MA 316L ODS 및 Wet 316L ODS 스테인리스강에서 충격에너지에 미치는 소결 공정의 영향

Effects of the Sintering Variable on Impact Energy in MA 316L ODS and Wet 316L ODS Stainless Steels

2

조회

0

다운로드

0

인용

0

참고문헌

키워드

주제분류금속공학

초록

Two kinds of oxide-dispersion-strengthened (ODS) 316L stainless steel were manufactured using a wet mixing process(wet) and a mechanical alloying method (MA). An MA 316L ODS was prepared by a mixing of metal powder and a mechanical alloying process. A wet 316L ODS was manufactured by a wet mixing with 316L stainless steel powder. A solution of yttrium nitrate was dried after being in the wet 316L ODS alloy. The results showed that carbon and oxygen were effectively reduced during the degassing process before the hydroisostatic process (HIP) in both alloys. It appeared that the effect of HIP treatment on increase in impact energy was pronounced in the MA 316L ODS alloy. The MA 316L ODS alloy showed a higher yield strength and a smaller elongation, when compared to the wet 316L ODS alloy. This seemed to be attributed to the enhancement of bonding between oxide and matrix particles from HIP and to the presence of a finer oxide of about 20 nm from the MA process in the MA 316L ODS alloy.

Abstract

Two kinds of oxide-dispersion-strengthened (ODS) 316L stainless steel were manufactured using a wet mixing process(wet) and a mechanical alloying method (MA). An MA 316L ODS was prepared by a mixing of metal powder and a mechanical alloying process. A wet 316L ODS was manufactured by a wet mixing with 316L stainless steel powder. A solution of yttrium nitrate was dried after being in the wet 316L ODS alloy. The results showed that carbon and oxygen were effectively reduced during the degassing process before the hydroisostatic process (HIP) in both alloys. It appeared that the effect of HIP treatment on increase in impact energy was pronounced in the MA 316L ODS alloy. The MA 316L ODS alloy showed a higher yield strength and a smaller elongation, when compared to the wet 316L ODS alloy. This seemed to be attributed to the enhancement of bonding between oxide and matrix particles from HIP and to the presence of a finer oxide of about 20 nm from the MA process in the MA 316L ODS alloy.

참고문헌 (14)

  1. J. H. Hong, , Mechanic and Materials, 19, pp.6~ (2007)
  2. S. Ukai, , J. Nucl.Mater, 283, pp.702~ (2000)
  3. A. Alamo, , J. Nucl. Mater, 329, pp.333~ (2004)
  4. S. Yamashita, , J. Nucl. Mater, 329, pp.377~ (2004)
  5. T. Kariya, "Publication of patent applications", ~ (2003), JP2003-027109
  6. J. H. Ahn, , J. Alloy.Comp, 483, pp.247~ (2009)
  7. P. Shunmi, , Transaction of Metal Heat Treatment, 18, pp.346~ (1997)
  8. H. J. Ryu, "ANS Annual Meeting", pp.6~12 (2008), Anaheim
  9. C. Capdevila, , Adv.Eng. Mater, 3, pp.647~ (2001)
  10. H. Y. Kim, , Scrip. Mater, 54, pp.1703~ (2006)
  11. Y. Z. Shen, , Nuclear Engineering and Technology, 40, pp.99~ (2008)
  12. M. P. Phaniraj, , Acta. Mater, 57, pp.1856~ (2009)
  13. 김민호, "산화물 분산강화형 316L 스테인리스강의 제조와 특성 연구", 한국분말야금학회지, 16(2), pp.122~130 (2009), 한국분말야금학회
  14. G. E. Dieter, "Mechanical Metalurgy", pp.212~ (1986), McGraw Hill

관련 논문AI추천

이 간행물의 다른 논문 (8건)