산화물 분산강화형 316L 스테인리스강의 제조와 특성 연구
Fabrication and Characterization of ODS 316L Stainless Steels
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Austenitic oxide-dispersion-strengthened (ODS) stainless steel was fabricated using a wet mixing process without a mechanical milling in order to reduce contaminations of impurities during their fabrication process. Solution of yttrium nitrate was dried after a wet mixing with 316L stainless steel powder. Carbon and oxygen contents were effectively reduced by this wet processing. Microstructural analysis showed that coarse yttrium silicates of about 150 ㎚ were formed in austenitic ODS steels with a silicon content of about 0.8 wt%. Wet-processed austenitic ODS steel without silicon showed higher yield strength by the presence of finer oxide of about 20㎚ nm.
Abstract
Austenitic oxide-dispersion-strengthened (ODS) stainless steel was fabricated using a wet mixing process without a mechanical milling in order to reduce contaminations of impurities during their fabrication process. Solution of yttrium nitrate was dried after a wet mixing with 316L stainless steel powder. Carbon and oxygen contents were effectively reduced by this wet processing. Microstructural analysis showed that coarse yttrium silicates of about 150 ㎚ were formed in austenitic ODS steels with a silicon content of about 0.8 wt%. Wet-processed austenitic ODS steel without silicon showed higher yield strength by the presence of finer oxide of about 20㎚ nm.
참고문헌 (16)
- J. H. Hong, , Mechanic and Materials, 19, pp.6~ (2007)
- A. Alamo, , J. Nucl. Mater., 329, pp.333~ (2004)
- S. Yamashita, , J. Nucl. Mater., 329, pp.377~ (2004)
- S. Ukai, , J. Nucl. Mater., 283, pp.702~ (2000)
- C. Capdevila, , Bhadeshia: Adv. Eng. Mater., 3, pp.647~ (2001)
- H. Y. Kim, , Scrip. Mater., 54, pp.1703~ (2006)
- Y. Z. Shen, , Nuclear Engineering and Technology, 40, pp.99~ (2008)
- M. P. Phaniraj, , Acta. Mater., 57, pp.1856~ (2009)
- T. Kariya, "Publication of patent applications, JP2003-027109", ~ (2003)
- J. H. Ahn, , J. Alloy. Comp. (2008)
- P. Shunmi, , Transaction of Metal Heat Treatment, 18, pp.346~ (1997)
- H. J. Ryu, , ANS Annual Meeting (2008)
- G. A. M. Hussein, , Thermochim. Acta., 244, pp.139~ (1994)
- V. de Castro, , J. Nucl. Mater., 322, pp.228~ (2003)
- S. Ohtsuka, , J. Nucl. Mater., 351, pp.241~ (2006)
- Y. Uchida, , Mater. Res. Soc. Symp. Proc., 통권 : 981, pp.9~ (2007)