One-pot 공정을 이용한 InP/ZnS core/shell 나노결정 합성및 특성 연구
Synthesis and Properties of InP/ZnS core/shell Nanoparticles with One-pot process
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, simple chemical synthesis of green emitting Cd-free InP/ZnS QDs is accomplished by reacting In, P, Zn, and S precursors by one-pot process. The particle size and the optical properties were tailored, by controlling various experimental conditions, including [In]/[MA] (MA: myristic acid) mole ratio, reaction temperature and reaction time. The results of ultraviolet–visible spectroscopy (UV-vis), and of photoluminescence (PL), reveal that the exciton emission of InP was improved by surface coating, with a layer of ZnS. We report the correlation between each experimental condition and the luminescent properties of InP/ZnS core/shell QDs. Transmission electron microscopy (TEM), and X-ray powder diffraction (XRD) techniques were used to characterize the as-synthesized QDs. In contrast to core nanoparticles, InP/ZnS core/shell treated with surface coating shows a clear ultraviolet peak. Besides this work, we need to study what clearly determines the shell kinetic growth mechanism of InP/ZnS core shell QDs.
Abstract
In this study, simple chemical synthesis of green emitting Cd-free InP/ZnS QDs is accomplished by reacting In, P, Zn, and S precursors by one-pot process. The particle size and the optical properties were tailored, by controlling various experimental conditions, including [In]/[MA] (MA: myristic acid) mole ratio, reaction temperature and reaction time. The results of ultraviolet–visible spectroscopy (UV-vis), and of photoluminescence (PL), reveal that the exciton emission of InP was improved by surface coating, with a layer of ZnS. We report the correlation between each experimental condition and the luminescent properties of InP/ZnS core/shell QDs. Transmission electron microscopy (TEM), and X-ray powder diffraction (XRD) techniques were used to characterize the as-synthesized QDs. In contrast to core nanoparticles, InP/ZnS core/shell treated with surface coating shows a clear ultraviolet peak. Besides this work, we need to study what clearly determines the shell kinetic growth mechanism of InP/ZnS core shell QDs.
참고문헌 (33)
- A. P. Alivisatos, , J. Phys. Chem, 100, pp.13226~ (1996)
- D. Pugh-Thomas, , Nanotechnology, 22, pp.185503~ (2011)
- V. L. Colvin, , Nature, 370, pp.354~ (1994)
- A. P. Alivisatos, , Science, 271, pp.933~ (1996)
- A. D. Yoffe, , Adv .Phys., 42, pp.173~ (1993)
- A. D. Yoffe, , Adv. Phys., 50, pp.1~ (2001)
- D. Bera, , Materials., 3, pp.2260~ (2010)
- C. B. Murray, , J. Am. Chem. Soc., 115, pp.8706~ (1993)
- M. Green, , SPIE Photonics Europe., 6, pp.355~ (2002)
- T. Greco, , SPIE Photonics Europe., pp.842439~ (2012)
- D. Battaglia, , Nano Lett., 2, pp.1027~ (2002)
- M. Brumer, , Adv. Funct. Mater., 15, pp.1111~ (2005)
- M. Anc, , ECS J. Solid State Sci. Technol., 2, pp.R3071~ (2013)
- H. Li, , J. Phys. Chem. C, 118, pp.46~ (2013)
- W. K. Bae, , Chem. Mater., 20, pp.531~ (2008)
- M. A. Hines, , J. Phys. Chem., 100, pp.468~ (1996)
- J. Lim, , Chem. Mater., 23, pp.4459~ (2011)
- B. Zhang, , Phys. Chem. Chem. Phys, 17, pp.25133~ (2015)
- D. Mijatovic, , Lab on a Chip, 5, pp.492~ (2005)
- C. de Mello Donegá, , Small, 1, pp.1152~ (2005)
- S. G. Kwon, , J. Am. Chem. Soc., 129, pp.12571~ (2007)
- J. Park, , Angewandte Chemie International Edition, 46, pp.4630~ (2007)
- S. Xu, , J. Am. Chem. Soc., 128, pp.1054~ (2006)
- L. Li, , J. Am. Chem. Soc., 130, pp.11588~ (2008)
- A. Narayanaswamy, , J. Phys. Chem. C, 112, pp.6775~ (2008)
- 이은진, "고 안정성 전구체를 사용한 InP", ZnS 반도체 나노입자합성 및 발광 특성 향상, 2015, pp.22(6), 385~390[DOI]
- K. Lim, , Nanotechnology, 23, pp.485609~ (2012)
- S. Haubold, , ChemPhysChem, 2, pp.331~ (2001)
- H. Huang, , Analyst, 139, pp.6536~ (2014)
- C. A. Leatherdale, , J. Phys. Chem. B, 106, pp.7619~ (2002)
- A. Mandal, , Analyst, 137, pp.765~ (2012)
- D. Mourad, , J. Appl. Phys., 121, pp.014307~ (2017)
- S. C. Pandey, , J. Appl. Phys., 111, pp.113526~ (2012)