Purpose: This study aimed to evaluate the influence of surface sealants on the surface roughness of composite resins. Materials and Methods: The study used microfilled composite resin (Metafil CX, Sun Medical Co.) and hybrid composite resin (Aelite™ LS posterior, Bisco). Sixty specimens (8 mm in diameter and 4 mm in height) of each composite resin type were prepared and divided into 3 groups. Each specimen was ground with 600, 1000, and 2000-grit sandpaper. The Surface roughness (Ra) values were measured using a surface roughness tester (SJ-301, Mytutoyo) before and after surface sealant application. Surface sealants, BisCover™ LV (Bisco), Optiguard® (Kerr), and Seal-n-Shine™ (Pulpdent), were applied to the specimens, as instructed and observed by scanning electron microscope (JSM-7500, JEOL) and atomic force microscope (MultiMode IV, Veeco Instruments). Results: Specimens ground with 600-grit sandpaper coated with surface sealants exhibited significantly lower Ra values than the untreated group (P < 0.05). Specimens ground with 1000 and 2000-grit sandpaper showed statistically no difference. There was no significant difference in surface roughness among BisCover™ LV, Optiguard®, and Seal-n-Shine™. SEM and AFM revealed remarkably decreased micro-defects on the surfaces of composite resins after surface sealant application. Conclusion: Surface sealants can influence surface roughness when applied on the rough surface of composite resins but not on highly polished composite resins.
Abstract
Purpose: This study aimed to evaluate the influence of surface sealants on the surface roughness of composite resins. Materials and Methods: The study used microfilled composite resin (Metafil CX, Sun Medical Co.) and hybrid composite resin (Aelite™ LS posterior, Bisco). Sixty specimens (8 mm in diameter and 4 mm in height) of each composite resin type were prepared and divided into 3 groups. Each specimen was ground with 600, 1000, and 2000-grit sandpaper. The Surface roughness (Ra) values were measured using a surface roughness tester (SJ-301, Mytutoyo) before and after surface sealant application. Surface sealants, BisCover™ LV (Bisco), Optiguard® (Kerr), and Seal-n-Shine™ (Pulpdent), were applied to the specimens, as instructed and observed by scanning electron microscope (JSM-7500, JEOL) and atomic force microscope (MultiMode IV, Veeco Instruments). Results: Specimens ground with 600-grit sandpaper coated with surface sealants exhibited significantly lower Ra values than the untreated group (P < 0.05). Specimens ground with 1000 and 2000-grit sandpaper showed statistically no difference. There was no significant difference in surface roughness among BisCover™ LV, Optiguard®, and Seal-n-Shine™. SEM and AFM revealed remarkably decreased micro-defects on the surfaces of composite resins after surface sealant application. Conclusion: Surface sealants can influence surface roughness when applied on the rough surface of composite resins but not on highly polished composite resins.
참고문헌 (14)
- Teixera EC, "In vitro toothbrush-dentifrice abrasion of two restorative composites", J Esthet Restor Dent, 17, pp.172~180 (2005)
- Stoddard JW, "An evaluation of polishing agents for composite resins", J Prosthet Dent, 65, pp.491~495 (1991)
- Pratten DH, "An evaluation of finishing instruments for an anterior and a posterior composite", J Prosthet Dent, 60, pp.154~158 (1988)
- Shinkai K, "Effect of surface-penetrating sealant on wear resistance of luting agents", Quintessence Int, 25, pp.767~771 (1994)
- Dickinson GL, "Effect of surface penetrating sealant on wear rate of posterior composite resins", J Am Dent Assoc, 121, pp.251~255 (1990)
- Reid JS, "The effect of bonding agent and fissure sealant on microleakage of composite resin restorations", Quintessence Int, 22, pp.295~298 (1991)
- Ramos RP, "Assessing microleakage in resin composite restorations rebonded with a surface sealant and three lowviscosity resin systems", Quintessence Int, 33, pp.450~456 (2002)
- Sarac D, "The effect of polishing techniques on the surface roughness and color change of composite resins", J Prosthet Dent, 96, pp.33~40 (2006)
- Bollen CM, "Comparison of surface roughness of oral hard materials to the threshold surface roughness for bacterial plaque retention : a review of the literature", Dent Mater, 13, pp.258~269 (1997)
- Seghi RR, "Spectrophotometric analysis of color differences between porcelain systems", J Prosthet Dent, 56, pp.35~40 (1986)
- Ramos RP, "Effect of three surface sealants on marginal sealing of class V composite resin restorations", Oper Dent, 25, pp.448~453 (2000)
- Kawai K, "Effect of surface-pen-etrating sealant on composite wear", Dent Mater, 9, pp.108~113 (1993)
- Rueggeberg FA, "The effect of oxygen inhibition on an unfilled", filled composite system, 1990, pp.69, 1652~1658
- Yao K, "SEM observation for composite resin filler", Shoni Shikagaku Zasshi, 28, pp.918~927 (1990)