)
- Al-Mansour K, "Curing depth of bulk-fill composites-an in-vitro study", Pak Oral Dent J, 35, pp.270~274 (2015)
- Yap AU, "Depth of cure of contemporary bulk-fill resin-based composites", Dent Mater J, 35, pp.503~510 (2016)
- Price RB, "Light energy transmission through cured resin composite and human dentin", Quintessence Int, 31, pp.659~667 (2000)
- Price RB, "Effect of light source and specimen thickness on the surface hardness of resin composite", Am J Dent, 15, pp.47~53 (2002)
- Moszner N, "Benzoyl germanium derivatives as novel visible light photoinitiators for dental materials", Dent Mater, 24, pp.901~907 (2008)