Flexural strength and reliability of highly translucent colored zirconia
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Purpose: The purpose of this study was to evaluate the flexural strength and reliability of highly translucent colored zirconia for all ceramic restoration. Materials and Methods: Bar-shaped specimens (25 × 4 × 2.5 mm) were prepared from highly translucent monolithic zirconia. Three experimental groups were set up according to color (shade A0, A1, and A3). For each group, 20 specimens were prepared. Flexural strength was determined using a 3-point flexural test and results were analyzed with one-way ANOVA test. Weibull statistical analysis provided 2 parameter estimates: Weibull modulus and characteristic strength. X-ray diffraction (XRD) analysis was performed. Results: There was statistically significant difference between uncolored (Shade A0) and colored (shade A1 and A3) (P < 0.05), but there was no difference between colored groups (P > 0.05). The uncolored group had higher reliability compared with colored study groups. On x-ray diffraction analysis of each group, typical peaks of tetragonal phase appeared in all groups. Conclusion: Within the limitations of this in vitro study, coloring highly translucent zirconia had significant effect on flexural strength and reliability. Therefore, clinicians should be careful when using highly translucent colored zirconia to prevent breakage of veneering ceramic and enhance aesthetics. (J Dent Rehabil Appl Sci 2020;36(1):41-7)
Abstract
Purpose: The purpose of this study was to evaluate the flexural strength and reliability of highly translucent colored zirconia for all ceramic restoration. Materials and Methods: Bar-shaped specimens (25 × 4 × 2.5 mm) were prepared from highly translucent monolithic zirconia. Three experimental groups were set up according to color (shade A0, A1, and A3). For each group, 20 specimens were prepared. Flexural strength was determined using a 3-point flexural test and results were analyzed with one-way ANOVA test. Weibull statistical analysis provided 2 parameter estimates: Weibull modulus and characteristic strength. X-ray diffraction (XRD) analysis was performed. Results: There was statistically significant difference between uncolored (Shade A0) and colored (shade A1 and A3) (P < 0.05), but there was no difference between colored groups (P > 0.05). The uncolored group had higher reliability compared with colored study groups. On x-ray diffraction analysis of each group, typical peaks of tetragonal phase appeared in all groups. Conclusion: Within the limitations of this in vitro study, coloring highly translucent zirconia had significant effect on flexural strength and reliability. Therefore, clinicians should be careful when using highly translucent colored zirconia to prevent breakage of veneering ceramic and enhance aesthetics. (J Dent Rehabil Appl Sci 2020;36(1):41-7)
참고문헌 (25)
- Johansson C, "Fracture strength of monolithic allceramic crowns made of high translucent yttrium oxide-stabilized zirconium dioxide compared to porcelain-veneered crowns and lithium disilicate crowns", Acta Odontol Scand, 72, pp.145~153 (2014)
- Kim HK, "Effect of the number of coloring liquid applications on the optical properties of monolithic zirconia", Dent Mater, 30, pp.229~237 (2014)
- Inokoshi M, "Crystallographic and morphological analysis of sandblasted highly translucent dental zirconia", Dent Mater, 34, pp.508~518 (2018)
- Kaya G, "Production and characterization of selfcolored dental zirconia blocks", Ceram Int, 39, pp.511~517 (2013)
- 신수연, "ShadepilotTM을 이용한 색조 선택", 구강회복응용과학지, 23(2), pp.119~131 (2007), 대한턱관절교합학회
- Hjerppe J, "Effect of shading the zirconia framework on biaxial strength and surface microhardness", Acta Odontol Scand, 66, pp.262~267 (2008)
- Zhang F, "Strength, toughness and aging stability of highly-translucent YTZP ceramics for dental restorations", Dent Mater, 32, pp.e327~e337 (2016)
- Zhang Y, "Making yttria-stabilized tetragonal zirconia translucent", Dent Mater, 30, pp.1195~1203 (2014)
- "ISO 6872:2008. Dentistry - Ceramic materials"[URL]
- Siarampi E, "Flexural strength and the probability of failure of cold isostatic pressed zirconia core ceramics", J Prosthet Dent, 108, pp.84~95 (2012)
- Garcia Fonseca R, "Effect of particle size on the flexural strength and phase transformation of an airborne-particle abraded yttria-stabilized tetragonal zirconia polycrystal ceramic", J Prosthet Dent, 110, pp.510~514 (2013)
- Weibull W, "A statistical distribution function of wide applicability", J Appl Mech, 18, pp.293~297 (1951)
- Ritter JE, "Predicting lifetimes of materials and material structures", Dent Mater, 11, pp.142~146 (1995)
- Kittl P, "Weibull’s fracture statistics or probabilistic strength of materials : state of the art", Res Mechanica, 24, pp.99~207 (1988)
- Garvie RC, "Phase analysis in zirconia systems", J Am Ceram Soc, 55, pp.303~305 (1972)
- Toraya H, "Calibration curve for quantitative analysis of the monoclinictetragonal ZrO2 system by x-ray diffraction", J Am Ceram Soc, 67, pp.119~121 (1984)
- Guess PC, "All-ceramic systems : laboratory and clinical performance", Dent Clin North Am, 55, pp.333~352 (2011)
- Håff A, "A retrospective evaluation of zirconia-fixed partial dentures in general practices : an up to 13-year study", Dent Mater, 31, pp.162~170 (2015)
- Stefanescu C, "Survival rates and complications for zirconia-based fixed dental prostheses in a period up to 10 years : a systematic review", Eur J Prosthodont Restor Dent, 26, pp.54~61 (2018)
- Tong H, "Characterization of three commercial Y-TZP ceramics produced for their high-translucency, high-strength and high surface area", Ceram Int, 42, pp.1077~1085 (2016)
- Ferrario VF, "Maximal bite forces in healthy young adults as predicted by surface electromyography", J Dent, 32, pp.451~457 (2004)
- Guazzato M, "Influence of surface and heat treatments on the flexural strength of Y-TZP dental ceramic", J Dent, 33, pp.9~18 (2005)
- Spyropoulou PE, "Composition, phase analysis, biaxial flexural strength, and fatigue of unshaded versus shaded Procera zirconia ceramic", J Prosthet Dent, 116, pp.269~276 (2016)
- Wen N, "The color of Fe2O3 and Bi2O3pigmented dental zirconia ceramic", Key Engineering Materials, 434, pp.582~585 (2010)
- Ozer F, "Effect of thickness and surface modifications on flexural strength of monolithic zirconia", J Prosthet Dent, 119, pp.987~993 (2018)