복합 밀링 공정으로 제조된 산화물 분산 강화 강의 미세조직 및 고온 기계적 특성
Microstructure and High Temperature Mechanical Properties of Oxide Dispersion Strengthened Steels Manufactured by Combination Milling Process
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Oxide dispersion-strengthened (ODS) steel has excellent high-temperature properties, corrosion resistance, and oxidation resistance, and is expected to be applicable in various fields. Recently, various studies on mechanical alloying (MA) have been conducted for the dispersion of oxide particles in ODS steel with a high number density. In this study, ODS steel is manufactured by introducing a complex milling process in which planetary ball milling, cryogenic ball milling, and drum ball milling are sequentially performed, and the microstructure and high-temperature mechanical properties of the ODS steel are investigated. The microstructure observation revealed that the structure is stretched in the extrusion direction, even after the heat treatment. In addition, transmission electron microscopy (TEM) analysis confirmed the presence of oxide particles in the range of 5 to 10 nm. As a result of the room-temperature and high-temperature compression tests, the yield strengths were measured as 1430, 1388, 418, and 163 MPa at 25, 500, 700, and 900oC, respectively. Based on these results, the correlation between the microstructure and mechanical properties of ODS steel manufactured using the composite milling process is also discussed.
Abstract
Oxide dispersion-strengthened (ODS) steel has excellent high-temperature properties, corrosion resistance, and oxidation resistance, and is expected to be applicable in various fields. Recently, various studies on mechanical alloying (MA) have been conducted for the dispersion of oxide particles in ODS steel with a high number density. In this study, ODS steel is manufactured by introducing a complex milling process in which planetary ball milling, cryogenic ball milling, and drum ball milling are sequentially performed, and the microstructure and high-temperature mechanical properties of the ODS steel are investigated. The microstructure observation revealed that the structure is stretched in the extrusion direction, even after the heat treatment. In addition, transmission electron microscopy (TEM) analysis confirmed the presence of oxide particles in the range of 5 to 10 nm. As a result of the room-temperature and high-temperature compression tests, the yield strengths were measured as 1430, 1388, 418, and 163 MPa at 25, 500, 700, and 900oC, respectively. Based on these results, the correlation between the microstructure and mechanical properties of ODS steel manufactured using the composite milling process is also discussed.
참고문헌 (21)
- H. Oka, , J. Nucl. Mater, 547, pp.152833~ (2021)
- M. J. Alinger, , Acta Mater, 57, pp.392~ (2009)
- A. Hirata, , Nat. Mater, 23, pp.1~ (2011)
- 김영균, "산화물 분산 강화 강 분말이 첨가된 자동차 부품용 철계 복합소재의 미세조직 및 마모 특성", 한국분말재료학회지, 25(1), pp.36~42 (2018), 한국분말재료학회[DOI]
- Y. Hwang, , Korean J. Crystallography, 10, pp.145~ (1999)
- M. J. Alinger, , Acta Mater, 57, pp.392~ (2009)
- X. Mao, , J. Nucl. Mater, 428, pp.82~ (2012)
- Q. Zhao, , Adv. Powder Technol, 26, pp.1578~ (2015)
- J. H. Kim, , Mater. Sci. Eng. A, 559, pp.111~ (2013)
- J. H. Gwon, , J. Nucl. Mater, 459, pp.205~ (2015)
- J. H. Kim, , J. Nucl. Mater, 449, pp.300~ (2014)
- X. K. Zhu, , Scr. Mater, 49, pp.429~ (2003)
- C. S. Tiwary, , Metall. Mater. Trans. A, 44, pp.1917~ (2013)
- Y. K. Kim, , Arch. Metall. Mater, 62, pp.1335~ (2017)
- M. Dade, , J. Nucl. Mater, 472, pp.143~ (2016)
- H. K. D. H. Bhadeshia, , Mater. Sci. Eng. A, 223, pp.64~ (1997)
- R. Husák, , Metals, 9, pp.1148~ (2019)
- 설재복, "복합 밀링 공정에 따른 철계 산화물분산강화 합금의 미세조직 및 기계적 특성 변화 연구", 대한금속·재료학회지, 54(3), pp.171~179 (2016), 대한금속·재료학회[DOI]
- M. A. Auger, , J. Nucl. Mater, 442, pp.S142~ (2013)
- 김영균, "Fe-14Cr계 페라이틱 산화물 분산 강화강의 고온 압축 및 크리프 특성에 미치는 열처리의 영향", 대한금속·재료학회지, 55(12), pp.862~869 (2017), 대한금속·재료학회[DOI]
- W. Han, , Nucl. Mater. Energy, 9, pp.610~ (2016)