Effect of solution temperature on the mechanical properties of dual-cure resin cements
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
PURPOSE. This study was to evaluate the effect of the solution temperature on the mechanical properties of dualcure resin cements. MATERIALS AND METHODS. For the study, five dual-cure resin cements were chosen and light cured. To evaluate the effect of temperature on the specimens, the light-cured specimens were immersed in deionized water at three different temperatures (4, 37 and 60℃) for 7 days. The control specimens were aged in a 37℃ dry and dark chamber for 24 hours. The mechanical properties of the light-cured specimens were evaluated using the Vickers hardness test, three-point bending test, and compression test, respectively. Both flexural and compressive properties were evaluated using a universal testing machine. The data were analyzed using a two way ANOVA with Tukey test to perform multiple comparisons (α=0.05). RESULTS. After immersion, the specimens showed significantly different microhardness, flexural, and compressive properties compared to the control case regardless of solution temperatures. Depending on the resin brand, the microhardness difference between the top and bottom surfaces ranged approximately 3.3-12.2%. Among the specimens, BisCem and Calibra showed the highest and lowest decrease of flexural strength, respectively. Also, Calibra and Multilink Automix showed the highest and lowest decrease of compressive strength, respectively compared to the control case. CONCLUSION. The examined dual-cure resin cements had compatible flexural and compressive properties with most methacrylate-based composite resins and the underlying dentin regardless of solution temperature. However, the effect of the solution temperature on the mechanical properties was not consistent and depended more on the resin brand.
Abstract
PURPOSE. This study was to evaluate the effect of the solution temperature on the mechanical properties of dualcure resin cements. MATERIALS AND METHODS. For the study, five dual-cure resin cements were chosen and light cured. To evaluate the effect of temperature on the specimens, the light-cured specimens were immersed in deionized water at three different temperatures (4, 37 and 60℃) for 7 days. The control specimens were aged in a 37℃ dry and dark chamber for 24 hours. The mechanical properties of the light-cured specimens were evaluated using the Vickers hardness test, three-point bending test, and compression test, respectively. Both flexural and compressive properties were evaluated using a universal testing machine. The data were analyzed using a two way ANOVA with Tukey test to perform multiple comparisons (α=0.05). RESULTS. After immersion, the specimens showed significantly different microhardness, flexural, and compressive properties compared to the control case regardless of solution temperatures. Depending on the resin brand, the microhardness difference between the top and bottom surfaces ranged approximately 3.3-12.2%. Among the specimens, BisCem and Calibra showed the highest and lowest decrease of flexural strength, respectively. Also, Calibra and Multilink Automix showed the highest and lowest decrease of compressive strength, respectively compared to the control case. CONCLUSION. The examined dual-cure resin cements had compatible flexural and compressive properties with most methacrylate-based composite resins and the underlying dentin regardless of solution temperature. However, the effect of the solution temperature on the mechanical properties was not consistent and depended more on the resin brand.
참고문헌 (32)
- Goracci C, "Microtensile bond strength and interfacial properties of self-etching and self-adhesive resin cements used to lute composite onlays under different seating forces", J Adhes Dent, 8, pp.327~335 (2006)
- Yang B, "Micro-tensile bond strength of three luting resins to human regional dentin", Dent Mater, 22, pp.45~56 (2006)
- De Munck J, "Bonding of an auto-adhesiveluting material to enamel and dentin", Dent Mater, 20, pp.963~971 (2004)
- Uy JN, "Load-fatigue performance of gold crowns luted with resin cements", J Prosthet Dent, 95, pp.315~322 (2006)
- Pace LL, "Comparison of the flexural strength of five adhesive resin cements", JProsthodont, 16, pp.18~24 (2007)
- Lee IB, "Influence of ceramic thickness and curing mode on the polymerization shrinkage kinetics of dual-cured resin cements", Dent Mater, 24, pp.1141~1147 (2008)
- Cattani-Lorente MA, "Effect of water on the physical properties of resin-modified glass ionomer cements", Dent Mater, 15, pp.71~78 (1999)
- el-Badrawy WA, "Chemical versus dual curing of resin inlay cements", J Prosthet Dent, 73, pp.515~524 (1995)
- Barghi N, "LED and halogen lights: effect of ceramic thickness and shade on curing luting resin", Compend Contin Educ Dent, 24, pp.497~504 (2003)
- Jung H, "Curing efficiency of different polymerization methods through ceramic restorations", Clin Oral Investig, 5, pp.156~161 (2001)
- Park SH, "Curing units’ability to cure restorative composites and dual-cured composite cements under composite overlay", Oper Dent, 29, pp.627~635 (2004)
- Hofmann N, "Comparison of photo-activation versus chemical or dual-curing of resinbased luting cements regarding flexural strength, modulus and surface hardness", J Oral Rehabil, 28, pp.1022~1028 (2001)
- Rueggeberg FA, "Effect of light intensity and exposure duration on cure of resin composite", Oper Dent, 19, pp.26~32 (1994)
- Witzel MF, "Bond strength between polymer resin-based cement and porcelaindentin surfaces: influence of polymerization mode and early cyclic loading", Int J Prosthodont, 16, pp.145~149 (2003)
- Spierings TA, "Verification of theoretical modeling of heat transmission in teeth by in vivo experiments", J Dent Res, 66, pp.1336~1339 (1987)
- Airoldi G, "Oral environment temperature changes induced by cold", hot liquid intake, 1997, pp.112, 58~63
- Cantoro A, "Effect of pre-cure temperature on the bonding potential of self-etch and self-adhesive resin cements", Dent Mater, 24, pp.577~583 (2008)
- Cantoro A, "Bonding potential of self-adhesive luting agents used at different temperatures to lute composite onlays", J Dent, 37, pp.454~461 (2009)
- "ISO 4049: Dentistry - Polymer-based restorative materials", ISO, ~ (2009)
- Chung KH, "Correlation between degree of conversion, filler concentration and mechanical properties of posterior composite resins", J Oral Rehabil, 17, pp.487~494 (1990)
- Asmussen E, "Influence of UEDMA BisGMA and TEGDMA on selected mechanical properties of experimental resin composites", Dent Mater, 14, pp.51~56 (1998)
- Floyd CJ, "Network structure of Bis-GMA- and UDMA-based resin systems", Dent Mater, 22, pp.1143~1149 (2006)
- Musanje L, "Effects of resin formulation and nanofiller surface treatment on the properties of experimental hybrid resin composite", Biomaterials, 25, pp.4065~4071 (2004)
- Mayworm CD, "Influence of artificial saliva on abrasive wear and microhardness of dental composites filled with nanoparticles", J Dent, 36, pp.703~710 (2008)
- Zeng K, "Flexure tests on dental ceramics. Int J Prosthodont", Int J Prosthodont, 9, pp.434~439 (1996)
- Bona AD, "Weibull analysis and flexural strength of hot-pressed core and veneered ceramic structures", Dent Mater, 19, pp.662~669 (2003)
- Mecholsky JJ Jr, "Fracture mechanics principles", Dent Mater, 11, pp.111~112 (1995)
- Ilie N, "Investigations on mechanical behaviour of dental composites", Clin Oral Investig, 13, pp.427~438 (2009)
- Xu HH, "Indentation damage and mechanical properties of human enamel and dentin", J Dent Res, 77, pp.472~480 (1998)
- Mahoney E, "The hardness and modulus of elasticity of primary molar teeth: an ultramicro-indentation study", J Dent, 28, pp.589~594 (2000)
- Craig RG, "Elastic and mechanical properties of human dentin", J Dent Res, 37, pp.710~718 (1958)
- Watts DC, "Temperaturedependence of compressive properties of human dentin", J Dent Res, 66, pp.29~32 (1987)