The influence of fitness and type of luting agents on bonding strength of fiber-reinforced composite resin posts
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Purpose: A mismatched size in the post and post space is a common problem during post-fixation. Since this discordance affects the bonding strength of the fiber-reinforced composite resin post (FRC Post), a corresponding luting agent is required. The aim of this study was to evaluate the bonding strength of the FRC post according to the fitness of the fiber post and the type of luting agent. Materials and Methods: Thirty mandibular premolar were endodontic-treated and assigned to two groups according to their prepared post space: Fitting (F) and Mismatching (M). These groups were further classified into three subgroups according to their luting agent: RelyX Unicem (ReX), Luxacore dual (Lux), and Duolink (Duo). A push-out test was performed to measure the push-out bond strengths. The fractured surfaces of each cross-section were then examined, and the fracture modes were classified. Results: In the ReX and Duo subgroups, the F group had a higher mean bond strength; however, the Lux subgroup had no significant difference between the F and M groups. In the analysis of the failure modes, the ReX subgroup had only adhesive failures between the cement and dentin. Conclusion: The result of this study showed that the bond strength of an FRC post was influenced by the type of luting agent and the mismatch between the diameter of the prepared post space and that of the post.
Abstract
Purpose: A mismatched size in the post and post space is a common problem during post-fixation. Since this discordance affects the bonding strength of the fiber-reinforced composite resin post (FRC Post), a corresponding luting agent is required. The aim of this study was to evaluate the bonding strength of the FRC post according to the fitness of the fiber post and the type of luting agent. Materials and Methods: Thirty mandibular premolar were endodontic-treated and assigned to two groups according to their prepared post space: Fitting (F) and Mismatching (M). These groups were further classified into three subgroups according to their luting agent: RelyX Unicem (ReX), Luxacore dual (Lux), and Duolink (Duo). A push-out test was performed to measure the push-out bond strengths. The fractured surfaces of each cross-section were then examined, and the fracture modes were classified. Results: In the ReX and Duo subgroups, the F group had a higher mean bond strength; however, the Lux subgroup had no significant difference between the F and M groups. In the analysis of the failure modes, the ReX subgroup had only adhesive failures between the cement and dentin. Conclusion: The result of this study showed that the bond strength of an FRC post was influenced by the type of luting agent and the mismatch between the diameter of the prepared post space and that of the post.
참고문헌 (15)
- Malferrari S, "Clinical evaluation of teeth restored with quartz fiber-reinforced epoxy resin posts", Int J Prosthodont, 16, pp.39~44 (2003)
- Asmussen E, "Stiffness, elastic limit, and strength of newer types of endodontic posts", J Dent, 27, pp.275~278 (1999)
- Torbjörner A, "Survival rate and failure characteristics for two post designs", J Prosthet Dent, 73, pp.439~444 (1995)
- Grandini S, "Fatigue resistance and structural characteristics of fiber posts : three-point bending test and SEM evaluation", Dent Mater, 21, pp.75~82 (2005)
- Moosavi H, "Fracture resistance of endodontically-treated teeth restored using three root-reinforcement methods", J Contemp Dent Pract, 9, pp.30~37 (2008)
- Erkut S, "Microleakage in overflared root canals restored with different fiber reinforced dowels", Oper Dent, 33, pp.96~105 (2008)
- Perdigão J, "The effect of dowel space on the bond strengths of fiber posts", J Prosthodont, 16, pp.154~164 (2007)
- D’Arcangelo C, "The effect of resin cement film thickness on the pullout strength of a fiber-reinforced post system", J Prosthet Dent, 98, pp.193~198 (2007)
- Nissan J, "The use of reinforced composite resin cement as compensation for reduced post length", J Prosthet Dent, 86, pp.304~308 (2001)
- Barfeie A, "Failure Mechanisms of Fibre Posts : A Literature Review", Eur J Prosthodont Restor Dent, 23, pp.115~127 (2015)
- Goracci C, "Evaluation of the adhesion of fiber posts to intraradicular dentin", Oper Dent, 30, pp.627~635 (2005)
- Bouillaguet S, "Microtensile bond strength between adhesive cements and root canal dentin", Dent Mater, 19, pp.199~205 (2003)
- Tay FR, "Variability in microleakage observed in a total-etch wetbonding technique under different handling conditions", J Dent Res, 74, pp.1168~1178 (1995)
- Goracci C, "The contribution of friction to the dislocation resistance of bonded fiber posts", J Endod, 31, pp.608~612 (2005)
- Hayashi M, "The root canal bonding of chemical-cured total-etch resin cements", J Endod, 34, pp.583~586 (2008)