InP 코어 합성온도에 따른 InP/ZnS의 코어/쉘 양자점의 발광특성
Luminescence Properties of InP/ZnS Quantum Dots depending on InP Core synthesis Temperature
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In this study, we investigate the optical properties of InP/ZnS core/shell quantum dots (QDs) by controlling the synthesis temperature of InP. The size of InP determined by the empirical formula tends to increase with temperature: the size of InP synthesized at 140oC and 220oC is 2.46 nm and 4.52 nm, respectively. However, the photoluminescence (PL) spectrum of InP is not observed because of the formation of defects on the InP surface. The growth of InP is observed during the deposition of the shell (ZnS) on the synthesized InP, which is ended up with green-red PL spectrum. We can adjust the PL spectrum and absorption spectrum of InP/ZnS by simply adjusting the core temperature. Thus, we conclude that there exists an optimum shell thickness for the QDs according to the size.
Abstract
In this study, we investigate the optical properties of InP/ZnS core/shell quantum dots (QDs) by controlling the synthesis temperature of InP. The size of InP determined by the empirical formula tends to increase with temperature: the size of InP synthesized at 140oC and 220oC is 2.46 nm and 4.52 nm, respectively. However, the photoluminescence (PL) spectrum of InP is not observed because of the formation of defects on the InP surface. The growth of InP is observed during the deposition of the shell (ZnS) on the synthesized InP, which is ended up with green-red PL spectrum. We can adjust the PL spectrum and absorption spectrum of InP/ZnS by simply adjusting the core temperature. Thus, we conclude that there exists an optimum shell thickness for the QDs according to the size.
참고문헌 (16)
- C. B. Murray, , J. Am. Chem. Soc., 115, pp.8706~ (1993)
- V. L. Colvin, , Nature, 370, pp.354~ (1994)
- H. S. Hong, , J. Korean Powder Metall. Inst., 19, pp.6~ (2012)
- O. I. Micic, , J. Phys. Chem., 98, pp.4966~ (1994)
- J. Lovrić, , Chem. & Bio., 12, pp.1227~ (2005)
- S. Tamang, , Chem. Mater., 28, pp.2491~ (2016)
- O. I. Mićić, , J. Phys. Chem. B, 101, pp.4904~ (1997)
- S. Haubold, , Chem. Phys. Chem., 2, pp.331~ (2001)
- J. D. Dow, , J. Vac. Sci. & Tech., 20, pp.659~ (1982)
- S. Adam, , J. Chem. Phys., 123, pp.084706~ (2005)
- W. S. Song, , J. Nanoparticle. Res., 15, pp.1750~ (2013)
- P. Reiss, , Small Mol., 5, pp.154~ (2009)
- 서한욱, "반응 용기법을 이용한 InP", ZnS 양자점 합성과정에서 InP 코어의 성장기구, 2017, pp.24(1), 6~10[DOI]
- J. R. Dethlefsen, , Nano lett., 11, pp.1964~ (2011)
- X. Yang, , Adv. Mater., 24, pp.4180~ (2012)
- Kyungnam Kim, "Halide-Amine Co-Passivated Indium Phosphide Colloidal Quantum Dots in Tetrahedral Shape", Angewandte Chemie International Edition, 55(11), pp.3714~3718 (2016), Wiley-Blackwell[DOI]