The effect of zirconia framework design on the failure of all-ceramic crown under static loading
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
PURPOSE. This in vitro study aimed to compare the failure load and failure characteristics of two different zirconia framework designs of premolar crowns when subjected to static loading. MATERIALS AND METHODS. Two types of zirconia frameworks, conventional 0.5 mm even thickness framework design (EV) and 0.8 mm cutback of full contour crown anatomy design (CB), were made for 10 samples each. The veneer porcelain was added on under polycarbonate shell crown made by vacuum of full contour crown to obtain the same total thickness of the experiment crowns. The crowns were cemented onto the Cobalt-Chromium die. The dies were tilted 45 degrees from the vertical plane to obtain the shear force to the cusp when loading. All crowns were loaded at the lingual incline of the buccal cusp until fracture using a universal testing machine with cross-head speed 0.5 mm/min. The load to fracture values (N) was recorded and statistically analyzed by independent sample t-test. RESULTS. The mean and standard deviations of the failure load were 1,170.1 ± 90.9 N for EV design and 1,450.4 ± 175.7 N for CB design. A significant difference in the compressive failure load was found (P<.05). For the failure characteristic, the EV design was found only cohesive failures within veneering porcelain, while the CB design found more failures through the zirconia framework (8 from 10 samples). CONCLUSION. There was a significant difference in the failure load between two designs, and the design of the framework influences failure characteristic of zirconia crown.
Abstract
PURPOSE. This in vitro study aimed to compare the failure load and failure characteristics of two different zirconia framework designs of premolar crowns when subjected to static loading. MATERIALS AND METHODS. Two types of zirconia frameworks, conventional 0.5 mm even thickness framework design (EV) and 0.8 mm cutback of full contour crown anatomy design (CB), were made for 10 samples each. The veneer porcelain was added on under polycarbonate shell crown made by vacuum of full contour crown to obtain the same total thickness of the experiment crowns. The crowns were cemented onto the Cobalt-Chromium die. The dies were tilted 45 degrees from the vertical plane to obtain the shear force to the cusp when loading. All crowns were loaded at the lingual incline of the buccal cusp until fracture using a universal testing machine with cross-head speed 0.5 mm/min. The load to fracture values (N) was recorded and statistically analyzed by independent sample t-test. RESULTS. The mean and standard deviations of the failure load were 1,170.1 ± 90.9 N for EV design and 1,450.4 ± 175.7 N for CB design. A significant difference in the compressive failure load was found (P<.05). For the failure characteristic, the EV design was found only cohesive failures within veneering porcelain, while the CB design found more failures through the zirconia framework (8 from 10 samples). CONCLUSION. There was a significant difference in the failure load between two designs, and the design of the framework influences failure characteristic of zirconia crown.
참고문헌 (21)
- Raigrodski AJ, "The efficacy of posterior threeunit zirconium-oxide-based ceramic fixed partial dental prostheses:a prospective clinical pilot study", J Prosthet Dent, 96, pp.237~244 (2006)
- Rosentritt M, "Influence of substructure design and spacer settings on the in vitro performance of molar zirconia crowns", J Dent, 37, pp.978~983 (2009)
- Coelho PG, "Fatigue testing of two porcelain-zirconia allceramic crown systems", Dent Mater, 25, pp.1122~1127 (2009)
- Marchack BW, "Customization of milled zirconia copings for all-ceramic crowns: a clinical report", J Prosthet Dent, 99, pp.169~173 (2008)
- Shoher I, "Reinforced porcelain system: a new concept in ceramometal restorations", J Prosthet Dent, 50, pp.489~496 (1983)
- Marker JC, "The compressive strength of nonprecious versus precious ceramometal restorations with various frame designs", J Prosthet Dent, 55, pp.560~567 (1986)
- Sailer I, "Prospective clinical study of zirconia posterior fixed partial dentures: 3-year follow-up", Quintessence Int, 37, pp.685~693 (2006)
- Al-Amleh B1, "Clinical trials in zirconia: a systematic review", J Oral Rehabil, 37, pp.641~652 (2010)
- Tinschert J, "Clinical behavior of zirconia-based fixed partial dentures made of DC-Zirkon: 3-year results", Int J Prosthodont, 21, pp.217~222 (2008)
- Larsson C1, "Fracture strength of yttria-stabilized tetragonal zirconia polycrystals crowns with different design: an in vitro study", Clin Oral Implants Res, 23, pp.820~826 (2012)
- Swain MV, "Unstable cracking (chipping) of veneering porcelain on all-ceramic dental crowns and fixed partial dentures", Acta Biomater, 5, pp.1668~1677 (2009)
- Richerson D, "Modern ceramic engineering:properties, processing and use in design" (2006), Taylor and Francis Group
- Bonfante EA, "Effect of framework design on crown failure", Eur J Oral Sci, 117, pp.194~199 (2009)
- Khers SC, "Anatomy of cusps of posterior teeth and their fracture potential", J Prosthet Dent, 64, pp.139~147 (1990)
- Failure models and criteria for FRP under in-plane or threedimensional stress states including shear non-linearity, "Pinho ST", NASA, ~, pp.NASA, TM-2005-213530, L-19089
- Cavel WT, "An in vivo study of cuspal fracture", J Prosthet Dent, 53, pp.38~42 (1985)
- Farah JW, "Distribution of stresses in porcelainfused-to-metal and porcelain jacket crowns", J Dent Res, 54, pp.255~261 (1975)
- Craig RG, "Stress distribution in porcelain-fused-to-gold crowns and preparations constructed with photoelastic plastics", J Dent Res, 50, pp.1278~1283 (1971)
- Nally JN, "Experimental stress analysis of dental restorations. IX. Two-dimensional photoelastic stress analysis of porcelain bonded to gold crowns", J Prosthet Dent, 25, pp.307~316 (1971)
- Lawn BR, "Materials design in the performance of all-ceramic crowns", Biomaterials, 25, pp.2885~2892 (2004)
- Kleinfelder JW, "Maximal bite force in patients with reduced periodontal tissue support with and without splinting", J Periodontol, 73, pp.1184~1187 (2002)