Curing efficiency of various resin-based materials polymerized through different ceramic thicknesses and curing time
2
조회
0
다운로드
1
인용
0
참고문헌
초록
PURPOSE. The aim of this in vitro study was to examine the curing efficiency of various resin-based materials polymerized through ceramic restorations with 3 different thicknesses. Curing efficiency was evaluated by determining the surface microhardness (VHN) of the resin specimens. MATERIALS AND METHODS. Four kinds of resin materials were used. Z350 (3M ESPE FiltekTM Z350: A2 Shade), Z250 (3M ESPE FiltekTM Z250: A2 Shade) and Variolink(R). II (VL: Ivoclar vivadent, base: transparent) either with or without a self-curing catalyst (VLC: Ivoclar vivadent, catalyst: low viscosity/transparent) were filled into the silicone mold (10 mm diameter, 1 mm thick). They were cured through ceramic discs (IPS e.max Press MO-0 ingot ivoclar vivadent, 10 mm diameter, 0.5, 1 and 2 mm thicknesses) by LED light-curing units for 20 and 40 seconds. Vicker’s microhardness numbers (VHNs) were measured on the bottom surfaces by a microhardness tester. Data were analyzed using a 3-way analysis of variance (ANOVA) at a significance level of 0.05. RESULTS. The thickness of ceramic disc increased, the VHNs of all four resin types were decreased (P<.05). The mean VHN values of the resins light cured for 40 seconds were significantly higher than that of LED for 20 seconds in all four resin materials (P<.05). VLC showed significantly higher VHN values than VL regardless of other conditions (P<.05). Z350 and Z250 showed higher values than VL or VLC (P<.01). CONCLUSION. Thinner ceramic disc with increased curing time resulted higher VHN values of all resin materials. The use of a catalyst produced a greater hardness with all polymerization methods. Restorative resin materials (Z350, Z250) showed higher VHN values than resin cement materials (VL, VLC).
Abstract
PURPOSE. The aim of this in vitro study was to examine the curing efficiency of various resin-based materials polymerized through ceramic restorations with 3 different thicknesses. Curing efficiency was evaluated by determining the surface microhardness (VHN) of the resin specimens. MATERIALS AND METHODS. Four kinds of resin materials were used. Z350 (3M ESPE FiltekTM Z350: A2 Shade), Z250 (3M ESPE FiltekTM Z250: A2 Shade) and Variolink(R). II (VL: Ivoclar vivadent, base: transparent) either with or without a self-curing catalyst (VLC: Ivoclar vivadent, catalyst: low viscosity/transparent) were filled into the silicone mold (10 mm diameter, 1 mm thick). They were cured through ceramic discs (IPS e.max Press MO-0 ingot ivoclar vivadent, 10 mm diameter, 0.5, 1 and 2 mm thicknesses) by LED light-curing units for 20 and 40 seconds. Vicker’s microhardness numbers (VHNs) were measured on the bottom surfaces by a microhardness tester. Data were analyzed using a 3-way analysis of variance (ANOVA) at a significance level of 0.05. RESULTS. The thickness of ceramic disc increased, the VHNs of all four resin types were decreased (P<.05). The mean VHN values of the resins light cured for 40 seconds were significantly higher than that of LED for 20 seconds in all four resin materials (P<.05). VLC showed significantly higher VHN values than VL regardless of other conditions (P<.05). Z350 and Z250 showed higher values than VL or VLC (P<.01). CONCLUSION. Thinner ceramic disc with increased curing time resulted higher VHN values of all resin materials. The use of a catalyst produced a greater hardness with all polymerization methods. Restorative resin materials (Z350, Z250) showed higher VHN values than resin cement materials (VL, VLC).
참고문헌 (27)
- Asmussen E, "Restorative resins: hardness and strength vs. quantity of remaining double bonds", Scand J Dent Res, 90, pp.484~489 (1982)
- Caughman WF, "Correlation of cytotoxicity, filler loading and curing time of dental composites", Biomaterials, 12, pp.737~740 (1991)
- El-Mowafy OM, "Influence of composite inlay", onlay thickness on hardening of dual-cured resin cements, 2000, pp.66, 147~
- Cheong C, "Incompatibility of self-etch adhesives with chemical", dualcured composites: two-step vs one-step systems, 2003, pp.28, 747~755
- Suh BI, "Factors contributing to the incompatibility between simplified-step adhesives and chemically-cured or dual-cured composites. Part III. Effect of acidic resin monomers", J Adhes Dent, 5, pp.267~282 (2003)
- Calamia JR, "Porcelain laminate veneers: reasons for 25 years of success", Dent Clin North Am, 51, pp.399~417 (2007)
- Garber DA, "Porcelain and composite inlays and onlays: esthetic posterior restorations" (1994), Publishing Co
- Strang R, "Variations in performance of curing light units by determination of composite resin setting time", Br Dent J, 162, pp.63~65 (1987)
- Blackman R, "Influence of ceramic thickness on the polymerization of light-cured resin cement", J Prosthet Dent, 63, pp.295~300 (1990)
- Peutzfeldt A, "The effect of postcuring on quantity of remaining double bonds, mechanical properties, and in vitro wear of two resin composites", J Dent, 28, pp.447~452 (2000)
- Pianelli C, "The micro-Raman spectroscopy, a useful tool to determine the degree of conversion of light-activated composite resins", J Biomed Mater Res, 48, pp.675~681 (1999)
- Shortall AC, "Effect of light intensity on polymerisation of three composite resins", Eur J Prosthodont Restor Dent, 4, pp.71~76 (1996)
- Koch A, "Influence of ceramic translucency on curing efficacy of different light-curing units", J Adhes Dent, 9, pp.449~462 (2007)
- Hooshmand T, "Microhardness of a resin cement polymerized by light-emitting diode and halogen lights through ceramic", J Prosthodont, 18, pp.411~416 (2009)
- Hofmann N, "Comparison of photo- activation versus chemical or dual-curing of resin-based luting cements regarding flexural strength, modulus and surface hardness", J Oral Rehabil, 28, pp.1022~1028 (2001)
- Rueggeberg FA, "Correlation of parameters used to estimate monomer conversion in a light-cured composite", J Dent Res, 67, pp.932~937 (1988)
- Rueggeberg FA, "Polymerization depths of contemporary light-curing units using microhardness", J Esthet Dent, 12, pp.340~349 (2000)
- Magne P, "Bonded porcelain restorations in the anterior dentition-a biomimetic approach" (2002), Quintessence Publishing Co
- Jung H, "Curing efficiency of different polymerization methods through ceramic restorations", Clin Oral Investig, 5, pp.156~161 (2001)
- Rasetto FH, "Effect of light source and time on the polymerization of resin cement through ceramic veneers", J Prosthodont, 10, pp.133~139 (2001)
- Santos GC Jr, "Hardening of dual-cure resin cements and a resin composite restorative cured with QTH and LED curing units", J Can Dent Assoc, 70, pp.323~328 (2004)
- Moon HJ, "Effects of various light curing methods on the leachability of uncured substances and hardness of a composite resin", J Oral Rehabil, 31, pp.258~264 (2004)
- O'Keefe KL, "Variables affecting the spectral transmittance of light through porcelain veneer samples", J Prosthet Dent, 66, pp.434~438 (1991)
- Brodbelt RH, "Translucency of dental porcelains", J Dent Res, 59, pp.70~75 (1980)
- Akgungor G, "Influence of ceramic thickness and polymerization mode of a resin luting agent on early bond strength and durability with a lithium disilicate-based ceramic system", J Prosthet Dent, 94, pp.234~241 (2005)
- Rueggeberg FA, "The influence of light exposure on polymerization of dual-cure resin cements", Oper Dent, 18, pp.48~55 (1993)
- van Meerbeek B, "Dual cure luting composites-Part II: Clinically related properties", J Oral Rehabil, 21, pp.57~66 (1994)