Evaluation of Surface Hardness and Wear Resistance of a Glass-Hybrid Restorative Material with Nano-filled Resin Coating
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
This study aimed to evaluate the surface hardness and wear resistance of a novel glass-hybrid restorative material in comparison with those of high-viscosity glass ionomer cement (GIC). Additionally, this study examined how the application of a nano-filled resin coating affected these mechanical properties. This study utilized 80 disk-shaped samples prepared from two distinct GI materials: Equia Forte HT Fil and Fuji IX GP. Half of the specimens from each material group were treated with an Equia Forte Coat. Vickers hardness tests were conducted on a set of 40 specimens, and wear resistance was measured on a separate set of 40 specimens. Equia Forte HT Fil showed significantly higher hardness than Fuji IX GP (p < 0.05). The nano-filled resin coating did not significantly affect the hardness in both groups (p > 0.05). In wear depth measurements, uncoated Equia Forte HT Fil showed significantly lower wear depth compared to uncoated Fuji IX GP (p < 0.05). After coating application, both GI groups showed significantly decreased wear depth (p < 0.05). In terms of both hardness and wear resistance, the properties of the glass-hybrid restorative material were superior to those of the high-viscosity GIC. Nano-filled resin coating exhibited no significant positive effect on the hardness of either GI cement material but significantly increased their wear resistance.
Abstract
This study aimed to evaluate the surface hardness and wear resistance of a novel glass-hybrid restorative material in comparison with those of high-viscosity glass ionomer cement (GIC). Additionally, this study examined how the application of a nano-filled resin coating affected these mechanical properties. This study utilized 80 disk-shaped samples prepared from two distinct GI materials: Equia Forte HT Fil and Fuji IX GP. Half of the specimens from each material group were treated with an Equia Forte Coat. Vickers hardness tests were conducted on a set of 40 specimens, and wear resistance was measured on a separate set of 40 specimens. Equia Forte HT Fil showed significantly higher hardness than Fuji IX GP (p < 0.05). The nano-filled resin coating did not significantly affect the hardness in both groups (p > 0.05). In wear depth measurements, uncoated Equia Forte HT Fil showed significantly lower wear depth compared to uncoated Fuji IX GP (p < 0.05). After coating application, both GI groups showed significantly decreased wear depth (p < 0.05). In terms of both hardness and wear resistance, the properties of the glass-hybrid restorative material were superior to those of the high-viscosity GIC. Nano-filled resin coating exhibited no significant positive effect on the hardness of either GI cement material but significantly increased their wear resistance.