Processing of porous hydroxyapatite scaffolds containing calcium phosphate glass-ceramics for bone tissue engineering
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Highly porous hydroxyapatite (HA) scaffolds containing calcium phosphate glass-ceramics with large pore size and improved compressive strength have been prepared using a combined processing route of polymer sponge and freeze/gel-casting. Tertiary-butyl alcohol (TBA) was used as a solvent. The sintered scaffolds were characterized in terms of microstructure, physical and mechanical properties. A reticulated structure with large pore size of 220-300 µm was formed on burn-out of polyurethane foam where the struts consisted of a few intergranular small-sized pores (< 2 µm) formed by freeze/gel-casting. The addition of glass-ceramics seemed to lead a matrix phase to partial liquid phase sintering and thus the strut structure became more dense with the small size reduction of coarsened pores consisting of reticulated structure. As a consequence, the compressive strength was improved. Also, with the addition of 10 wt.% glass-ceramics the in vitro bioactivity of the scaffolds was further enhanced.
Abstract
Highly porous hydroxyapatite (HA) scaffolds containing calcium phosphate glass-ceramics with large pore size and improved compressive strength have been prepared using a combined processing route of polymer sponge and freeze/gel-casting. Tertiary-butyl alcohol (TBA) was used as a solvent. The sintered scaffolds were characterized in terms of microstructure, physical and mechanical properties. A reticulated structure with large pore size of 220-300 µm was formed on burn-out of polyurethane foam where the struts consisted of a few intergranular small-sized pores (< 2 µm) formed by freeze/gel-casting. The addition of glass-ceramics seemed to lead a matrix phase to partial liquid phase sintering and thus the strut structure became more dense with the small size reduction of coarsened pores consisting of reticulated structure. As a consequence, the compressive strength was improved. Also, with the addition of 10 wt.% glass-ceramics the in vitro bioactivity of the scaffolds was further enhanced.
참고문헌 (26)
- S. Padilla, , J. Biomed. Mater. Res, 75A, pp.63~72 (2005)
- L. Cerroni, , Biomol. Eng, 19, pp.119~124 (2002)
- L.L. Hench, , Science, 226, pp.630~636 (1984)
- K.J.L. Burg, , Biomaterials, 21, pp.2347~2359 (2000)
- S.F. Hulbert, "High Tech Ceramics", pp.189~213 (1987), Elsevier
- A.R. Studart, , J. Am. Ceram. Soc, 89, pp.1771~1789 (2006)
- I.K. Jun, , J. Am. Ceram. Soc, 90, pp.2703~2708 (2007)
- H.W. Kim, , J. Mater. Sci. Mater. Med, 16, pp.189~195 (2005)
- Y. Zhang, , J. Biomed. Mater. Res, 61, pp.1~8 (2002)
- T.M.G. Chu, , J. Mater. Sci, 12, pp.471~478 (2001)
- Sepulveda, , J. Biomed. Mater. Res, 50, pp.27~34 (2000)
- S. Deville, , Materials, 3, pp.1913~1927 (2010)
- U.G.K. Wegst, , Phil. Trans. R. Soc. A, 368, pp.2099~2121 (2010)
- B.H. Yoon, , J. Am. Ceram. Soc, 90, pp.1744~1752 (2007)
- Y.M. Soon, , Mater. Lett, 63, pp.1548~1550 (2009)
- A. Macchetta, , Acta. Biometer, 25, pp.1319~1327 (2009)
- H.R. Ramay, , Biomaterials, 24, pp.3293~3302 (2003)
- N. Monmaturapoj, , J. Porous Mater, 19, pp.441~447 (2012)
- J.H. Kim, , Ceram. Inter, 37, pp.2317~2322 (2011)
- 송창원, "실리카를 함유하지 않는 생체활성 칼슘인산염 글라스-세라믹스의 합성 및 특성", 한국세라믹학회지, 48(3), pp.217~221 (2011), 한국세라믹학회
- V.S. Komlev, , J. Mater. Sci. Mater. Med, 13, pp.295~299 (2002)
- T.Y. Yang, , J. Mater. Sci. Mater. Med, 21, pp.1495~1502 (2010)
- F.H. Lin, , Biomaterials, 22, pp.2981~2992 (2001)
- C. Liu, , Biomaterials, 22, pp.301~306 (2001)
- M. Tanahashi, , J. Mater. Sci. Mater. Med, 3, pp.48~53 (1992)
- H. Monma, , J. Ceram. Soc. Japan, 84, pp.209~213 (1976)