Objectives: In this study, we evaluated the influence of different radiant exposures provided by single-peak and polywave light-curing units (LCUs) on the degree of conversion (DC) and the mechanical properties of resin cements. Materials and Methods: Six experimental groups were established for each cement (RelyX ARC, 3M ESPE; LuxaCore Dual, Ivoclar Vivadent; Variolink, DMG), according to the different radiant exposures (5, 10, and 20 J/cm2) and two LCUs (single-peak and polywave). The specimens were made (7 mm in length × 2 mm in width × 1 mm in height) using silicone molds. After 24 hours of preparation, DC measurement was performed using Fourier transform infrared spectrometry. The same specimens were used for the evaluation of mechanical properties (flexural strength, FS; elastic modulus, E) by a three-point bending test. Data were assessed for normality, after which twoway analysis of variance (ANOVA) and post hoc Tukey’s test were performed. Results: No properties of the Variolink cement were influenced by any of the considered experimental conditions. In the case of the RelyX ARC cement, DC was higher when polywave LCU was used; FS and E were not influenced by the conditions evaluated. The LuxaCore cement showed greater sensitivity to the different protocols. Conclusions: On the basis of these results, both the spectrum of light emitted and the radiant exposure used could affect the properties of resin cements. However, the influence was materialdependent.
Abstract
Objectives: In this study, we evaluated the influence of different radiant exposures provided by single-peak and polywave light-curing units (LCUs) on the degree of conversion (DC) and the mechanical properties of resin cements. Materials and Methods: Six experimental groups were established for each cement (RelyX ARC, 3M ESPE; LuxaCore Dual, Ivoclar Vivadent; Variolink, DMG), according to the different radiant exposures (5, 10, and 20 J/cm2) and two LCUs (single-peak and polywave). The specimens were made (7 mm in length × 2 mm in width × 1 mm in height) using silicone molds. After 24 hours of preparation, DC measurement was performed using Fourier transform infrared spectrometry. The same specimens were used for the evaluation of mechanical properties (flexural strength, FS; elastic modulus, E) by a three-point bending test. Data were assessed for normality, after which twoway analysis of variance (ANOVA) and post hoc Tukey’s test were performed. Results: No properties of the Variolink cement were influenced by any of the considered experimental conditions. In the case of the RelyX ARC cement, DC was higher when polywave LCU was used; FS and E were not influenced by the conditions evaluated. The LuxaCore cement showed greater sensitivity to the different protocols. Conclusions: On the basis of these results, both the spectrum of light emitted and the radiant exposure used could affect the properties of resin cements. However, the influence was materialdependent.
참고문헌 (32)
- Carvalho AP, "Analysis of the microtensile bond strength to enamel of two adhesive systems polymerized by halogen light or LED", Braz Oral Res, 19, pp.307~311 (2005)
- Dunn WJ, "Polymerization of orthodontic resin cement with light emitting diode curing units", Am J Orthod Dentofacial Orthop, 122, pp.236~241 (2002)
- Arrais CA, "Degree of conversion of adhesive systems light-cured by LED and halogen light", Braz Dent J, 18, pp.54~59 (2007)
- Jiménez-Planas A, "Developments in polymerization lamps", Quintessence Int, 39, pp.e74~e84 (2008)
- Jandt KD, "A brief history of LED photopolymerization", Dent Mater, 29, pp.605~617 (2013)
- Santini A, "Degree of conversion and microhardness of TPO-containing resinbased composites cured by polywave and monowave LED units", J Dent, 40, pp.577~584 (2012)
- Dressano D, "Effect of diphenyliodonium hexafluorophosphate on the physical and chemical properties of ethanolic solvated resins containing camphorquinone and 1-phenyl-1,2-propanedione sensitizers as initiators", Dent Mater, 32, pp.756~764 (2016)
- Meereis CT, "BAPO as an alternative photoinitiator for the radical polymerization of dental resins", Dent Mater, 30, pp.945~953 (2014)
- Schneider LF, "Curing efficiency of dental resin composites formulated with camphorquinone or trimethylbenzoyl-diphenyl-phosphine oxide", Dent Mater, 28, pp.392~397 (2012)
- Arrais CA, "Kinetic analysis of monomer conversion in auto- and dual-polymerizing modes of commercial resin luting cements", J Prosthet Dent, 101, pp.128~136 (2009)
- Gaglianone LA, "Mechanical properties and degree of conversion of etch-and-rinse and self-etch adhesive systems cured by a quartz tungsten halogen lamp and a light-emitting diode", J Mech Behav Biomed Mater, 12, pp.139~143 (2012)
- Jandt KD, "Depth of cure and compressive strength of dental composites cured with blue light emitting diodes (LEDs)", Dent Mater, 16, pp.41~47 (2000)
- Nakamura T, "Mechanical properties of new self-adhesive resin-based cement", J Prosthodont Res, 54, pp.59~64 (2010)
- Faria-e-Silva AL, "Degree of conversion of etch-and-rinse and selfetch adhesives light-cured using QTH or LED", Oper Dent, 35, pp.649~654 (2010)
- Gaglianone LA, "Influence of different shades and LED irradiance on the degree of conversion of composite resins", Braz Oral Res, 26, pp.165~169 (2012)
- Lima AF, "Influence of light source and extended time of curing on microhardness and degree of conversion of different regions of a nanofilled composite resin", Eur J Dent, 6, pp.153~157 (2012)
- Lima AF, "Effect of surface sealants on microleakage of Class II restorations after thermocycling and long-term water storage", J Adhes Dent, 13, pp.249~254 (2011)
- De Goes MF, "Microtensile bond strength between crown and root dentin and two adhesive systems", J Prosthet Dent, 97, pp.223~228 (2007)
- Souza-Junior EJ, "The effect of curing light and chemical catalyst on the degree of conversion of two dual cured resin luting cements", Lasers Med Sci, 27, pp.145~151 (2012)
- Yenisey M, "Effect of surface treatments on the bond strength between resin cement and differently sintered zirconium-oxide ceramics", J Prosthodont Res, 60, pp.36~46 (2016)
- Usumez A, "Two-year color changes of light-cured composites: influence of different lightcuring units", Oper Dent, 30, pp.655~660 (2005)
- Rueggeberg FA, "Novel approach to measure composite conversion kinetics during exposure with stepped or continuous light-curing", J Esthet Dent, 11, pp.197~205 (1999)
- Arrais CA, "Effect of curing mode on the polymerization characteristics of dual-cured resin cement systems", J Dent, 36, pp.418~426 (2008)
- Moraes RR, "Impact of immediate and delayed light activation on self-polymerization of dual-cured dental resin luting agents", Acta Biomater, 5, pp.2095~2100 (2009)
- Van Landuyt KL, "Systematic review of the chemical composition of contemporary dental adhesives", Biomaterials, 28, pp.3757~3785 (2007)
- Asmussen E, "Influence of selected components on crosslink density in polymer structures", Eur J Oral Sci, 109, pp.282~285 (2001)
- Gonçalves LS, "Braga Effects of light on resin cement properties RR, Consani S. Improved polymerization efficiency of methacrylate-based cements containing an iodonium salt", Dent Mater, 29, pp.1251~1255 (2013)
- Andrade KM, "Effect of diphenyliodonium hexafluorphosphate on resin cements containing different concentrations of ethyl 4-(dimethylamino)benzoate and 2-(dimethylamino)ethyl methacrylate as co-initiators", Dent Mater, 32, pp.749~755 (2016)
- Hadis MA, "Dynamic monitoring of refractive index change through photoactive resins", Dent Mater, 26, pp.1106~1112 (2010)
- Price RB, "Effect of delivering light in specific narrow bandwidths from 394 to 515 nm on the microhardness of resin composites", Dent Mater, 25, pp.899~908 (2009)
- Mainardi Mdo C, "Effect of energy density and delay time on the degree of conversion and Knoop microhardness of a dual resin cement", J Investig Clin Dent, 6, pp.53~58 (2015)
- Reginato CF, "Polymerization efficiency through translucent and opaque fiber posts and bonding to root dentin", J Prosthodont Res, 57, pp.20~23 (2013)