The effect of thermocycling on the degree of conversion and mechanical properties of a microhybrid dental resin composite
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Objective The purpose of this study was to investigate the degree of conversion (DC) and mechanical properties of a microhybrid Filtek Z250 (3M ESPE) resin composite after aging. Method The specimens were fabricated using circular molds to investigate Vickers microhardness (Vickers hardness number [VHN]) and DC, and were prepared according to ISO 4049 for flexural strength testing. The initial DC (%) of discs was recorded using attenuated total reflectance-Fourier transforming infrared spectroscopy. The initial VHN of the specimens was measured using a microhardness tester under a load of 300 g for 15 seconds and the flexural strength test was carried out with a universal testing machine (crosshead speed, 0.5 mm/min). The specimens were then subjected to thermocycling in 5°C and 55°C water baths. Properties were assessed after 1,000–10,000 cycles of thermocycling. The surfaces were evaluated using scanning electron microscopy (SEM). Data were analyzed using 1-way analysis of variance followed by the Tukey honest significant difference post hoc test. Results Statistical analysis showed that DC tended to increase up to 4,000 cycles, with no significant changes. VHN and flexural strength values significantly decreased upon thermal cycling when compared to baseline (p < 0.05). However, there was no significant difference between initial and post-thermocycling VHN results at 1,000 cycles. SEM images after aging showed deteriorative changes in the resin composite surfaces. Conclusions The Z250 microhybrid resin composite showed reduced surface microhardness and flexural strength and increased DC after thermocycling.
Abstract
Objective The purpose of this study was to investigate the degree of conversion (DC) and mechanical properties of a microhybrid Filtek Z250 (3M ESPE) resin composite after aging. Method The specimens were fabricated using circular molds to investigate Vickers microhardness (Vickers hardness number [VHN]) and DC, and were prepared according to ISO 4049 for flexural strength testing. The initial DC (%) of discs was recorded using attenuated total reflectance-Fourier transforming infrared spectroscopy. The initial VHN of the specimens was measured using a microhardness tester under a load of 300 g for 15 seconds and the flexural strength test was carried out with a universal testing machine (crosshead speed, 0.5 mm/min). The specimens were then subjected to thermocycling in 5°C and 55°C water baths. Properties were assessed after 1,000–10,000 cycles of thermocycling. The surfaces were evaluated using scanning electron microscopy (SEM). Data were analyzed using 1-way analysis of variance followed by the Tukey honest significant difference post hoc test. Results Statistical analysis showed that DC tended to increase up to 4,000 cycles, with no significant changes. VHN and flexural strength values significantly decreased upon thermal cycling when compared to baseline (p < 0.05). However, there was no significant difference between initial and post-thermocycling VHN results at 1,000 cycles. SEM images after aging showed deteriorative changes in the resin composite surfaces. Conclusions The Z250 microhybrid resin composite showed reduced surface microhardness and flexural strength and increased DC after thermocycling.
참고문헌 (32)
- Anusavice KJ, "Phillips' science of dental materials", pp.2013, Elsevier
- Souza RO, "Conversion degree of indirect resin composites and effect of thermocycling on their physical properties", J Prosthodont, 19, pp.218~225 (2010)[DOI]
- Martos J, "Hydrolytic degradation of composite resins: effects on the microhardness", Mater Res, 6, pp.599~604 (2003)[DOI]
- Toledano M, "Sorption and solubility of resin-based restorative dental materials", J Dent, 31, pp.43~50 (2003)[DOI]
- Ozcan M, "Repair bond strength of microhybrid, nanohybrid and nanofilled resin composites: effect of substrate resin type, surface conditioning and ageing", Clin Oral Investig, 17, pp.1751~1758 (2013)[DOI]
- Chung SM, "Flexural strength of dental composite restoratives: comparison of biaxial and three-point bending test", J Biomed Mater Res B Appl Biomater, 71, pp.278~283 (2004)
- Obici AC, "Degree of conversion of Z250 composite determined by fourier transform infrared spectroscopy: comparison of techniques, storage periods and photo-activation methods", Mater Res, 7, pp.605~610 (2004)[DOI]
- Tonetto MR, "Degree of conversion of polymer-matrix composite assessed by FTIR analysis", J Contemp Dent Pract, 14, pp.76~79 (2013)
- Jafarzadeh TS, "Evaluation of polymerization efficacy in composite resins via FT-IR spectroscopy and vickers microhardness test", J Dent Res Dent Clin Dent Prospects, 9, pp.226~232 (2015)[DOI]
- Goncalves L, "Solubility, salivary sorption and degree of conversion of dimethacrylate-based polymeric matrixes", J Biomed Mater Res B Appl Biomater, 85, pp.320~325 (2008)
- Tosun G, "Effect of light curing units and storage time on the degree of conversion of fissure sealants", Rev Clin Pesqui Odontol, 5, pp.111~119 (2009)
- Pallikari F, "A study of aging in dental composites using IR and Raman spectroscopy", e-Polymers, 4, pp.793~802 (2004)
- Moraes LG, "Infrared spectroscopy: a tool for determination of the degree of conversion in dental composites", J Appl Oral Sci, 16, pp.145~149 (2008)[DOI]
- McCabe JF, "Applied dental materials" (2013), John Wiley & Sons
- de Oliveira JC, "Effect of storage in water and thermocycling on hardness and roughness of resin materials for temporary restorations", Mater Res, 13, pp.355~359 (2010)[DOI]
- International Organization for Standardization, "ISO", TS 11405 Dentistry -- Testing of adhesion to tooth structure. 3rd ed., 2015
- Gale MS, "Thermal cycling procedures for laboratory testing of dental restorations", J Dent, 27, pp.89~99 (1999)[DOI]
- Tabatabaei MH, "Effect of food stimulated liquids and thermocycling on the monomer elution from a nanofilled composite", Open Dent J, 7, pp.62~67 (2013)[DOI]
- Sideridou ID, "Elution study of unreacted Bis-GMA, TEGDMA, UDMA, and Bis-EMA from light-cured dental resins and resin composites using HPLC", J Biomed Mater Res B Appl Biomater, 74, pp.617~626 (2005)
- Durner J, "Correlation of the degree of conversion with the amount of elutable substances in nano-hybrid dental composites", Dent Mater, 28, pp.1146~1153 (2012)[DOI]
- Andrzejewska E, "Photopolymerization kinetics of multifunctional monomers", Prog Polym Sci, 26, pp.605~665 (2001)[DOI]
- Leprince J, "Kinetic study of free radicals trapped in dental resins stored in different environments", Acta Biomater, 5, pp.2518~2524 (2009)[DOI]
- Leprince JG, "Irradiation modes' impact on radical entrapment in photoactive resins", J Dent Res, 89, pp.1494~1498 (2010)[DOI]
- Leprince JG, "Progress in dimethacrylate-based dental composite technology and curing efficiency", Dent Mater, 29, pp.139~156 (2013)[DOI]
- Truffier-Boutry D, "A physico-chemical explanation of the post-polymerization shrinkage in dental resins", Dent Mater, 22, pp.405~412 (2006)[DOI]
- International Organization for Standardization, "ISO 4049 Dentistry -- Polymer-based restorative materials. 4th ed.", International Organization for Standardization, ~ (2015)
- Attar N, "Flow, strength, stiffness and radiopacity of flowable resin composites", J Can Dent Assoc, 69, pp.516~521 (2003)
- Janda R, "The effects of thermocycling on the flexural strength and flexural modulus of modern resin-based filling materials", Dent Mater, 22, pp.1103~1108 (2006)[DOI]
- de Moraes RR, "Hydrolytic stability of dental composites: one-year aging effect on surface roughness and surface", subsurface hardness, 2007, pp.36, 383~387
- Pereira SM, "Thermocycling effect on microhardness of laboratory composite resins", Braz J Oral Sci, 6, pp.1372~1375 (2007)
- Ferracane JL, "Rate of elution of leachable components from composite", Dent Mater, 6, pp.282~287 (1990)[DOI]
- Ferracane JL, "In vitro aging of dental composites in water--effect of degree of conversion, filler volume, and filler", matrix coupling, 1998, pp.42, 465~472