The effects of autoclave sterilization on the cyclic fatigue resistance of ProTaper Universal, ProTaper Next, and ProTaper Gold nickel-titanium instruments
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Objectives: It was aimed to compare the cyclic fatigue resistances of ProTaper Universal (PTU), ProTaper Next (PTN), and ProTaper Gold (PTG) and the effects of sterilization by autoclave on the cyclic fatigue life of nickel-titanium (NiTi) instruments. Materials and Methods: Eighty PTU, 80 PTN, and 80 PTG were included to the present study. Files were tested in a simulated canal. Each brand of the NiTi files were divided into 4 subgroups: group 1, as received condition; group 2, pre-sterilized instruments exposed to 10 times sterilization by autoclave; group 3, instruments tested were sterilized after being exposed to 25%, 50%, and 75% of the mean cycles to failure, then cycled fatigue test was performed; group 4, instruments exposed to the same experiment with group 3 without sterilization. The number of cycles to failure (NCF) was calculated. The data was statistically analyzed by using one-way analysis of variance and post hoc Tukey tests. Results: PTG showed significantly higher NCF than PTU and PTN in group 1 (p < 0.05). Sterilization significantly increased the NCF of PTN and PTG (p < 0.05) in group 2. PTN in group 3 had significantly higher cyclic fatigue resistance than PTN group 4 (p < 0.05). Also, significantly higher NCF was observed for PTG in group 2 than in groups 3 and 4 (p < 0.05). Conclusions: PTG instrument made of new gold alloy was more resistant to fatigue failure than PTN and PTU. Autoclaving increased the cyclic fatigue resistances of PTN and PTG.
Abstract
Objectives: It was aimed to compare the cyclic fatigue resistances of ProTaper Universal (PTU), ProTaper Next (PTN), and ProTaper Gold (PTG) and the effects of sterilization by autoclave on the cyclic fatigue life of nickel-titanium (NiTi) instruments. Materials and Methods: Eighty PTU, 80 PTN, and 80 PTG were included to the present study. Files were tested in a simulated canal. Each brand of the NiTi files were divided into 4 subgroups: group 1, as received condition; group 2, pre-sterilized instruments exposed to 10 times sterilization by autoclave; group 3, instruments tested were sterilized after being exposed to 25%, 50%, and 75% of the mean cycles to failure, then cycled fatigue test was performed; group 4, instruments exposed to the same experiment with group 3 without sterilization. The number of cycles to failure (NCF) was calculated. The data was statistically analyzed by using one-way analysis of variance and post hoc Tukey tests. Results: PTG showed significantly higher NCF than PTU and PTN in group 1 (p < 0.05). Sterilization significantly increased the NCF of PTN and PTG (p < 0.05) in group 2. PTN in group 3 had significantly higher cyclic fatigue resistance than PTN group 4 (p < 0.05). Also, significantly higher NCF was observed for PTG in group 2 than in groups 3 and 4 (p < 0.05). Conclusions: PTG instrument made of new gold alloy was more resistant to fatigue failure than PTN and PTU. Autoclaving increased the cyclic fatigue resistances of PTN and PTG.
참고문헌 (27)
- Ingle JI, "Endodontics", pp.409~410 (2002), BC Decker Inc
- Sattapan B, "Defects in rotary nickel-titanium files after clinical use", J Endod, 26, pp.161~165 (2000)
- Cheung GS, "Instrument fracture: mechanisms, removal of fragments, and clinical outcomes", Endod Topics, 16, pp.1~26 (2007)
- Gao Y, "Evaluation of the impact of raw materials on the fatigue and mechanical properties of ProFile Vortex rotary instruments", J Endod, 38, pp.398~401 (2012)
- "Dentsply Sirona Endodontics (US): ProTaper Next Brochure"[URL]
- Arias A, "Torque and force induced by ProTaper Universal and ProTaper Next during shaping of large and small root canals in extracted teeth", J Endod, 40 (2014)
- Zinelis S, "The effect of thermal treatment on the resistance of nickel-titanium rotary files in cyclic fatigue", Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 103, pp.843~847 (2007)
- Yahata Y, "Effect of heat treatment on transformation temperatures and bending properties of nickel-titanium endodontic instruments", Int Endod J, 42, pp.621~626 (2009)
- Viana AC, "Influence of sterilization on mechanical properties and fatigue resistance of nickel-titanium rotary endodontic instruments", Int Endod J, 39, pp.709~715 (2006)
- Plotino G, "Experimental evaluation on the influence of autoclave sterilization on the cyclic fatigue of new nickel-titanium rotary instruments", J Endod, 38, pp.222~225 (2012)
- Hilfer PB, "Multiple autoclave cycle effects on cyclic fatigue of nickel-titanium rotary files produced by new manufacturing methods", J Endod, 37, pp.72~74 (2011)
- Mize SB, "Effect of sterilization on cyclic fatigue of rotary nickel-titanium endodontic instruments", J Endod, 24, pp.843~847 (1998)
- Parashos P, "Factors influencing defects of rotary nickel-titanium endodontic instruments after clinical use", J Endod, 30, pp.722~725 (2004)
- Cheung GS, "Defects in ProTaper S1 instruments after clinical use: fractographic examination", Int Endod J, 38, pp.802~809 (2005)
- Peng B, "Defects in ProTaper S1 instruments after clinical use: longitudinal examination", Int Endod J, 38, pp.550~557 (2005)
- Chaves Craveiro de Melo M, "Fatigue resistance of engine-driven rotary nickel-titanium endodontic instruments", J Endod, 28, pp.765~769 (2002)
- Gambarini G, "Fatigue resistance of engine-driven rotary nickel-titanium instruments produced by new manufacturing methods", J Endod, 34, pp.1003~1005 (2008)
- Larsen CM, "Cyclic fatigue analysis of a new generation of nickel titanium rotary instruments", J Endod, 35, pp.401~403 (2009)
- Testarelli L, "Cyclic fatigue of different nickel-titanium rotary instruments: a comparative study", Open Dent J, 3, pp.55~58 (2009)
- Yared GM, "Influence of rotational speed, torque and operator's proficiency on ProFile failures", Int Endod J, 34, pp.47~53 (2001)
- Valois CR, "Multiple autoclave cycles affect the surface of rotary nickel-titanium files: an atomic force microscopy study", J Endod, 34, pp.859~862 (2008)
- Zhao D, "Effect of autoclave sterilization on the cyclic fatigue resistance of thermally treated nickel-titanium instruments", Int Endod J, 49, pp.990~995 (2016)
- Canalda-Sahli C, "The effect of sterilization on bending and torsional properties of K-files manufactured with different metallic alloys", Int Endod J, 31, pp.48~52 (1998)
- Uygun AD, "Variations in cyclic fatigue resistance among ProTaper Gold, ProTaper Next and ProTaper Universal Instruments at different levels", Int Endod J, 49, pp.494~499 (2016)
- Hieawy A, "Phase transformation behavior and resistance to bending and cyclic fatigue of ProTaper Gold and ProTaper Universal Instruments", J Endod, 41, pp.1134~1138 (2015)
- Pérez-Higueras JJ, "Cyclic fatigue resistance of K3, K3XF, and twisted file nickel-titanium files under continuous rotation or reciprocating motion", J Endod, 39, pp.1585~1588 (2013)
- Elnaghy AM, "Cyclic fatigue resistance of ProTaper Next nickel-titanium rotary files", Int Endod J, 47, pp.1034~1039 (2014)