Effect of resin thickness on the microhardness and optical properties of bulk-fill resin composites
2
조회
0
다운로드
8
인용
0
참고문헌
키워드
초록
Objectives: This study evaluated the effects of the resin thickness on the microhardness and optical properties of bulk-fill resin composites. Materials and Methods: Four bulk-fill (Venus Bulk Fill, Heraeus Kulzer; SDR, Dentsply Caulk; Tetric N-Ceram Bulk Fill, Ivoclar vivadent; SonicFill, Kerr) and two regular resin composites (Charisma flow, Heraeus Kulzer; Tetric N-Ceram, Ivoclar vivadent) were used. Sixty acrylic cylindrical molds were prepared for each thickness (2, 3 and 4 mm). The molds were divided into six groups for resin composites. The microhardness was measured on the top and bottom surfaces, and the colors were measured using Commission Internationale d’Eclairage (CIE) L*a*b* system. Color differences according to the thickness and translucency parameters and the correlations between the microhardness and translucency parameter were analyzed. The microhardness and color differences were analyzed by ANOVA and Scheffe’s post hoc test, and a student t-test, respectively. The level of significance was set to α = 0.05. Results: The microhardness decreased with increasing resin thickness. The bulk-fill resin composites showed a bottom/ top hardness ratio of almost 80% or more in 4 mm thick specimens. The highest translucency parameter was observed in Venus Bulk Fill. All resin composites used in this study except for Venus Bulk Fill showed linear correlations between the microhardness and translucency parameter according to the thickness. Conclusions: Within the limitations of this study, the bulk-fill resin composites used in this study can be placed and cured properly in the 4 mm bulk.
Abstract
Objectives: This study evaluated the effects of the resin thickness on the microhardness and optical properties of bulk-fill resin composites. Materials and Methods: Four bulk-fill (Venus Bulk Fill, Heraeus Kulzer; SDR, Dentsply Caulk; Tetric N-Ceram Bulk Fill, Ivoclar vivadent; SonicFill, Kerr) and two regular resin composites (Charisma flow, Heraeus Kulzer; Tetric N-Ceram, Ivoclar vivadent) were used. Sixty acrylic cylindrical molds were prepared for each thickness (2, 3 and 4 mm). The molds were divided into six groups for resin composites. The microhardness was measured on the top and bottom surfaces, and the colors were measured using Commission Internationale d’Eclairage (CIE) L*a*b* system. Color differences according to the thickness and translucency parameters and the correlations between the microhardness and translucency parameter were analyzed. The microhardness and color differences were analyzed by ANOVA and Scheffe’s post hoc test, and a student t-test, respectively. The level of significance was set to α = 0.05. Results: The microhardness decreased with increasing resin thickness. The bulk-fill resin composites showed a bottom/ top hardness ratio of almost 80% or more in 4 mm thick specimens. The highest translucency parameter was observed in Venus Bulk Fill. All resin composites used in this study except for Venus Bulk Fill showed linear correlations between the microhardness and translucency parameter according to the thickness. Conclusions: Within the limitations of this study, the bulk-fill resin composites used in this study can be placed and cured properly in the 4 mm bulk.
참고문헌 (19)
- Lassila LV, "Translucency of flowable bulk-filling composites of various thickness", Chin J Dent Res, 15, pp.31~35 (2012)
- Ilie N, "Bulk-fill resin-based composites: an in vitro assessment of their mechanical performance", Oper Dent, 38, pp.618~625 (2013)
- Czasch P, "In vitro comparison of mechanical properties and degree of cure of bulk fill composites", Clin Oral Investig, 17, pp.227~235 (2013)
- Ilie N, "Influence of various irradiation processes on the mechanical properties and polymerisation kinetics of bulk-fill resin based composites", J Dent, 41, pp.695~702 (2013)
- Flury S, "Depth of cure of resin composites: is the ISO 4049 method suitable for bulk fill materials?", Dent Mater, 28, pp.521~528 (2012)
- Tanthanuch S, "Optimal depth of cure for nanohybrid resin composite using quartz tungsten halogen and new high intensity lightemitting diode curing units", Gen Dent, 61, pp.e14~e17 (2013)
- Finan L, "The influence of irradiation potential on the degree of conversion and mechanical properties of two bulk-fill flowable resin composite base materials", Dent Mater, 29, pp.906~912 (2013)
- Price RB, "Effect of light source and specimen thickness on the surface hardness of resin composites", Am J Dent, 15, pp.47~53 (2002)
- Ilie N, "Investigations on a methacrylate-based flowable composite based on the SDRTM technology", Dent Mater, 27, pp.348~355 (2011)
- Bouschlicher MR, "Correlation of bottom-to-top surface microhardness and conversion ratios for a variety of resin composite compositions", Oper Dent, 29, pp.698~704 (2004)
- Moore BK, "Depth of cure of dental resin composites: ISO 4049depth and microhardness of types of materials and shades", Oper Dent, 33, pp.408~412 (2008)
- Yeh CL, "Color of selected shades of composites by reflection spectrophotometry", J Dent Res, 61, pp.1176~1179 (1982)
- Inokoshi S, "Opacity and color changes of tooth-colored restorative materials", Oper Dent, 21, pp.73~80 (1996)
- Miyagawa Y, "Optical properties of direct restorative materials", J Dent Res, 60, pp.890~894 (1981)
- Johnston WM, "Color and translucency changes during and after curing of esthetic restorative materials", Dent Mater, 13, pp.89~97 (1997)
- Kim IJ, "Changes in color and color parameters of dental resin composites after polymerization", J Biomed Mater Res B Appl Biomater, 80, pp.541~546 (2007)
- Lee YK, "Influence of filler on the difference between the transmitted and reflected colors of experimental resin composites", Dent Mater, 24, pp.1243~1247 (2008)
- Campbell PM, "Light scattering and gloss of an experimental quartz-filled composite", J Dent Res, 65, pp.892~894 (1986)
- Kim SJ, "Translucency and masking ability of various opaque-shade composite resins", J Dent, 37, pp.102~107 (2009)