Push-out bond strengths of fiber-reinforced composite posts with various resin cements according to the root level
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
PURPOSE. The aim of this study was to determine whether the push-out bond strengths between the radicular dentin and fiber reinforced-composite (FRC) posts with various resin cements decreased or not, according to the coronal, middle or apical level of the root. MATERIALS AND METHODS. FRC posts were cemented with one of five resin cement groups (RelyX Unicem: Uni, Contax with activator & LuxaCore-Dual: LuA, Contax & LuxaCore-Dual: Lu, Panavia F 2.0: PA, Super-Bond C&B: SB) into extracted human mandibular premolars. The roots were sliced into discs at the coronal, middle and apical levels. Push-out bond strength tests were performed with a universal testing machine at a crosshead speed of 0.5 mm/min, and the failure aspect was analyzed. RESULTS. There were no significant differences (P>.05) in the bond strengths of the different resin cements at the coronal level, but there were significant differences in the bond strengths at the middle and apical levels (P<.05). Only the Uni and LuA cements did not show any significant decrease in their bond strengths at all the root levels (P>.05); all other groups had a significant decrease in bond strength at the middle or apical level (P<.05). The failure aspect was dominantly cohesive at the coronal level of all resin cements (P<.05), whereas it was dominantly adhesive at the apical level. CONCLUSION. All resin cement groups showed decreases in bond strengths at the middle or apical level except LuA and Uni.
Abstract
PURPOSE. The aim of this study was to determine whether the push-out bond strengths between the radicular dentin and fiber reinforced-composite (FRC) posts with various resin cements decreased or not, according to the coronal, middle or apical level of the root. MATERIALS AND METHODS. FRC posts were cemented with one of five resin cement groups (RelyX Unicem: Uni, Contax with activator & LuxaCore-Dual: LuA, Contax & LuxaCore-Dual: Lu, Panavia F 2.0: PA, Super-Bond C&B: SB) into extracted human mandibular premolars. The roots were sliced into discs at the coronal, middle and apical levels. Push-out bond strength tests were performed with a universal testing machine at a crosshead speed of 0.5 mm/min, and the failure aspect was analyzed. RESULTS. There were no significant differences (P>.05) in the bond strengths of the different resin cements at the coronal level, but there were significant differences in the bond strengths at the middle and apical levels (P<.05). Only the Uni and LuA cements did not show any significant decrease in their bond strengths at all the root levels (P>.05); all other groups had a significant decrease in bond strength at the middle or apical level (P<.05). The failure aspect was dominantly cohesive at the coronal level of all resin cements (P<.05), whereas it was dominantly adhesive at the apical level. CONCLUSION. All resin cement groups showed decreases in bond strengths at the middle or apical level except LuA and Uni.
참고문헌 (42)
- Schwartz RS, "Post placement and restoration of endodontically treated teeth: a literature review", J Endod, 30, pp.289~301 (2004)
- Sorensen JA, "Ferrule design and fracture resistance of endodontically treated teeth", J Prosthet Dent, 63, pp.529~536 (1990)
- Akkayan B, "Resistance to fracture of endodontically treated teeth restored with different post systems", J Prosthet Dent, 87, pp.431~437 (2002)
- Bae JM, "Fatigue strengths of particulate filler composites reinforced with fibers", Dent Mater J, 23, pp.166~174 (2004)
- Jung SH, "Microleakage and fracture patterns of teeth restored with different posts under dynamic loading", J Prosthet Dent, 98, pp.270~276 (2007)
- Mezzomo E, "Fracture resistance of teeth restored with two different post-and-core designs cemented with two different cements: an in vitro study. Part I", Quintessence Int, 34, pp.301~306 (2003)
- Drummond JL, "Thermal and cyclic loading of endodontic posts", Eur J Oral Sci, 107, pp.220~224 (1999)
- Mannocci F, "Intermittent loading of teeth restored using quartz fiber, carbon-quartz fiber, and zirconium dioxide ceramic root canal posts", J Adhes Dent, 1, pp.153~158 (1999)
- Viguie G, "Epoxy", carbon composite resins in dentistry: mechanical properties related to fiber reinforcements, 1994, pp.72, 245~249
- Vallittu PK, "Prosthodontic treatment with a glass fiber-reinforced resin-bonded fixed partial denture: A clinical report", J Prosthet Dent, 82, pp.132~135 (1999)
- Duarte S Jr, "Microtensile bond strengths and scanning electron microscopic evaluation of self-adhesive and self-etch resin cements to intact and etched enamel", J Prosthet Dent, 100, pp.203~210 (2008)
- Krämer N, "Adhesive luting of indirect restorations", Am J Dent, 13, pp.60~76 (2000)
- Özcan M, "Adhesion of conventional and simplified resin-based luting cements to superficial and deep dentin", Clin Oral Investig, 16, pp.1081~1088 (2012)
- Li N, "The role of functional monomers in bonding to enamel: acid-base resistant zone and bonding performance", J Dent, 38, pp.722~730 (2010)
- Ramos MB, "Effects of curing protocol and storage time on the microhardness of resin cements used to lute fiber-reinforced resin posts", J Appl Oral Sci, 20, pp.556~562 (2012)
- Sigemori RM, "Curing depth of a resin-modified glass ionomer and two resin-based luting agents", Oper Dent, 30, pp.185~189 (2005)
- Ritter AV, "Dentin and enamel bond strengths of dual-cure composite luting agents used with dual-cure dental adhesives", J Dent, 37, pp.59~64 (2009)
- Bell AM, "Bonding of fibre-reinforced composite post to root canal dentin", J Dent, 33, pp.533~539 (2005)
- Benetti AR, "Influence of curing rate of resin composite on the bond strength to dentin", Oper Dent, 32, pp.144~148 (2007)
- Bitter K, "Effects of luting agent and thermocycling on bond strengths to root canal dentine", Int Endod J, 39, pp.809~818 (2006)
- Bitter K, "In vitro evaluation of push-out bond strengths of various luting agents to tooth-colored posts", J Prosthet Dent, 95, pp.302~310 (2006)
- D’'Arcangelo C, "The effect of resin cement film thickness on the pullout strength of a fiber-reinforced post system", J Prosthet Dent, 98, pp.193~198 (2007)
- Ramin Mosharraf, "Comparative evaluation of effects of different surface treatment methods on bond strength between fiber post and composite core", The Journal of Advanced of Prosthodontics, 4(2), pp.103~108 (2012), 대한치과보철학회
- Khamverdi Zahra, "Effect of ascorbic acid, ethanol and acetone on adhesion between the treated fiber posts and composite resin cores", The Journal of Advanced of Prosthodontics, 4(4), pp.187~191 (2012), 대한치과보철학회
- International Standards Organization, "ISO", TS 11405:2003(E) Dental materials - Testing of adhesion to tooth structure, 2003
- Vallittu PK, "Flexural properties of acrylic resin polymers re-inforced with unidirectional and woven glass fibers", J Prosthet Dent, 81, pp.318~326 (1999)
- Carvalho CA, "Push-out bond strength and SEM evaluation of a new bonding approach into the root canal", J Appl Oral Sci, 20, pp.613~619 (2012)
- Gaston BA, "Evaluation of regional bond strength of resin cement to endodontic surfaces", J Endod, 27, pp.321~324 (2001)
- Foxton RM, "Adhesion to root canal dentine using one and two-step adhesives with dual-cure composite core materials", J Oral Rehabil, 32, pp.97~104 (2005)
- Pereira PC, "The adhesive system and root canal region do not influence the degree of conversion of dual resin cement", J Appl Oral Sci, 18, pp.477~481 (2010)
- Teixeira CS, "Bond strength of fiber posts to weakened roots after resin restoration with different light-curing times", J Endod, 35, pp.1034~1039 (2009)
- Mallmann A, "Microtensile bond strength of light- and self-cured adhesive systems to intraradicular dentin using a translucent fiber post", Oper Dent, 30, pp.500~506 (2005)
- Bouillaguet S, "Microtensile bond strength between adhesive cements and root canal dentin", Dent Mater, 19, pp.199~205 (2003)
- Perdigão J, "The effect of silane on the bond strengths of fiber posts", Dent Mater, 22, pp.752~758 (2006)
- Acquaviva PA, "Degree of conversion of three composite materials employed in the adhesive cementation of indirect restorations: a micro-Raman analysis", J Dent, 37, pp.610~615 (2009)
- Feilzer AJ, "Setting stresses in composites for two different curing modes", Dent Mater, 9, pp.2~5 (1993)
- Kato H, "Effect of etching and sandblasting on bond strength to sintered porcelain of unfilled resin", J Oral Rehabil, 27, pp.103~110 (2000)
- Radovic I, "Self-adhesive resin cements: a literature review", J Adhes Dent, 10, pp.251~258 (2008)
- Barkmeier WW, "Laboratory evaluation of adhesive systems", Oper Dent, (5), pp.50~61 (1992)
- Staninec M, "Adhesion and microleakage tests of a new dentin bonding system", Dent Mater, 9, pp.204~208 (1993)
- Watanabe I, "Pashley DH. Bonding to ground dentin by a phenyl-P self-etching primer", J Dent Res, 73, pp.1212~1220 (1994)
- Gomes AL, "Influence of sandblasting granulometry and resin cement composition on microtensile bond strength to zirconia ceramic for dental prosthetic frameworks", J Dent, 41, pp.31~41 (2013)