글루타티온이 캡핑된 ZnSe 나노 입자 발광 특성에 미치는 합성 조건의 영향
Effects of Synthesis Conditions on Luminescence Characteristics of Glutathione Capped ZnSe Nano particles
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Zinc selenide (ZnSe) nanoparticles were synthesized in aqueous solution using glutathione (GSH) as a ligand. The influence of the ligand content, reaction temperature, and hydroxyl ion concentration (pH) on the fabrication of the ZnSe particles was investigated. The optical properties of the synthesized ZnSe particles were characterized using various analytical techniques. The nanoparticles absorbed UV-vis light in the range of 350-400 nm, which is shorter than the absorption wavelength of bulk ZnSe particles (460 nm). The lowest ligand concentration for achieving good light absorption and emission properties was 0.6 mmol. The reaction temperature had an impact on the emission properties; photoluminescence spectroscopic analysis showed that the photo-discharge characteristics were greatly enhanced at high temperatures. These discharge characteristics were also affected by the hydroxyl ion concentration in solution; at pH 13, sound emission characteristics were observed, even at a low temperature of 25oC. The manufactured nanoparticles showed excellent light absorption and emission properties, suggesting the possibility of fabricating ZnSe QDs in aqueous solutions at low temperatures.
Abstract
Zinc selenide (ZnSe) nanoparticles were synthesized in aqueous solution using glutathione (GSH) as a ligand. The influence of the ligand content, reaction temperature, and hydroxyl ion concentration (pH) on the fabrication of the ZnSe particles was investigated. The optical properties of the synthesized ZnSe particles were characterized using various analytical techniques. The nanoparticles absorbed UV-vis light in the range of 350-400 nm, which is shorter than the absorption wavelength of bulk ZnSe particles (460 nm). The lowest ligand concentration for achieving good light absorption and emission properties was 0.6 mmol. The reaction temperature had an impact on the emission properties; photoluminescence spectroscopic analysis showed that the photo-discharge characteristics were greatly enhanced at high temperatures. These discharge characteristics were also affected by the hydroxyl ion concentration in solution; at pH 13, sound emission characteristics were observed, even at a low temperature of 25oC. The manufactured nanoparticles showed excellent light absorption and emission properties, suggesting the possibility of fabricating ZnSe QDs in aqueous solutions at low temperatures.
참고문헌 (25)
- A. P. Alivisatos, , Science, 271, pp.933~ (1996)
- D. J. Norris, , Science, 319, pp.1776~ (2008)
- A. Valizadeh, , Nanoscale Res. Lett, 7, pp.480~ (2012)
- C. J. Barrelet, , J. Am. Chem. Soc, 125, pp.11498~ (2003)
- K. S. Leschkies, , Nano Letters, 7, pp.1793~ (2007)
- D. J. Norris, , Phys. Rev. B, 53, pp.16338~ (1996)
- L. W. Wang, , Phys. Rev. B, 53, pp.9579~ (1996)
- C. Wang, , J. Lumin, 225, pp.117354~ (2020)
- L. Langof, , Chem. Phys, 297, pp.93~ (2004)
- F. Ángel-Huerta, , J. Lumin, 197, pp.277~ (2018)
- P. Reiss, , New J. Chem, 31, pp.1843~ (2007)
- K. Saikia, "Facile synthesis of highly luminescent ZnSe(S) alloyed quantum dot for biomedical imaging", Current Applied Physics, 13(5), pp.925~930 (2013), 한국물리학회
- G. Y. Lan, , J. Mater. Chem, 17, pp.2661~ (2007)
- Z. Deng, , Langmuir, 25, pp.434~ (2009)
- A. Shavel, , J. Phys. Chem. B, 108, pp.5905~ (2004)
- L. C. He, , Mater. Technol, 33, pp.205~ (2017)
- 김미소, "수열합성법에 의한 Zinc Selenide 나노 분말 합성 및 미세구조 특성 연구", 한국재료학회지, 27(9), pp.459~465 (2017), 한국재료학회
- H. Hong, , J. Crystal Growth, 535, pp.125523~ (2020)
- C. Lee, , Vac. Magazine, 6, pp.29~ (2017)
- F. O. Silva, , Nanoscale Res. Lett, 7, pp.1~ (2012)
- F. Jiang, , Langmuir, 28, pp.12931~ (2012)
- S. Ramanathan, , Nanotechnology, 19, pp.195601~ (2008)
- P. Wu, , Colloids and Surfaces A: Physicochem. Eng. Aspects, 375, pp.109~ (2011)
- F. Jiang, , Langmuir, 28, pp.12931~ (2012)
- L. Sun, , Mater. Express, 5, pp.219~ (2015)