Clinical gap changes after porcelain firing cycles of zirconia fixed dentures
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
PURPOSE. The aim of this study was to measure the changes on the marginal and internal adaptation of zirconia based anterior fixed partial dentures after the porcelain firing process. MATERIALS AND METHODS. A total of 34 anterior fixed partial dentures using LAVA CAD/CAM system (3M ESPE, Germany) were applied. Two silicone replicas were obtained: one is obtained before porcelain firing process (initial) and the other is obtained after porcelain firing process (final), followed by the examination under a binocular stereomicroscope. Kruskal Wallis and Wilcoxon Signed Ranks tests were used for the statistical analysis (P<.05). RESULTS. No statistically significant difference was found between initial and final marginal gap values (P>.05). At the internal gap measurements, final marginal area values (59.54 µm) were significantly lower than the initial marginal area values (68.68 µm)(P<.05). The highest and the lowest internal gap values were observed at the incisal/occlusal area and at the marginal area, respectively. In addition, lower internal gap values were obtained for canines than for central incisors, lateral incisors and premolars at the incisal area (P<.05). CONCLUSION. The firing cycles did not affect the marginal gap of Lava CAD/CAM system, but it is controversial for the internal gap.
Abstract
PURPOSE. The aim of this study was to measure the changes on the marginal and internal adaptation of zirconia based anterior fixed partial dentures after the porcelain firing process. MATERIALS AND METHODS. A total of 34 anterior fixed partial dentures using LAVA CAD/CAM system (3M ESPE, Germany) were applied. Two silicone replicas were obtained: one is obtained before porcelain firing process (initial) and the other is obtained after porcelain firing process (final), followed by the examination under a binocular stereomicroscope. Kruskal Wallis and Wilcoxon Signed Ranks tests were used for the statistical analysis (P<.05). RESULTS. No statistically significant difference was found between initial and final marginal gap values (P>.05). At the internal gap measurements, final marginal area values (59.54 µm) were significantly lower than the initial marginal area values (68.68 µm)(P<.05). The highest and the lowest internal gap values were observed at the incisal/occlusal area and at the marginal area, respectively. In addition, lower internal gap values were obtained for canines than for central incisors, lateral incisors and premolars at the incisal area (P<.05). CONCLUSION. The firing cycles did not affect the marginal gap of Lava CAD/CAM system, but it is controversial for the internal gap.
참고문헌 (31)
- Raigrodski AJ., "Contemporary materials and technologies for all-ceramic fixed partial dentures : a review of the literature", J Prosthet Dent, 92, pp.557~562 (2004)
- Aboushelib MN., "Microtensile bond strength of different components of core veneered all-ceramic restorations", Dent Mater, 21, pp.984~991 (2005)
- Yanagida H., "The chemistry of ceramics" (1996), Wiley
- Piwowarczyk A., "A clinical report and overview of scientific studies and clinical procedures conducted on the 3M ESPE Lava All-Ceramic System", J Prosthodont, 14, pp.39~45 (2005)
- Holmes JR., "Considerations in measurement of marginal fit", J Prosthet Dent, 62, pp.405~408 (1989)
- Sulaiman F., "A comparison of the marginal fit of In-Ceram, IPS Empress, and Procera crowns", Int J Prosthodont, 10, pp.478~484 (1997)
- Jacobs MS., "An investigation of dental luting cement solubility as a function of the marginal gap", J Prosthet Dent, 65, pp.436~442 (1991)
- Goldman M., "Microleakage-full crowns and the dental pulp", J Endod, 18, pp.473~475 (1992)
- Jørgensen KD., "Factors affecting the film thickness of zinc phosphate cements", Acta Odontol Scand, 18, pp.479~490 (1960)
- Tinschert J., "Marginal fit of alumina-and zirconia-based fixed partial dentures produced by a CAD", CAM system, 2001, pp.26, 367~374
- Boening KW., "Clinical fit of Procera AllCeram crowns", J Prosthet Dent, 84, pp.419~424 (2000)
- Reich S., "Clinical fit of all-ceramic three-unit fixed partial dentures, generated with three different CAD", CAM systems, 2005, pp.113, 174~179
- Reich S., "Clinical fit of fourunit zirconia posterior fixed dental prostheses", Eur J Oral Sci, 116, pp.579~584 (2008)
- Gonzalo E., "Marginal fit of Zirconia posterior fixed partial dentures", Int J Prosthodont, 21, pp.398~399 (2008)
- Vigolo P., "An in vitro evaluation of fit of zirconiumoxide-based ceramic four-unit fixed partial dentures, generated with three different CAD", CAM systems, before and after porcelain firing cycles and after glaze cycles, 2008, pp.17, 621~626
- Gonzalo E., "A comparison of the marginal vertical discrepancies of zirconium and metal ceramic posterior fixed dental prostheses before and after cementation", J Prosthet Dent, 102, pp.378~384 (2009)
- Beuer F., "Marginal and internal fits of fixed dental prostheses zirconia retainers", Dent Mater, 25, pp.94~102 (2009)
- Wettstein F., "Clinical study of the internal gaps of zirconia and metal frameworks for fixed partial dentures", Eur J Oral Sci, 116, pp.272~279 (2008)
- Denissen H., "Marginal fit and short-term clinical performance of porcelain-veneered CICERO, CEREC, and Procera onlays", J Prosthet Dent, 84, pp.506~513 (2000)
- Bindl A., "Marginal and internal fit of all-ceramic CAD", CAM crown-copings on chamfer preparations, 2005, pp.32, 441~447
- Reich S., "Measurement of cement thickness under lithium disilicate crowns using an impression material technique", Clin Oral Investig, 15, pp.521~526 (2011)
- Kokubo Y., "Clinical marginal and internal gaps of In-Ceram crowns fabricated using the GN-I system", J Oral Rehabil, 32, pp.753~758 (2005)
- Castellani D., "Thermal distortion of different materials in crown construction", J Prosthet Dent, 72, pp.360~366 (1994)
- Balkaya MC., "Influence of firing cycles on the margin distortion of 3 all-ceramic crown systems", J Prosthet Dent, 93, pp.346~355 (2005)
- Att W., "Marginal adaptation of three different zirconium dioxide three-unit fixed dental prostheses", J Prosthet Dent, 101, pp.239~247 (2009)
- Dittmer MP., "Stresses and distortions within zirconia-fixed dental prostheses due to the veneering process", Acta Biomater, 5, pp.3231~3239 (2009)
- Kohorst P., "Influence of the veneering process on the marginal fit of zirconia fixed dental prostheses", J Oral Rehabil, 37, pp.283~291 (2010)
- Aboushelib MN., "Prestresses in bilayered all-ceramic restorations", J Biomed Mater Res B Appl Biomater, 87, pp.139~145 (2008)
- Pospiech PR., "Clinical evaluation of zirconia-based all ceramic posterior bridges : two-year results", J Dent Res, 82, pp.114~ (2003)
- Raigrodski AJ., "The efficacy of posterior three-unit zirconium-oxide-based ceramic fixed partial dental prostheses : a prospective clinical pilot study", J Prosthet Dent, 96, pp.237~244 (2006)
- Crisp RJ., "A clinical evaluation of all-ceramic bridges placed in UK general dental practices : first-year results", Br Dent J, 205, pp.477~482 (2008)