Comparative study of surface modification on bond strength of polyetherketoneketone adhesively bonded to resins for temporary restoration
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Purpose: The purpose was to compare shear bond strength (SBS) of three types of resin for temporary restoration to polyether- ketoneketone (PEKK) depending on surface modification. Materials and Methods: Sixty disks made from PEKK were air-abraded with 110 μm alumina particles (Cobra, Renfert GmbH, Hilzinge, Germany) and thirty specimens were divided into two groups each: PEKK without Visio.link (Bredent, Senden, Germany)(U) and with Visio.link (P). Resins for temporary restoration (polymethylmethac- rylate; PMMA, polyethylmethacrylate; PEMA, bis-acryl composite resin) in the shape of a square with one side 3.2 mm were bonded to PEKK twenty respectively and classified into six groups (UM, UE, UC, PM, PE and PC). All specimens were stored in distilled water at 37°C for 24 hours. SBS of each group was measured at a crosshead speed of 2 mm/min in universal testing machine. SBS was compared using one-way ANOVA and a Tukey HSD test (P = 0.05). Results: Group UM and group UE showed a significant difference in SBS with group UC (P < 0.05). Group PC showed a significant increase in SBS than group UC (P < 0.05). Conclusion: It is recom- mended to apply Visio.link to PEKK for adhering bis-acrylic composite resin, but not for PMMA and PEMA in clinical practice. (J Dent Rehabil Appl Sci 2020;36(1):1-11)
Abstract
Purpose: The purpose was to compare shear bond strength (SBS) of three types of resin for temporary restoration to polyether- ketoneketone (PEKK) depending on surface modification. Materials and Methods: Sixty disks made from PEKK were air-abraded with 110 μm alumina particles (Cobra, Renfert GmbH, Hilzinge, Germany) and thirty specimens were divided into two groups each: PEKK without Visio.link (Bredent, Senden, Germany)(U) and with Visio.link (P). Resins for temporary restoration (polymethylmethac- rylate; PMMA, polyethylmethacrylate; PEMA, bis-acryl composite resin) in the shape of a square with one side 3.2 mm were bonded to PEKK twenty respectively and classified into six groups (UM, UE, UC, PM, PE and PC). All specimens were stored in distilled water at 37°C for 24 hours. SBS of each group was measured at a crosshead speed of 2 mm/min in universal testing machine. SBS was compared using one-way ANOVA and a Tukey HSD test (P = 0.05). Results: Group UM and group UE showed a significant difference in SBS with group UC (P < 0.05). Group PC showed a significant increase in SBS than group UC (P < 0.05). Conclusion: It is recom- mended to apply Visio.link to PEKK for adhering bis-acrylic composite resin, but not for PMMA and PEMA in clinical practice. (J Dent Rehabil Appl Sci 2020;36(1):1-11)
참고문헌 (35)
- Kurtz SM, "PEEK biomaterials in trauma, orthopedic, and spinal implants", Biomaterials, 28, pp.4845~4869 (2007)
- Fuhrmann G, "Resin bonding to three types of polyaryletherketones(PAEKs)-durability and influence of surface conditioning", Dent Mater, 30, pp.357~363 (2014)
- Williams DF, "Potential of polyetheretherketone(PEEK)and carbon-fibrereinforced PEEK in medical applications", J Mater Sci Lett, 6, pp.188~190 (1987)
- Stawarczyk B, "Tensile bond strength of veneering resins to PEEK : impact of different adhesives", Dent Mater J, 32, pp.441~448 (2013)
- Liebermann A, "Physicomechanical characterization of polyetheretherketone and current esthetic dental CAD", CAM polymers after aging in different storage media, 2016, pp.115, 321~328
- Wimmer T, "Two-body wear rate of PEEK, CAD", CAM resin composite and PMMA : Effect of specimen geometries, antagonist materials and test set-up configuration, 2016, pp.32, e127~e136
- Geringer J, "Wear behavior of PAEK, poly (aryl-ether-ketone), under physiological conditions, outlooks for performing these materials in the field of hip prosthesis", Wear, 271, pp.2793~2803 (2011)
- Bae SY, "Three-dimensional analysis of marginal and internal fit of copings fabricated with polyetherketoneketone(PEKK)and zirconia", J Prosthodont Res, 61, pp.106~112 (2017)
- Lee KS, "Biomechanical evaluation of a tooth restored with high performance polymer PEKK post-core system : a 3D finite element analysis", Biomed Res Int, 2017, pp.1373127~ (2017)
- Han KH, "Implant-and tooth-supported fixed prostheses using a high-performance polymer(Pekkton)framework", Int J Prosthodont, 29, pp.451~454 (2016)
- Zoidis P, "Modified PEEK resinbonded fixed dental prosthesis as an interim restoration after implant placement", J Prosthet Dent, 116, pp.637~641 (2016)
- Tannous F, "Retentive forces and fatigue resistance of thermoplastic resin clasps", Dent Mater, 28, pp.273~278 (2012)
- Burns DR, "A review of selected dental literature on contemporary provisional fixed prosthodontic treatment: report of the Committee on Research in Fixed Prosthodontics of the Academy of Fixed Prosthodontics", J Prosthet Dent, 90, pp.474~497 (2003)
- Vallittu PK, "The effect of glass fiber reinforcement on the fracture resistance of a provisional fixed partial denture", J Prosthet Dent, 79, pp.125~130 (1998)
- Kim JY, "Effect of laboratory procedures and thermocycling on the shear bond strength of resin-metal bonding systems", J Prosthet Dent, 90, pp.184~189 (2003)
- Tetelman ED, "A new transitional abutment for immediate aesthetics and function", Implant Dent, 17, pp.51~58 (2008)
- Wittneben JG, "Periimplant soft tissue conditioning with provisional restorations in the esthetic zone : the dynamic compression technique", Int J Periodontics Restorative Dent, 33, pp.447~455 (2013)
- Harder S, "Provisional treatment and soft tissue conditioning before and after implantation for single tooth replacement", Implantologie, 18, pp.407~415 (2010)
- Hallmann L, "The improvement of adhesive properties of PEEK through different pre-treatments", Appl Surf Sci, 258, pp.7213~7218 (2012)
- Keul C, "Influence of PEEK surface modification on surface properties and bond strength to veneering resin composites", J Adhes Dent, 16, pp.383~392 (2014)
- Sproesser O, "Work of adhesion between resin composite cements and PEEK as a function of etching duration with sulfuric acid and its correlation with bond strength values", Int J Adhes Adhes, 54, pp.184~190 (2014)
- Sproesser O, "Effect of sulfuric acid etching of polyetheretherketone on the shear bond strength to resin cements", J Adhes Dent, 16, pp.465~472 (2014)
- Stawarczyk B, "Effect of different surface pretreatments and adhesives on the load-bearing capacity of veneered 3-unit PEEK FDPs", J Prosthet Dent, 114, pp.666~673 (2015)
- Stawarczyk B, "PEEK surface treatment effects on tensile bond strength to veneering resins", J Prosthet Dent, 112, pp.1278~1288 (2014)
- Stawarczyk B, "Influence of plasma pretreatment on shear bond strength of self-adhesive resin cements to polyetheretherketone", Clin Oral Investig, 18, pp.163~170 (2014)
- Stawarczyk B, "Tensile bond strength of veneering resins to PEEK : impact of different adhesives", Dent Mater J, 32, pp.441~448 (2013)
- Mondragon E, "Shear Strength of Dentin and Dentin Bonded Composites", J Adhes Dent, 3, pp.227~236 (2001)
- Oliveira ACC, "Influence of chisel width on shear bond strength of composite to enamel", Rev odonto Ciênc, 24, pp.19~21 (2009)
- Sinhoreti MA, "Influence of loading types on the shear strength of the dentin-resin interface bonding", J Mater Sci Mater Med, 12, pp.39~44 (2001)
- Stawarczyk B, "Bonding of composite resins to PEEK : the influence of adhesive systems and airabrasion parameters", Clin Oral Investig, 22, pp.763~771 (2018)
- Lümkemann N, "Impact of air-abrasion pressure and adhesive systems on bonding parameters for polyetheretherketone dental restorations", Int J Adhes Adhes, 80, pp.30~38 (2018)
- Kern M, "Influence of surface conditioning on bonding to polyetheretherketon(PEEK)", Dent Mater, 28, pp.1280~1283 (2012)
- Stawarczyk B, "Bonding Behaviour of Polyetherketoneketone to Methylmethacrylate-and Dimethacrylate-based Polymers", J Adhes Dent, 19, pp.331~338 (2017)
- Silthampitag P, "Effect of surface pretreatments on resin composite bonding to PEEK", Dent Mater J, 35, pp.668~674 (2016)
- Schmidlin PR, "Effect of different surface pre-treatments and luting materials on shear bond strength to PEEK", Dent Mater, 26, pp.553~559 (2010)