Electrical properties of Sb-doped apatite-type lanthanum silicate materials for SOFCsmullite
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
La9.33-xSbx(SiO4)6O2 (0 ≤ x ≤ 2.0) ceramics were fabricated using the standard solid-state synthesis method for solid oxide electrolytes. Increasing the Sb content in apatite-type La9.33-xSbx(SiO4)6O2 leads to an increased unit cell volume. The roomtemperature structure is hexagonal, space group P63 or P63/m, with a = 9.728 Å, and c = 7.191 Å for La8.33Sb(SiO4)6O2. The average grain size in sintered specimens was approximately 1.5 to 1.9 μm. La9.33-xSbx(SiO4)6O2 (1.5 ≤ x ≤ 2.0) apatite ceramics showed the formation of a second phase of La2Si2O7, due to the volatilization of the Sb atoms. The electrical conductivity at 800 o C and activation energy of La8.33Sb(SiO4)6O2 doped with 1.0 mol% Sb showed a maximum value of 3.3 × 10-3 S cm-1 and 1.47 eV, respectively.
Abstract
La9.33-xSbx(SiO4)6O2 (0 ≤ x ≤ 2.0) ceramics were fabricated using the standard solid-state synthesis method for solid oxide electrolytes. Increasing the Sb content in apatite-type La9.33-xSbx(SiO4)6O2 leads to an increased unit cell volume. The roomtemperature structure is hexagonal, space group P63 or P63/m, with a = 9.728 Å, and c = 7.191 Å for La8.33Sb(SiO4)6O2. The average grain size in sintered specimens was approximately 1.5 to 1.9 μm. La9.33-xSbx(SiO4)6O2 (1.5 ≤ x ≤ 2.0) apatite ceramics showed the formation of a second phase of La2Si2O7, due to the volatilization of the Sb atoms. The electrical conductivity at 800 o C and activation energy of La8.33Sb(SiO4)6O2 doped with 1.0 mol% Sb showed a maximum value of 3.3 × 10-3 S cm-1 and 1.47 eV, respectively.
참고문헌 (17)
- H. Arikawa, , Solid State Ionics, 31, pp.136~ (2000)
- M. Higuchi, , Cryst. Growth, 207, pp.298~ (1999)
- Hyun-Soo Kang, "A Feasibility Design of PEMFC Parallel Operation for a Fuel Cell Generation System", Journal of Electrical Engineering & Technology, 3(3), pp.408~421 (2008), 대한전기학회
- Amin Hajizadeh, "Power Flow Control of Grid-Connected Fuel Cell Distributed Generation Systems", Journal of Electrical Engineering & Technology, 3(2), pp.143~151 (2008), 대한전기학회
- S. Nakayama, , J. Eur. Cream. Soc, 18, pp.1413~ (1998)
- 곽동주, "Comparison of transparent conductive indium tin oxide, titanium-doped indium oxide, and fluorine-doped tin oxide films for dye-sensitized solar cell application", Journal of Electrical Engineering & Technology, 6(5), pp.684~687 (2011), 대한전기학회
- J. R. Tolcahrd, , J. Mater. Chem, 13, pp.1956~ (2003)
- Jong-Kyou Jeong, "Grid-tied Power Conditioning System for Fuel Cell Composed of Three-phase Current-fed DC-DC Converter and PWM Inverter", Journal of Electrical Engineering & Technology, 6(2), pp.255~262 (2011), 대한전기학회
- J. Mcfarlane, , Ionics, 8, pp.149~ (2002)
- A. L. Shaula, , J. Eur. Ceram. Soc, 25, pp.2583~ (2005)
- 니겔사메즈, "Concept, Manufacture and Results of the Microtubular Solid Oxide Fuel Cell", Transactions on Electrical and Electronic Materials, 12(1), pp.1~6 (2011), 한국전기전자재료학회
- J. E. H. Sansom, , Solid State Ionics, 139, pp.205~ (2001)
- P. R. Slater, , Solid State Phenom, 90-91, pp.195~ (2003)
- M. Glerup, , J. Solid State Chem, 160, pp.25~ (2001)
- R. D. Shannon, , Acta Crystallogr, A32, pp.751~ (1976)
- A. A. Yaremchenko, , Solid State Ionics, 171, pp.51~ (2004)
- L. L. Reina, , J. Solid State Chem, 180, pp.1250~ (2007)