Ni-22Cr-18Fe-9Mo계 ODS 합금의 미세조직 및 고온인장 특성 평가
Microstructural Evaluation and High Temperature Mechanical Properties of Ni-22Cr-18Fe-9Mo ODS Alloy
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Yttrium oxide is one of the most thermo-dynamically stable materials, so that it is generally used as a dispersoid in many kinds of dispersion strengthed alloys. In this study, a nickel-base superalloy is strengthened by dispersion of yttrium oxide particles. Elemental powders with the composition of Ni-22Cr-18Fe-9Mo were mechanically alloyed(M.A.) with 0.6 wt% Y_2O_3. The MA powders were then HIP(hot isotactic press)ed and hot rolled. Most oxide particles in Ni-22Cr-18Fe-9Mo base ODS alloy were found to be Y-Ti-O type. The oxide particles were uniformly dispersed in the matrix and also on the grain boundaries. Tensile test results show that the yield strength and ultimate tensile strength of ODS alloy specimens were 1.2~1.7 times higher than those of the conventional Hastelloy^(TM) X(R), which has the same chemical compositions with ODS alloy specimens except the oxide particles.
Abstract
Yttrium oxide is one of the most thermo-dynamically stable materials, so that it is generally used as a dispersoid in many kinds of dispersion strengthed alloys. In this study, a nickel-base superalloy is strengthened by dispersion of yttrium oxide particles. Elemental powders with the composition of Ni-22Cr-18Fe-9Mo were mechanically alloyed(M.A.) with 0.6 wt% Y_2O_3. The MA powders were then HIP(hot isotactic press)ed and hot rolled. Most oxide particles in Ni-22Cr-18Fe-9Mo base ODS alloy were found to be Y-Ti-O type. The oxide particles were uniformly dispersed in the matrix and also on the grain boundaries. Tensile test results show that the yield strength and ultimate tensile strength of ODS alloy specimens were 1.2~1.7 times higher than those of the conventional Hastelloy^(TM) X(R), which has the same chemical compositions with ODS alloy specimens except the oxide particles.
참고문헌 (10)
- I.-S. Kim, , J. Kor. Inst. Met. Mater, 24, pp.10~ (2011)
- 김민철, "원자로 압력용기용 Mn-Mo-Ni계 및 Ni-Mo-Cr계 저합금강의 미세조직과 기계적 특성 비교", 대한금속·재료학회지, 48(3), pp.194~202 (2010), 대한금속·재료학회
- S. G. Druce, , Nucl. Energ, 19, pp.347~ (1980)
- B. Chapelle, , Nucl. Energy, 31, pp.417~ (1992)
- K. Suzuki, , Nucl. Eng. Design, 151, pp.523~ (1994)
- A. F. Rowcliffe, , J. Nucl. Mater, 392, pp.341~ (2009)
- 김익수, "나노사이즈-산화물 분산강화 Fe-17% Cr 페라이트계 합금의 고온인장 성질에 미치는 미세조직의 영향", 대한금속·재료학회지, 42(2), pp.109~116 (2004), 대한금속·재료학회
- 김익수, "기계적이로 합금화시킨 Fe-12-17% Cr 페라이트계 나노사이즈 산화물 분산강화합금의 강도특성", 대한금속·재료학회지, 41(6), pp.1~341 (2003), 대한금속·재료학회
- H. Tsuji, , J. Nucl. Mater, 151, pp.1~ (1987)
- H. Tsuji, , J. Nucl. Mater, 199, pp.43~ (1992)