EFFECT OF CROSS-SECTIONAL AREA OF 6 NICKEL-TITANIUM ROTARY INSTRUMENTS ON THE FATIGUE FRACTURE UNDER CYCLIC FLEXURAL STRESS: A FRACTOGRAPHIC ANALYSIS
3
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
This study aimed to assess the influence of different cross-sectional area on the cyclic fatigue fracture of Ni-Ti rotary files using a fatigue tester incorporating cyclical axial movement. Six brands of Ni-Ti rotary files (ISO 30 size with .04 taper) of 10 each were tested: Alpha system (KOMET), HeroShaper (MicroMega), K3 (SybronEndo), Mtwo (VDW), NRT (Mani), and ProFile (Dentsply). A fatigue-tester (Denbotix) was designed to allow cyclic tension and compressive stress on the tip of the instrument. Each file was mounted on a torque controlled motor (Aseptico) using a 1:20 reduction contra-angle and was rotated at 300 rpm with a continuous, 6 mm axial oscillating motion inside an artificial steel canal. The canal had a 60angle and a 5 mm radius of curvature. Instrument fracture was visually detected and the time until fracture was recorded by a digital stop watch. The data were analyzed statistically. Fractographic analysis of all fractured surfaces was performed to determine the fracture modes using a scanning electron microscope. Cross-sectional area at 3 mm from the tip of 3 unused Ni-Ti instruments for each group was calculated using Image-Pro Plus (Imagej 1.34n, NIH). Results showed that NRT and ProFile had significantly longer time to fracture compared to the other groups (p < .05). The cross-sectional area was not significantly associated with fatigue resistance. Fractographycally, all fractured surfaces demonstrated a combination of ductile and brittle fracture. In conclusion, there was no significant relationship between fatigue resistance and the cross-sectional area of Ni-Ti instruments under experimental conditions.
Abstract
This study aimed to assess the influence of different cross-sectional area on the cyclic fatigue fracture of Ni-Ti rotary files using a fatigue tester incorporating cyclical axial movement. Six brands of Ni-Ti rotary files (ISO 30 size with .04 taper) of 10 each were tested: Alpha system (KOMET), HeroShaper (MicroMega), K3 (SybronEndo), Mtwo (VDW), NRT (Mani), and ProFile (Dentsply). A fatigue-tester (Denbotix) was designed to allow cyclic tension and compressive stress on the tip of the instrument. Each file was mounted on a torque controlled motor (Aseptico) using a 1:20 reduction contra-angle and was rotated at 300 rpm with a continuous, 6 mm axial oscillating motion inside an artificial steel canal. The canal had a 60angle and a 5 mm radius of curvature. Instrument fracture was visually detected and the time until fracture was recorded by a digital stop watch. The data were analyzed statistically. Fractographic analysis of all fractured surfaces was performed to determine the fracture modes using a scanning electron microscope. Cross-sectional area at 3 mm from the tip of 3 unused Ni-Ti instruments for each group was calculated using Image-Pro Plus (Imagej 1.34n, NIH). Results showed that NRT and ProFile had significantly longer time to fracture compared to the other groups (p < .05). The cross-sectional area was not significantly associated with fatigue resistance. Fractographycally, all fractured surfaces demonstrated a combination of ductile and brittle fracture. In conclusion, there was no significant relationship between fatigue resistance and the cross-sectional area of Ni-Ti instruments under experimental conditions.
참고문헌 (22)
- Esposito PT, "A comparison of canal preparation with nickel-titanium and stainless steel instruments", J Endod, 21, pp.173~176 (1995)
- Peters OA, "Current challenges and concepts in the preparation of root canal systems: a review", J Endod, 30, pp.559~567 (2004)
- Kosa DA, "An analysis of canal centering using mechanical instrumentation techniques", J Endod, 25, pp.441~445 (1999)
- Bahia MGA, "Influence of simulated clinical use on the torsional behavior of nickeltitanium rotary endodontic instruments", Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 101, pp.675~680 (2006)
- Pruett JP, "Cyclic fatigue testing of nickel-titanium endodontic instruments", J Endod, 23, pp.77~85 (1997)
- Sattapan B, "Defects in rotary nickel-titanium files after clinical use", J Endod, 26, pp.161~165 (2000)
- Turpin YL, "Impact of two theoretical cross-sections on torsional and bending stresses of nickel-titanium root canal instrument models", J Endod, 26, pp.414~417 (2000)
- Xu X, "Comparative study of torsional and bending properties for six models of nickel-titanium root canal instruments with different cross-sections", J Endod, 32, pp.372~375 (2006)
- Berutti E, "Comparative analysis of torsional and bending stresses in two mathematical models of nickel-titanium rotary instruments: ProTaper versus ProFile", J Endod, 29, pp.15~19 (2003)
- Cheung GS, "Low-cycle fatigue of Ni-Ti rotary instruments of various cross-sectional shapes", Int Endod J, 40, pp.626~632 (2007)
- 신유미, "전동식 니켈 티타늄 파일의 표면 결함 및 단면 형태가 반복응력 하에서 피로 파절에 미치는 영향", 대한치과보존학회지, 29(3), pp.267~272 (2004), 대한치과보존학회
- 김재관, "수종의 Niti 전동 파일 단면 형태 비교 및 pecking motion의 사용방법이 피로 파절에 미치는 영향", 대한치과보존학회지, 31(2), pp.96~102 (2006), 대한치과보존학회
- Haikel Y, "Dynamic and cyclic fatigue of engine-driven rotary nickel-titanium endodontic instruments", J Endod, 25, pp.434~440 (1999)
- Li UM, "Cyclic fatigue of endodontic nickel titanium rotary instruments: Static and dynamic tests", J Endod, 28, pp.448~451 (2002)
- Dederich DN, "The effects of cyclical axial motion on rotary endodontic instrument fatigue", Oral Surg Oral Med Oral Pathol, 61, pp.192~196 (1986)
- Dieter GE, "Mechanical metallurgy", pp.119~ (1986), McGraw-Hill
- Sch¨afer E, "Bending properties of rotary nickel-titanium instruments", Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 96, pp.757~763 (2003)
- Ruddle CL, "Nickel-titanium rotary systems: review of existing instruments and geometries", Dent Today, 19, pp.86~95 (2000)
- Yao JH, "Cyclic fatigue of three types of rotary nickel-titanium files in a dynamic model", J Endod, 32, pp.55~65 (2006)
- Tripi TR, "Cyclic fatigue of different nickel-titanium endodontic rotary instruments", Oral Surg Oral Med Oral Pathol Oral radiol Endod, 102, pp.106~114 (2006)
- Hayashi Y, "Phase transformation behavior and bending properties of hybrid nickel-titanium rotary endodontic instruments", Int Endod J, 40, pp.247~253 (2007)
- 구재훈, "만곡된 레진 모형 근관에서 4종의 엔진 구동형 니켈-티타늄 기구의 근관 중심율 유지 능력", 대한치과보존학회지, 31(2), pp.113~118 (2006), 대한치과보존학회