Comparative analysis on intaglio surface trueness, wear volume loss of antagonist, and fracture resistance of full-contour monolithic zirconia crown for single-visit dentistry under simulated mastication
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
PURPOSE. This analysis aimed to evaluate the intaglio surface trueness, antagonist’s wear volume loss, and fracture resistance of full-contour crowns of (Y, Nb)-stabilized fully-sintered zirconia (FSZ), 4 mol% or 5 mol% yttria-stabilized partially sintered zirconia (4YZ or 5YZ) with high-speed sintering. MATERIALS AND METHODS. A total of 42 zirconia crowns were separated into three groups: FSZ, 4YZ, and 5YZ (n = 14). The intaglio surface trueness of the crowns was evaluated at the inner surface, occlusal, margin, and axial areas and reported as root-meansquare, positive and negative average deviation. Half of the specimens were aged for 120,000 cycles in the chewing simulator, and the wear volume loss of antagonist was measured. Before and after chewing, the fracture load was measured for each group. The trueness values were analyzed with Welch's ANOVA, and the wear volume loss with the Kruskal-Wallis tests. Effect of the zirconia type and aging on fracture resistance of crowns was tested using two-way ANOVA. RESULTS. The intaglio surface trueness measured at four different areas of the crown was less than 50 μm, regardless of the type of zirconia. No significant P in wear volume loss of antagonists were detected among the groups (P > .05). Both the type of zirconia and aging showed statistically significant effects on fracture resistance (P < .05). CONCLUSION. The full-contour crowns of FSZ as well as 4YZ or 5YZ with high-speed sintering were clinically acceptable, in terms of intaglio surface trueness, antagonist’s wear volume loss, and fracture resistance after simulated mastication.
Abstract
PURPOSE. This analysis aimed to evaluate the intaglio surface trueness, antagonist’s wear volume loss, and fracture resistance of full-contour crowns of (Y, Nb)-stabilized fully-sintered zirconia (FSZ), 4 mol% or 5 mol% yttria-stabilized partially sintered zirconia (4YZ or 5YZ) with high-speed sintering. MATERIALS AND METHODS. A total of 42 zirconia crowns were separated into three groups: FSZ, 4YZ, and 5YZ (n = 14). The intaglio surface trueness of the crowns was evaluated at the inner surface, occlusal, margin, and axial areas and reported as root-meansquare, positive and negative average deviation. Half of the specimens were aged for 120,000 cycles in the chewing simulator, and the wear volume loss of antagonist was measured. Before and after chewing, the fracture load was measured for each group. The trueness values were analyzed with Welch's ANOVA, and the wear volume loss with the Kruskal-Wallis tests. Effect of the zirconia type and aging on fracture resistance of crowns was tested using two-way ANOVA. RESULTS. The intaglio surface trueness measured at four different areas of the crown was less than 50 μm, regardless of the type of zirconia. No significant P in wear volume loss of antagonists were detected among the groups (P > .05). Both the type of zirconia and aging showed statistically significant effects on fracture resistance (P < .05). CONCLUSION. The full-contour crowns of FSZ as well as 4YZ or 5YZ with high-speed sintering were clinically acceptable, in terms of intaglio surface trueness, antagonist’s wear volume loss, and fracture resistance after simulated mastication.
참고문헌 (40)
- Zhang Y, "Novel zirconia materials in dentistry", J Dent Res, 97, pp.140~147 (2018)
- Schriwer C, "Monolithic zirconia dental crowns. Internal fit, margin quality, fracture mode and load at fracture", Dent Mater, 33, pp.1012~1020 (2017)
- Denry I, "State of the art of zirconia for dental applications", Dent Mater, 24, pp.299~307 (2008)
- Antón X, "Impact of high-speed sintering on accuracy and fit of 4 mol% yttria-stabilized tetragonal zirconia polycrystals(4Y-TZPs)", Int J Prosthodont, 34, pp.775~783 (2021)
- Jansen JU, "Impact of high-speed sintering on translucency, phase content, grain sizes, and flexural strength of 3Y-TZP and 4Y-TZP zirconia materials", J Prosthet Dent, 122, pp.396~403 (2019)
- Wiedenmann F, "Impact of high-speed sintering, layer thickness and artificial aging on the fracture load and two-body wear of zirconia crowns", Dent Mater, 36, pp.846~853 (2020)
- Stawarczyk B, "The effect of zirconia sintering temperature on flexural strength, grain size, and contrast ratio", Clin Oral Investig, 17, pp.269~274 (2013)
- Cho JH, "Trueness of the inner surface of monolithic crowns fabricated by milling of a fully sintered(Y, Nb)-TZP block in chairside CADCAM system for single-visit dentistry", Materials(Basel), 12, pp.3253~ (2019)
- Ahmed WM, "The influence of altering sintering protocols on the optical and mechanical properties of zirconia : A review", J Esthet Restor Dent, 31, pp.423~430 (2019)
- Tinschert J, "Status of current CAD", CAM technology in dental medicine, 2004, pp.7, 25~45
- Jeong KW, "Clinical feasibility of fully sintered (Y, Nb)-TZP for CADCAM single-unit restoration: a pilot study", Materials(Basel), 14, pp.2762~ (2021)
- Kim DJ, "Mechanical properties, phase stability, and biocompatibility of (Y,Nb)-TZP", Al(2)O(3) composite abutments for dental implant, 2000, pp.53, 438~443
- Kirsch C, "Trueness of four different milling procedures used in dental CAD", CAM systems, 2017, pp.21, 551~558
- Bindl A, "Fit of all-ceramic posterior fixed partial denture frameworks in vitro", Int J Periodontics Restorative Dent, 27, pp.567~575 (2007)
- Rekow D, "Near-surface damage-a persistent problem in crowns obtained by computer-aided design and manufacturing", Proc Inst Mech Eng H, 219, pp.233~243 (2005)
- Sailer I, "Five-year clinical results of zirconia frameworks for posterior fixed partial dentures", Int J Prosthodont, 20, pp.383~388 (2007)
- Lang NP, "Clinical and microbiological effects of subgingival restorations with overhanging or clinically perfect margins", J Clin Periodontol, 10, pp.563~578 (1983)
- Felton DA, "Effect of in vivo crown margin discrepancies on periodontal health", J Prosthet Dent, 65, pp.357~364 (1991)
- Goldman M, "Microleakage--full crowns and the dental pulp", J Endod, 18, pp.473~475 (1992)
- Mehl A, "Accuracy, trueness, and precision - a guideline for the evaluation of these basic values in digital dentistry", Int J Comput Dent, 24, pp.341~352 (2021)
- Scherrer SS, "The fracture resistance of all-ceramic crowns on supporting structures with different elastic moduli", Int J Prosthodont, 6, pp.462~467 (1993)
- Scherrer SS, "The effect of crown length on the fracture resistance of posterior porcelain and glass-ceramic crowns", Int J Prosthodont, 5, pp.550~557 (1992)
- Nakamura K, "Fracture resistance of monolithic zirconia molar crowns with reduced thickness", Acta Odontol Scand, 73, pp.602~608 (2015)
- White SN, "Flexural strength of a layered zirconia and porcelain dental all-ceramic system", J Prosthet Dent, 94, pp.125~131 (2005)
- Stawarczyk B, "Three generations of zirconia:From veneered to monolithic", Quintessence Int, 48, pp.369~380 (2017)
- Miyazaki T, "Current status of zirconia restoration", J Prosthodont Res, 57, pp.236~261 (2013)
- Wiskott HW, "Stress fatigue : basic principles and prosthodontic implications", Int J Prosthodont, 8, pp.105~116 (1995)
- Liu SY, "Fatigue of yttria-stabilized zirconia: I, fatigue damage, fracture origins, and lifetime prediction", J Am Ceram Soc, 74, pp.1197~1205 (1991)
- Chevalier J, "Low-temperature degradation of zirconia and implications for biomedical implants", Annu Rev Mater Res, 37, pp.1~32 (2007)
- Lümkemann N, "Impact of hydrothermal aging on the light transmittance and flexural strength of colored yttria-stabilized zirconia materials of different formulations", J Prosthet Dent, 125, pp.518~526 (2021)
- Camposilvan E, "Aging resistance, mechanical properties and translucency of different yttria-stabilized zirconia ceramics for monolithic dental crown applications", Dent Mater, 34, pp.879~890 (2018)
- Zhang F, "Strength, toughness and aging stability of highly-translucent Y-TZP ceramics for dental restorations", Dent Mater, 32, pp.e327~e337 (2016)
- Nakamura T, "In vitro investigation of fracture load and aging resistance of high-speed sintered monolithic tooth-borne zirconia crowns", J Prosthodont Res, 64, pp.182~187 (2020)
- Hao Z, "Influence of low-temperature degradation on the wear characteristics of zirconia against polymer-infiltrated ceramic-network material", J Prosthet Dent, 120, pp.596~602 (2018)
- DeLong R, "An artificial oral environment for testing dental materials", IEEE Trans Biomed Eng, 38, pp.339~345 (1991)
- Steiner M, "In vitro evaluation of a mechanical testing chewing simulator", Dent Mater, 25, pp.494~499 (2009)
- Alghazzawi TF, "Advancements in CAD", CAM technology : Options for practical implementation, 2016, pp.60, 72~84
- Kim CM, "Trueness of milled prostheses according to number of ball-end mill burs", J Prosthet Dent, 115, pp.624~629 (2016)
- Edwards Rezende CE, "Dimensional changes from the sintering process and fit of Y-TZP copings : Micro-CT analysis", Dent Mater, 33, pp.e405~e413 (2017)
- Pereira GKR, "Mechanical reliability, fatigue strength and survival analysis of new polycrystalline translucent zirconia ceramics for monolithic restorations", J Mech Behav Biomed Mater, 85, pp.57~65 (2018)