Comparison of the cyclic fatigue resistance of One Curve, F6 Skytaper, Protaper Next, and Hyflex CM endodontic files
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Objectives: This study compared the cyclic fatigue resistance of One Curve (C wire) and F6 Skytaper (conventional austenite nickel-titanium [NiTi]), and 2 instruments with thermo-mechanically treated NiTi: Protaper Next X2 (M wire) and Hyflex CM (CM wire). Materials and methods: Ten new instruments of each group (size: 0.25 mm, 6% taper in the 3 mm tip region) were tested using a rotary bending machine with a 60° curvature angle and a 5 mm curvature radius, at room temperature. The number of cycles until fracture was recorded. The length of the fractured instruments was measured. The fracture surface of each fragment was examined with a scanning electron microscope (SEM). The data were analyzed using one-way analysis of variance and the post hoc Tukey test. The significance level was set at 0.05. Results: At 60°, One Curve, F6 Skytaper and Hyflex CM had significantly longer fatigue lives than Protaper Next X2 (p < 0.05). No statistically significant differences were found in the cyclic fatigue lives of One Curve, F6 Skytaper, and Hyflex CM (p > 0.05). SEM images of the fracture surfaces of the different instruments showed typical features of fatigue failure. Conclusions: Within the conditions of this study, at 60° and with a 5 mm curvature radius, the cyclic fatigue life of One Curve was not significantly different from those of F6 Skytaper and Hyflex CM. The cyclic fatigue lives of these 3 instruments were statistically significantly longer than that of Protaper Next.
Abstract
Objectives: This study compared the cyclic fatigue resistance of One Curve (C wire) and F6 Skytaper (conventional austenite nickel-titanium [NiTi]), and 2 instruments with thermo-mechanically treated NiTi: Protaper Next X2 (M wire) and Hyflex CM (CM wire). Materials and methods: Ten new instruments of each group (size: 0.25 mm, 6% taper in the 3 mm tip region) were tested using a rotary bending machine with a 60° curvature angle and a 5 mm curvature radius, at room temperature. The number of cycles until fracture was recorded. The length of the fractured instruments was measured. The fracture surface of each fragment was examined with a scanning electron microscope (SEM). The data were analyzed using one-way analysis of variance and the post hoc Tukey test. The significance level was set at 0.05. Results: At 60°, One Curve, F6 Skytaper and Hyflex CM had significantly longer fatigue lives than Protaper Next X2 (p < 0.05). No statistically significant differences were found in the cyclic fatigue lives of One Curve, F6 Skytaper, and Hyflex CM (p > 0.05). SEM images of the fracture surfaces of the different instruments showed typical features of fatigue failure. Conclusions: Within the conditions of this study, at 60° and with a 5 mm curvature radius, the cyclic fatigue life of One Curve was not significantly different from those of F6 Skytaper and Hyflex CM. The cyclic fatigue lives of these 3 instruments were statistically significantly longer than that of Protaper Next.
참고문헌 (46)
- Neurohr AJ, "Shape-memory NiTi with two-dimensional networks of micro-channels", Acta Biomater, 7, pp.1862~1872 (2011)
- Frotscher M, "Achieving small structures in thin NiTi sheets for medical applications with water jet and micro machining: a comparison", J Mater Eng Perform, 20, pp.776~782 (2011)
- Stoeckel D, "Nitinol medical devices and implants", Minim Invasive Ther Allied Technol, 9, pp.81~88 (2000)
- Oshida Y, "Bioscience and bioengineering of titanium materials" (2007), Elsevier
- Thompson SA, "An overview of nickel-titanium alloys used in dentistry", Int Endod J, 33, pp.297~310 (2000)
- Peters OA, "Current challenges and concepts in the preparation of root canal systems: a review", J Endod, 30, pp.559~567 (2004)
- Parashos P, "Rotary NiTi instrument fracture and its consequences", J Endod, 32, pp.1031~1043 (2006)
- Çapar ID, "A review of instrumentation kinematics of engine-driven nickel-titanium instruments", Int Endod J, 49, pp.119~135 (2016)
- Yared G, "Canal preparation using only one Ni-Ti rotary instrument: preliminary observations", Int Endod J, 41, pp.339~344 (2008)
- Franco V, "Investigation on the shaping ability of nickel-titanium files when used with a reciprocating motion", J Endod, 37, pp.1398~1401 (2011)
- Bürklein S, "Shaping ability and cleaning effectiveness of two single-file systems in severely curved root canals of extracted teeth: Reciproc and WaveOne versus Mtwo and ProTaper", Int Endod J, 45, pp.449~461 (2012)
- Mohammadi Z, "A Review of the various surface treatments of NiTi Instruments", Iran Endod J, 9, pp.235~240 (2014)
- Aun DP, "Enhancement of NiTi superelastic endodontic instruments by TiO2 coating", Mater Sci Eng C, 68, pp.675~680 (2016)
- Lopes HP, "Influence of surface roughness on the fatigue life of nickel-titanium rotary endodontic instruments", J Endod, 42, pp.965~968 (2016)
- Zupanc J, "New thermomechanically treated NiTi alloys - a review", Int Endod J, 51, pp.1088~1103 (2018)
- Pereira ES, "Physical and mechanical properties of a thermomechanically treated NiTi wire used in the manufacture of rotary endodontic instruments", Int Endod J, 45, pp.469~474 (2012)
- Alapati SB, "Metallurgical characterization of a new nickel-titanium wire for rotary endodontic instruments", J Endod, 35, pp.1589~1593 (2009)
- Siu C, "An in vivo comparison of the Root ZX II, the Apex NRG XFR, and Mini Apex Locator by using rotary nickel-titanium files", J Endod, 35, pp.962~965 (2009)
- Kaval ME, "Comparative evaluation of cyclic fatigue resistance of four different nickel-titanium rotary files with different cross-sectional designs and alloy properties", Clin Oral Investig, 21, pp.1527~1530 (2017)
- Serafin M, "In vitro comparison of cyclic fatigue resistance of two rotary single-file endodontic systems: OneCurve versus OneShape", Odontology, 107, pp.196~201 (2019)
- Shen Y, "HyFlex nickel-titanium rotary instruments after clinical use: metallurgical properties", Int Endod J, 46, pp.720~729 (2013)
- Ninan E, "Torsion and bending properties of shape memory and superelastic nickel-titanium rotary instruments", J Endod, 39, pp.101~104 (2013)
- Topçuoğlu HS, "In vitro comparison of cyclic fatigue resistance of ProTaper Next, HyFlex CM, OneShape, and ProTaper universal instruments in a canal with a double curvature", J Endod, 42, pp.969~971 (2016)
- Tobushi H, "Low-cycle fatigue of Ni-Ti shape memory alloy and formulation of fatigue life", J Eng Mater Technol, 122, pp.186~191 (2000)
- Shen Y, "Effect of environment on fatigue failure of controlled memory wire nickel-titanium rotary instruments", J Endod, 38, pp.376~380 (2012)
- Vadhana S, "Cyclic fatigue resistance of RaCe and Mtwo rotary files in continuous rotation and reciprocating motion", J Endod, 40, pp.995~999 (2014)
- Grande NM, "Cyclic fatigue resistance and threedimensional analysis of instruments from two nickel-titanium rotary systems", Int Endod J, 39, pp.755~763 (2006)
- La Rosa GR, "Influence of surrounding temperature and angle of file access on cyclic fatigue resistance of two single file nickel-titanium instruments", Aust Endod J, 47, pp.260~264 (2021)
- Rubio J, "A comparative study of cyclic fatigue of 10 different types of endodontic instruments: an in vitro study", Acta Stomatol Croat, 53, pp.28~36 (2019)
- Cheung GS, "A numerical method for predicting the bending fatigue life of NiTi and stainless steel root canal instruments", Int Endod J, 44, pp.357~361 (2011)
- Capar ID, "Comparison of cyclic fatigue resistance of novel nickel-titanium rotary instruments", Aust Endod J, 41, pp.24~28 (2015)
- Elnaghy AM, "Cyclic fatigue resistance of One Curve, 2Shape, ProFile Vortex, Vortex Blue, and RaCe nickel-titanium rotary instruments in single and double curvature canals", J Endod, 44, pp.1725~1730 (2018)
- Ye J, "Metallurgical characterization of M-Wire nickel-titanium shape memory alloy used for endodontic rotary instruments during low-cycle fatigue", J Endod, 38, pp.105~107 (2012)
- Shen Y, "Metallurgical characterization of controlled memory wire nickel-titanium rotary instruments", J Endod, 37, pp.1566~1571 (2011)
- Iacono F, "Structural analysis of HyFlex EDM instruments", Int Endod J, 50, pp.303~313 (2017)
- Testarelli L, "Bending properties of a new nickel-titanium alloy with a lower percent by weight of nickel", J Endod, 37, pp.1293~1295 (2011)
- Pongione G, "Flexibility and resistance to cyclic fatigue of endodontic instruments made with different nickel-titanium alloys: a comparative test", Ann Stomatol (Roma), 3, pp.119~122 (2012)
- Santos LA, "Comparison of the mechanical behavior between controlled memory and superelastic nickel-titanium files via finite element analysis", J Endod, 39, pp.1444~1447 (2013)
- Pereira ES, "Behavior of nickel-titanium instruments manufactured with different thermal treatments", J Endod, 41, pp.67~71 (2015)
- Goo HJ, "Mechanical properties of various heat-treated nickeltitanium rotary instruments", J Endod, 43, pp.1872~1877 (2017)
- Soares RG, "Comparative study of the mechanical properties of instruments made of conventional, M-wire, R-phase, and controlled memory nickel-titanium alloys", ENDO, 11, pp.271~277 (2017)
- Zhou HM, "Mechanical properties of controlled memory and superelastic nickel-titanium wires used in the manufacture of rotary endodontic instruments", J Endod, 38, pp.1535~1540 (2012)
- Capar ID, "Comparison of the cyclic fatigue resistance of 5 different rotary pathfinding instruments made of conventional nickel-titanium wire, M-wire, and controlled memory wire", J Endod, 41, pp.535~538 (2015)
- Pedullà E, "Influence of cyclic torsional preloading on cyclic fatigue resistance of nickel - titanium instruments", Int Endod J, 48, pp.1043~1050 (2015)
- Palma PJ, "Cyclic fatigue resistance of three rotary file systems in a dynamic model after immersion in sodium hypochlorite", Odontology, 107, pp.324~332 (2019)
- Topçuoğlu HS, "Effect of two different temperatures on resistance to cyclic fatigue of one Curve, EdgeFile, HyFlex CM and ProTaper next files", Aust Endod J, 46, pp.68~72 (2020)