Cyclic fatigue, bending resistance, and surface roughness of ProTaper Gold and EdgeEvolve files in canals with single- and double-curvature
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Objectives: The purpose of this study was to evaluate the cyclic fatigue, bending resistance, and surface roughness of EdgeEvolve (EdgeEndo) and ProTaper Gold (Dentsply Tulsa Dental Specialties) nickel-titanium (NiTi) rotary files. Materials and Methods: The instruments (n = 15/each) were tested for cyclic fatigue in single- (60° curvature, 5-mm radius) and double-curved (coronal curvature 60°, 5-mm radius, and apical curvature of 30° and 2-mm radius) artificial canals. The number of cycles to fracture was calculated. The bending resistance of both files were tested using a universal testing machine where the files were bent until reach 45°. Scanning electron microscopy and x-ray energy-dispersive spectrometric analysis were used for imaging the fractured segments, while the atomic force microscope was used to quantify the surface roughness average (Ra). Results: EdgeEvolve files exhibited higher cyclic fatigue resistance than ProTaper Gold files in single- and double-curved canals (p < 0.05) and both files were more resistant to cyclic fatigue in single-curved canals than double-curved canals (p < 0.05). EdgeEvolve files exhibited significantly more flexibility than did ProTaper Gold files (p < 0.05). Both files had approximately similar Ni and Ti contents (p > 0.05). EdgeEvolve files showed significantly lower Ra values than ProTaper Gold files (p < 0.05). Conclusions: Within the limitation of this study, EdgeEvolve files exhibited significantly higher cyclic fatigue resistance than ProTaper Gold files in both single- and double-curved canals.
Abstract
Objectives: The purpose of this study was to evaluate the cyclic fatigue, bending resistance, and surface roughness of EdgeEvolve (EdgeEndo) and ProTaper Gold (Dentsply Tulsa Dental Specialties) nickel-titanium (NiTi) rotary files. Materials and Methods: The instruments (n = 15/each) were tested for cyclic fatigue in single- (60° curvature, 5-mm radius) and double-curved (coronal curvature 60°, 5-mm radius, and apical curvature of 30° and 2-mm radius) artificial canals. The number of cycles to fracture was calculated. The bending resistance of both files were tested using a universal testing machine where the files were bent until reach 45°. Scanning electron microscopy and x-ray energy-dispersive spectrometric analysis were used for imaging the fractured segments, while the atomic force microscope was used to quantify the surface roughness average (Ra). Results: EdgeEvolve files exhibited higher cyclic fatigue resistance than ProTaper Gold files in single- and double-curved canals (p < 0.05) and both files were more resistant to cyclic fatigue in single-curved canals than double-curved canals (p < 0.05). EdgeEvolve files exhibited significantly more flexibility than did ProTaper Gold files (p < 0.05). Both files had approximately similar Ni and Ti contents (p > 0.05). EdgeEvolve files showed significantly lower Ra values than ProTaper Gold files (p < 0.05). Conclusions: Within the limitation of this study, EdgeEvolve files exhibited significantly higher cyclic fatigue resistance than ProTaper Gold files in both single- and double-curved canals.
참고문헌 (28)
- Cheung GS, "A retrospective study of endodontic treatment outcome between nickel-titanium rotary and stainless steel hand filing techniques", J Endod, 35, pp.938~943 (2009)
- Sattapan B, "Defects in rotary nickel-titanium files after clinical use", J Endod, 26, pp.161~165 (2000)
- Parashos P, "Factors influencing defects of rotary nickel-titanium endodontic instruments after clinical use", J Endod, 30, pp.722~725 (2004)
- Shen Y, "Fatigue testing of controlled memory wire nickel-titanium rotary instruments", J Endod, 37, pp.997~1001 (2011)
- Al-Sudani D, "Cyclic fatigue of nickel-titanium rotary instruments in a double(S-shaped)simulated curvature", J Endod, 38, pp.987~989 (2012)
- Duke F, "Cyclic fatigue of ProFile Vortex and Vortex Blue nickel-titanium files in single and double curvatures", J Endod, 41, pp.1686~1690 (2015)
- de Arruda Santos L, "Comparison of the mechanical behavior between controlled memory and superelastic nickel-titanium files via finite element analysis", J Endod, 39, pp.1444~1447 (2013)
- Hieawy A, "Phase transformation behavior and resistance to bending and cyclic fatigue of ProTaper Gold and ProTaper Universal instruments", J Endod, 41, pp.1134~1138 (2015)
- Capar ID, "Comparison of the cyclic fatigue resistance of 5 different rotary pathfinding instruments made of conventional nickel-titanium wire, M-wire, and controlled memory wire", J Endod, 41, pp.535~538 (2015)
- Topçuoğlu HS, "In vitro comparison of cyclic fatigue resistance of ProTaper Next, HyFlex CM, OneShape, and ProTaper Universal instruments in a canal with a double curvature", J Endod, 42, pp.969~971 (2016)
- Uygun AD, "Variations in cyclic fatigue resistance among ProTaper Gold, ProTaper Next and ProTaper Universal instruments at different levels", Int Endod J, 49, pp.494~499 (2016)
- Plotino G, "Measurement of the trajectory of different NiTi rotary instruments in an artificial canal specifically designed for cyclic fatigue tests", Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 108, pp.e152~e156 (2009)
- Silva EJ, "Bending resistance and cyclic fatigue of a new heat-treated reciprocating instrument", Scanning, 38, pp.837~841 (2016)
- De-Deus G, "Blue thermomechanical treatment optimizes fatigue resistance and flexibility of the Reciproc files", J Endod, 43, pp.462~466 (2017)
- Cai JJ, "Effect of irrigation on surface roughness and fatigue resistance of controlled memory wire nickel-titanium instruments", Int Endod J, 50, pp.718~724 (2017)
- Lin LM, "Do procedural errors cause endodontic treatment failure?", J Am Dent Assoc, 136, pp.187~193 (2005)
- Shen Y, "Fatigue resistance of a 3-dimensional conforming nickel-titanium rotary instrument in double curvatures", J Endod, 42, pp.961~964 (2016)
- Zhang Y, "Influence of cooling rate on phase transformation and microstructure of Ti-50.9%Ni shape memory alloy", T Nonferr Metal Soc J, 22, pp.2685~2690 (2012)
- Yahata Y, "Effect of heat treatment on transformation temperatures and bending properties of nickel-titanium endodontic instruments", Int Endod J, 42, pp.621~626 (2009)
- Braga LC, "Impact of heat treatments on the fatigue resistance of different rotary nickel-titanium instruments", J Endod, 40, pp.1494~1497 (2014)
- Gu Y, "Various heat-treated nickel-titanium rotary instruments evaluated in S-shaped simulated resin canals", J Dent Sci, 12, pp.14~20 (2017)
- Lopes HP, "Influence of surface roughness on the fatigue life of nickel-titanium rotary endodontic instruments", J Endod, 42, pp.965~968 (2016)
- Kim BH, "Effect from surface treatment of nickel-titanium rotary files on the fracture resistance", Scanning, 37, pp.82~87 (2015)
- Grande NM, "Cyclic fatigue resistance and three-dimensional analysis of instruments from two nickel-titanium rotary systems", Int Endod J, 39, pp.755~763 (2006)
- Elnaghy AM, "Mechanical properties of ProTaper Gold nickel-titanium rotary instruments", Int Endod J, 49, pp.1073~1078 (2016)
- Kaval ME, "Evaluation of the cyclic fatigue and torsional resistance of novel nickel-titanium rotary files with various alloy properties", J Endod, 42, pp.1840~1843 (2016)
- Zhang YQ, "Influence of cooling rate on phase transformation and microstructure of Ti-50.9%Ni shape memory alloy", Trans Nonferrous Met Soc China, 22, pp.2685~2690 (2012)
- Schäfer E, "Bending properties of rotary nickel-titanium instruments", Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 96, pp.757~763 (2003)