Objectives: This study examined the influence of the resin thickness on the polymerization of silorane- and methacrylate-based composites. Materials and Methods: One silorane-based (Filtek P90, 3M ESPE) and two methacrylate-based (Filtek Z250 and Z350, 3M ESPE) composite resins were used. The number of photons were detected using a photodiode detector at the different thicknesses (thickness, 1, 2 and 3 mm) specimens. The microhardness of the top and bottom surfaces was measured (n = 15) using a Vickers hardness with 200 gf load and 15 sec dwell time conditions. The degree of conversion (DC) of the specimens was determined using Fourier transform infrared spectroscopy (FTIR). Scratched powder of each top and bottom surface of the specimen dissolved in ethanol for transmission FTIR spectroscopy. The refractive index was measured using a Abbe-type refractometer. To measure the polymerization shrinkage, a linometer was used. The results were analyzed using two-way ANOVA and Tukey’s test at p < 0.05 level. Results: The silorane-based resin composite showed the lowest filler content and light attenuation among the specimens. P90 showed the highest values in the DC and the lowest microhardness at all depth. In the polymerization shrinkage, P90 showed a significantly lower shrinkage than the rest two resin products (p < 0.05). P90 showed a significantly lower refractive index than the remaining two resin products (p < 0.05). Conclusions: DC, microhardness, polymerization rate and refractive index linearly decreased as specimen thickness linearly increased. P90 showed much less polymerization shrinkage compared to other specimens. P90, even though achieved the highest DC, showed the lowest microhardness and refractive index.
Abstract
Objectives: This study examined the influence of the resin thickness on the polymerization of silorane- and methacrylate-based composites. Materials and Methods: One silorane-based (Filtek P90, 3M ESPE) and two methacrylate-based (Filtek Z250 and Z350, 3M ESPE) composite resins were used. The number of photons were detected using a photodiode detector at the different thicknesses (thickness, 1, 2 and 3 mm) specimens. The microhardness of the top and bottom surfaces was measured (n = 15) using a Vickers hardness with 200 gf load and 15 sec dwell time conditions. The degree of conversion (DC) of the specimens was determined using Fourier transform infrared spectroscopy (FTIR). Scratched powder of each top and bottom surface of the specimen dissolved in ethanol for transmission FTIR spectroscopy. The refractive index was measured using a Abbe-type refractometer. To measure the polymerization shrinkage, a linometer was used. The results were analyzed using two-way ANOVA and Tukey’s test at p < 0.05 level. Results: The silorane-based resin composite showed the lowest filler content and light attenuation among the specimens. P90 showed the highest values in the DC and the lowest microhardness at all depth. In the polymerization shrinkage, P90 showed a significantly lower shrinkage than the rest two resin products (p < 0.05). P90 showed a significantly lower refractive index than the remaining two resin products (p < 0.05). Conclusions: DC, microhardness, polymerization rate and refractive index linearly decreased as specimen thickness linearly increased. P90 showed much less polymerization shrinkage compared to other specimens. P90, even though achieved the highest DC, showed the lowest microhardness and refractive index.
참고문헌 (36)
- Bowen RL., "Use of epoxy resins in restorative materials", J Dent Res, 35, pp.360~369 (1956)
- Eick JD, "Polymerization shrinkage of posterior composite resins and its possible influence on postoperative sensitivity", Quintessence Int, 17, pp.103~111 (1986)
- Sakaguchi RL, "Effects of polymerization contraction in composite restorations", J Dent, 20, pp.178~182 (1992)
- Eick JD, "Properties of silorane-based dental resins and composites containing a stress-reducing monomer", Dent Mater, 23, pp.1011~1017 (2007)
- Lien W, "Physical properties of a new silorane-based restorative system", Dent Mater, 26, pp.337~344 (2010)
- Papadogiannis D, "Setting characteristics and cavity adaptation of low-shrinking resin composites", Dent Mater, 25, pp.1509~1516 (2009)
- Weinmann W, "Siloranes in dental composites", Dent Mater, 21, pp.68~74 (2005)
- Ilie N, "Silorane-based dental composite: behavior and abilities", Dent Mater J, 25, pp.445~454 (2006)
- Bala O, "Barcoll hardness of different resin-based composites cured by halogen or light emitting diode (LED)", Oper Dent, 30, pp.69~74 (2005)
- Rueggeberg FA, "Factors affecting cure at depths within light-activated resin composites", Am J Dent, 6, pp.91~95 (1993)
- Soh MS, "The effectiveness of cure of LED and halogen curing lights at varying cavity depths", Oper Dent, 28, pp.707~715 (2003)
- Emami N, "How filler properties, filler fraction, sample thickness and light source affect light attenuation in particulate filled resin composites", Dent Mater, 21, pp.721~730 (2005)
- Ferracane JL., "Correlation between hardness and degree of conversion during the setting reaction of unfilled dental restorative resins", Dent Mater, 1, pp.11~14 (1985)
- Visvanathan A, "The influence of curing times and light curing methods on the polymerization shrinkage stress of a shrinkage-optimized composite with hybrid-type prepolymer fillers", Dent Mater, 23, pp.777~784 (2007)
- Yap AU., "Effectiveness of polymerization in composite restoratives claiming bulk placement: impact of cavity depth and exposure time", Oper Dent, 25, pp.113~120 (2000)
- Chen YC, "A pilot study of a simple photon migration model for predicting depth of cure in dental composite", Dent Mater, 21, pp.1075~1086 (2005)
- Schneider LF, "Influence of photoinitiator type on the rate of polymerization, degree of conversion, hardness and yellowing of dental resin composites", Dent Mater, 24, pp.1169~1177 (2008)
- Bala O, "Effect of LED and halogen light curing on polymerization of resin-based composites", J Oral Rehabil, 32, pp.134~140 (2005)
- Tarle Z, "Composite conversion and temperature rise using a conventional, plasma arc, and an experimental blue LED curing unit", J Oral Rehabil, 29, pp.662~667 (2002)
- Palin WM, "Monomer conversion versus flexure strength of a novel dental composite", J Dent, 31, pp.341~351 (2003)
- Kusgoz A, "Silorane-based composite: depth of cure, surface hardness, degree of conversion, and cervical microleakage in Class II cavities", J Esthet Restor Dent, 23, pp.324~335 (2011)
- Palin WM, "The reliability in flexural strength testing of a novel dental composite", J Dent, 31, pp.549~557 (2003)
- D'Alpino PH, "Methacrylate- and silorane-based composite restorations: hardness, depth of cure and interfacial gap formation as a function of the energy dose", Dent Mater, 27, pp.1162~1169 (2011)
- Rueggeberg FA, "Calibration of FTIR conversion analysis of contemporary dental resin composites", Dent Mater, 6, pp.241~249 (1990)
- Torres SA, "qDegree of conversion and hardness of a silorane-based composite resin: effect of light-curing unit and depth", 39, pp.137~146 (2014)
- Guiraldo RD, "Comparison of silorane and methacrylate-based composite resins on the curing light transmission", Braz Dent J, (21), pp.538~542 (2010)
- Andrzejewska E, "The role of oxygen in camphorquinone-initiated photopolymerization", Macromol Chem Phys, 199, pp.441~449 (1998)
- Schulze S, "Aspects of the safe storage of acrylic monomers: kinetics of the oxygen consumption", Chem Eng Technol, 21, pp.829~837 (1998)
- Corr AB, "Effect of the increase of energy density on Knoop hardness of dental composites light-cured by conventional QTH, LED and xenon plasma arc", Braz Dent J, 16, pp.218~224 (2005)
- Tilbrook DA, "Photocurable epoxy-polyol matrices for use in dental composites I", Biomaterials, 21, pp.1743~1753 (2000)
- Bechtold J, "Hardness, polymerization depth, and internal adaptation of Class II silorane composite restorations as a function of polymerization protocol", Eur J Dent, 6, pp.133~140 (2012)
- Bouschlicher MR, "Correlation of bottom-to-top surface microhardness and conversion ratios for a variety of resin composite compositions", Oper Dent, 29, pp.698~704 (2004)
- Eick JD, "In vitro biocompatibility of oxirane", polyol dental composites with promising physical properties, 2002, pp.18, 413~421
- Fujita K, "Effect of base monomer's refractive index on curing depth and polymerization conversion of photo-cured resin composites", Dent Mater J, 24, pp.403~408 (2005)
- Odian G., "Principles of polymerization" (2004), John Wiley
- Shibayama M, "Real-time dynamic light scattering on gelation and vitrification", Polymer, 46, pp.2381~2388 (2005)