STS 316L 소결체의 부식 저항 특성에 미치는 금속산화물 첨가의 영향
The Effect of Oxides Additives on Anti-corrosion Properties of Sintered 316L Stainless Steel
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
As wrought stainless steel, sintered stainless steel (STS) has excellent high-temperature anti-corrosion even at high temperature of 800ºC and exhibit corrosion resistance in air. The oxidation behavior and oxidation mechanism of the sintered 316L stainless was reported at the high temperature in our previous study. In this study, the effects of additives on high-temperature corrosion resistances were investigated above 800ºC at the various oxides (SiO2, Al2O3, MgO and Y2O3) added STS respectively as an oxidation inhibitor. The morphology of the oxide layers were observed by SEM and the oxides phase and composition were confirmed by XRD and EDX. As a result, the weight of STS 316L sintered body increased sharply at 1000oC and the relative density of specimen decreased as metallic oxide addition increased. Compared with STS 316L sintered parts, weight change ratio corresponding to different oxidation time at 900oC and 1000oC, decreased gradually with the addition of metallic oxide. The best corrosion resistance properties of STS could be improved in case of using Y2O3. The oxidation rate was diminished dramatically by suppression the peeling on oxide layers at Y2O3 added sintered stainless steel.
Abstract
As wrought stainless steel, sintered stainless steel (STS) has excellent high-temperature anti-corrosion even at high temperature of 800ºC and exhibit corrosion resistance in air. The oxidation behavior and oxidation mechanism of the sintered 316L stainless was reported at the high temperature in our previous study. In this study, the effects of additives on high-temperature corrosion resistances were investigated above 800ºC at the various oxides (SiO2, Al2O3, MgO and Y2O3) added STS respectively as an oxidation inhibitor. The morphology of the oxide layers were observed by SEM and the oxides phase and composition were confirmed by XRD and EDX. As a result, the weight of STS 316L sintered body increased sharply at 1000oC and the relative density of specimen decreased as metallic oxide addition increased. Compared with STS 316L sintered parts, weight change ratio corresponding to different oxidation time at 900oC and 1000oC, decreased gradually with the addition of metallic oxide. The best corrosion resistance properties of STS could be improved in case of using Y2O3. The oxidation rate was diminished dramatically by suppression the peeling on oxide layers at Y2O3 added sintered stainless steel.
참고문헌 (14)
- 이동복, "Fe-16Cr-6Ni-6Mn-1.7Mo 스테인리스 합금의 700~900℃에서의 대기중 산화", 대한금속·재료학회지, 49(2), pp.153~160 (2011), 대한금속·재료학회
- Y. Y. Lee, , Korean J. Met Mater., 32, pp.123~ (1994)
- A. Ferriere, , Solar Energy, 80, pp.1338~1343 (2006)
- A. Bautista, , Corrosion Science, 51, pp.785~792 (2009)
- 김혜성, "STS 316L 소결체의 대기중 고온산화 거동", 한국분말야금학회지, 20(6), pp.432~438 (2013), 한국분말야금학회
- A. Tiziani, , Corros. Sci., 45, pp.672~ (1990)
- A. Bautista, , Oxidation of Metals, 45, pp.1343~1354 (2003)
- C. -Y. Son, , Metall. Mater. Trans. A., 38, pp.2776~2787 (2007)
- A. V. C. Sobral, , Mater. Corros, 51, pp.791~ (2000)
- 강창룡, "심랭 처리된 오스템퍼드 구상흑연주철의 기계적 성질에 미치는 Cu의 영향", 대한금속·재료학회지, 41(1), pp.2~12 (2003), 대한금속·재료학회
- M. F. Pills, , Meterials Research., 9, pp.375~379 (2006)
- A. Bautista, , Corros. Sci., 45, pp.1343~ (2002)
- J. Botella, , Oxid. Met., 49, pp.297~ (1998)
- F. J. Perez, , Oxid. Met., 55, pp.165~ (2001)