Effect of dopants(Tri-valent, Penta-valent) on the electrical and optical properties of SnO2 based transparent electrodes
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this work, we studied the influence of the dopant elements concentration on the properties of SnO2 thin films deposited by pulsed laser deposition. X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), Hall effect measurement and UV-Vis studies were performed to characterize the deposited films. XRD results showed that the films had polycrystalline nature with tetragonal rutile structure. FE-SEM micrographs revealed that the as deposited films composed of dense microstructures with uniform grain size distribution. All the films show n-type conduction and the best transparent conductive oxide (TCO) performance was obtained on 6 wt% Sb2O5 doped SnO2 film prepared at pO2 of 60mtorr and Ts of 500 ο C. Its resitivity, optical transmittance, figure of merit are 7.8 × 10-4 Ω cm, 85% and 1.2 × 10-2 Ω-1, respectively.
Abstract
In this work, we studied the influence of the dopant elements concentration on the properties of SnO2 thin films deposited by pulsed laser deposition. X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), Hall effect measurement and UV-Vis studies were performed to characterize the deposited films. XRD results showed that the films had polycrystalline nature with tetragonal rutile structure. FE-SEM micrographs revealed that the as deposited films composed of dense microstructures with uniform grain size distribution. All the films show n-type conduction and the best transparent conductive oxide (TCO) performance was obtained on 6 wt% Sb2O5 doped SnO2 film prepared at pO2 of 60mtorr and Ts of 500 ο C. Its resitivity, optical transmittance, figure of merit are 7.8 × 10-4 Ω cm, 85% and 1.2 × 10-2 Ω-1, respectively.
참고문헌 (14)
- Y. S. He, , J. Mater. Res, 8, pp.3131~ (1993)
- W. A. Badway, , J. Electrochem. soc, 137, pp.1592~ (1990)
- Y. L. Fang, , Thin Solid Films, 169, pp.52~ (1989)
- J. C. Manifacier, , Mater. Res. Bull, 14, pp.109~ (1979)
- H. Kim, , Thin Solid Films, 516, pp.5052~ (2005)
- H. Kim, , Appl. Phys. Lett, 74, pp.3444~ (1999)
- Y. Onuma, , Jpn. J. Appl. Phys. Part1, 37, pp.963~ (1998)
- H. Kim, , Appl. Phys. Lett, 79, pp.284~ (2001)
- R.D. Shannon, , Acta Cryst. A, 32, pp.751~ (1976)
- B. Thangaraju, , Thin Solid Films, 402, pp.71~ (2002)
- S. Shanthi, , J. Crystal Growth, 197, pp.858~ (1999)
- N. s. Murty, , Thin Solid Films, 108, pp.277~ (1983)
- G. Haacke, , J. Appl. Phys, 47, pp.4086~4089 (1976)
- A. M. Bazargan, , Chem. Eng. J, 155, pp.523~ (2009)