Comparison of the cyclic fatigue resistance of VDW.ROTATE, TruNatomy, 2Shape, and HyFlex CM nickel-titanium rotary files at body temperature
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Objectives: This study aims to compare the cyclic fatigue resistance of VDW.ROTATE, TruNatomy, 2Shape, and HyFlex CM nickel-titanium (NiTi) rotary files at body temperature. Materials and Methods: In total, 80 VDW.ROTATE (25/0.04), TruNatomy (26/0.04), 2Shape (25/0.04), and HyFlex CM (25/0.04) NiTi rotary files (n = 20 in each group) were subjected to static cyclic fatigue testing at body temperature (37°C) in stainless-steel artificial canals prepared according to the size and taper of the instruments until fracture occurred. The number of cycles to fracture (NCF) was calculated, and the lengths of the fractured fragments were measured. The data were statistically analyzed using a 1-way analysis of variance and post hoc Tamhane tests at the 5% significance level (p < 0.05). Results: There were significant differences in the cyclic fatigue resistance among the groups (p < 0.05), with the highest to lowest NCF values of the files as follows: VDW.ROTATE, HyFlex CM, 2Shape, and TruNatomy. There was no significant difference in the lengths of the fractured fragments among the groups. The scanning electron microscope images of the files revealed typical characteristics of fracture due to cyclic fatigue. Conclusions: The VDW.ROTATE files had the highest cyclic fatigue resistance, and the TruNatomy and 2Shape files had the lowest cyclic fatigue resistance in artificial canals at body temperature.
Abstract
Objectives: This study aims to compare the cyclic fatigue resistance of VDW.ROTATE, TruNatomy, 2Shape, and HyFlex CM nickel-titanium (NiTi) rotary files at body temperature. Materials and Methods: In total, 80 VDW.ROTATE (25/0.04), TruNatomy (26/0.04), 2Shape (25/0.04), and HyFlex CM (25/0.04) NiTi rotary files (n = 20 in each group) were subjected to static cyclic fatigue testing at body temperature (37°C) in stainless-steel artificial canals prepared according to the size and taper of the instruments until fracture occurred. The number of cycles to fracture (NCF) was calculated, and the lengths of the fractured fragments were measured. The data were statistically analyzed using a 1-way analysis of variance and post hoc Tamhane tests at the 5% significance level (p < 0.05). Results: There were significant differences in the cyclic fatigue resistance among the groups (p < 0.05), with the highest to lowest NCF values of the files as follows: VDW.ROTATE, HyFlex CM, 2Shape, and TruNatomy. There was no significant difference in the lengths of the fractured fragments among the groups. The scanning electron microscope images of the files revealed typical characteristics of fracture due to cyclic fatigue. Conclusions: The VDW.ROTATE files had the highest cyclic fatigue resistance, and the TruNatomy and 2Shape files had the lowest cyclic fatigue resistance in artificial canals at body temperature.
참고문헌 (33)
- Clark D, "Modern molar endodontic access and directed dentin conservation", Dent Clin North Am, 54, pp.249~273 (2010)
- Plotino G, "Fracture strength of endodontically treated teeth with different access cavity designs", J Endod, 43, pp.995~1000 (2017)
- Plotino G, "Influence of size and taper of basic root canal preparation on root canal cleanliness : a scanning electron microscopy study", Int Endod J, 52, pp.343~351 (2019)
- Filizola de Oliveira DJ, "Changes in geometry and transportation of root canals with severe curvature prepared by different heat-treated nickel-titanium instruments : a micro-computed tomographic study", J Endod, 45, pp.768~773 (2019)
- Lang H, "Impact of endodontic treatments on the rigidity of the root", J Dent Res, 85, pp.364~368 (2006)
- Sabeti M, "Impact of access cavity design and root canal taper on fracture resistance of endodontically treated teeth : an ex vivo investigation", J Endod, 44, pp.1402~1406 (2018)
- "ROTATE Brochure" (2019)[URL]
- "TruNatomy Brochure" (2019)[URL]
- Uslu G, "Cyclic fatigue resistance of R-Pilot, HyFlex EDM and PathFile nickel-titanium glide path files in artificial canals with double (S-shaped) curvature", Int Endod J, 51, pp.584~589 (2018)
- Özyürek T, "Comparison of cyclic fatigue resistance and bending properties of two reciprocating nickel-titanium glide path files", Int Endod J, 51, pp.1047~1052 (2018)
- Huang X, "Fatigue resistance of nickel-titanium instruments exposed to high-concentration hypochlorite", J Endod, 43, pp.1847~1851 (2017)
- Plotino G, "Influence of size and taper of artificial canals on the trajectory of NiTi rotary instruments in cyclic fatigue studies", Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 109, pp.e60~e66 (2010)
- Plotino G, "Cyclic fatigue of Reciproc and WaveOne reciprocating instruments", Int Endod J, 45, pp.614~618 (2012)
- Shen Y, "Metallurgical characterization of controlled memory wire nickel-titanium rotary instruments", J Endod, 37, pp.1566~1571 (2011)
- de Vasconcelos RA, "Evidence for reduced fatigue resistance of contemporary rotary instruments exposed to body temperature", J Endod, 42, pp.782~787 (2016)
- Plotino G, "Influence of temperature on cyclic fatigue resistance of ProTaper Gold and ProTaper Universal rotary files", J Endod, 43, pp.200~202 (2017)
- Alfawaz H, "Effects of sodium hypochlorite concentration and temperature on the cyclic fatigue resistance of heat-treated nickel-titanium rotary instruments", J Endod, 44, pp.1563~1566 (2018)
- Klymus ME, "Effect of temperature on the cyclic fatigue resistance of thermally treated reciprocating instruments", Clin Oral Investig, 23, pp.3047~3052 (2019)
- Plotino G, "A review of cyclic fatigue testing of nickel-titanium rotary instruments", J Endod, 35, pp.1469~1476 (2009)
- Wan J, "A comparison of cyclic fatigue resistance in reciprocating and rotary nickel-titanium instruments", Aust Endod J, 37, pp.122~127 (2011)
- Keleş A, "Influence of static and dynamic cyclic fatigue tests on the lifespan of four reciprocating systems at different temperatures", Int Endod J, 52, pp.880~886 (2019)
- Gambarini G, "Fatigue resistance of engine-driven rotary nickel-titanium instruments produced by new manufacturing methods", J Endod, 34, pp.1003~1005 (2008)
- Gambarini G, "Mechanical properties of nickel-titanium rotary instruments produced with a new manufacturing technique", Int Endod J, 44, pp.337~341 (2011)
- Tripi TR, "Cyclic fatigue of different nickel-titanium endodontic rotary instruments", Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 102, pp.e106~e114 (2006)
- Grande NM, "Cyclic fatigue resistance and three-dimensional analysis of instruments from two nickel-titanium rotary systems", Int Endod J, 39, pp.755~763 (2006)
- Cheung GS, "A numerical method for predicting the bending fatigue life of NiTi and stainless steel root canal instruments", Int Endod J, 44, pp.357~361 (2011)
- Plotino G, "Cyclic fatigue of NiTi rotary instruments in a simulated apical abrupt curvature", Int Endod J, 43, pp.226~230 (2010)
- Kaval ME, "Comparative evaluation of cyclic fatigue resistance of four different nickel-titanium rotary files with different cross-sectional designs and alloy properties", Clin Oral Investig, 21, pp.1527~1530 (2017)
- Staffoli S, "Influence of environmental temperature, heat-treatment and design on the cyclic fatigue resistance of three generations of a single-file nickel-titanium rotary instrument", Odontology, 107, pp.301~307 (2019)
- Lopes HP, "Fatigue life of Reciproc and Mtwo instruments subjected to static and dynamic tests", J Endod, 39, pp.693~696 (2013)
- Özyürek T, "Cyclic fatigue resistances of Hyflex EDM, WaveOne gold, Reciproc blue and 2shape NiTi rotary files in different artificial canals", Odontology, 106, pp.408~413 (2018)
- Capar ID, "Comparison of the cyclic fatigue resistance of 5 different rotary pathfinding instruments made of conventional nickel-titanium wire, M-wire, and controlled memory wire", J Endod, 41, pp.535~538 (2015)
- Pedullà E, "Cyclic fatigue resistance of two nickel-titanium rotary instruments in interrupted rotation", Int Endod J, 50, pp.194~201 (2017)