Se 전구체 함량 따른 CdSe 양자점 형광체의 발광특성
Luminescent Characteristics of CdSe Quantum Dot Phosphor Depending on Se Precursor Ratio
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
The quantum dots (QD) have unique electrical and optical properties due to quantum dot confinement effect. The optical properties of QDs are decided by various synthesis conditions. In a prior QDs study, a study on the QDs size with synthesis condition such as synthesis time and temperature is being extensively researched. However, the research on QDs size with composition ratio has hitherto received scant attention. In order to evaluate the ratio dependence of CdSe crystal, synthesis ratio of Se precursor is changed from 16.7 mol%Se to 44 mol%Se. As the increasing Se ratio, the band gap was increased. This is caused by red shift of emission. We confirmed optical property of CdSe QDs with composition ratio.
Abstract
The quantum dots (QD) have unique electrical and optical properties due to quantum dot confinement effect. The optical properties of QDs are decided by various synthesis conditions. In a prior QDs study, a study on the QDs size with synthesis condition such as synthesis time and temperature is being extensively researched. However, the research on QDs size with composition ratio has hitherto received scant attention. In order to evaluate the ratio dependence of CdSe crystal, synthesis ratio of Se precursor is changed from 16.7 mol%Se to 44 mol%Se. As the increasing Se ratio, the band gap was increased. This is caused by red shift of emission. We confirmed optical property of CdSe QDs with composition ratio.
참고문헌 (11)
- 심성주, "전기화학증착법으로 양극산화 알루미늄(AAO) 템플레이트를 이용한 Ni 나노와이어의 제조 및 성장에 관한 연구", 한국분말야금학회지, 18(1), pp.49~55 (2011), 한국분말야금학회
- S. Coe, , Nature, 420, pp.800~ (2002)
- B. Dubertert, , Science, 298, pp.1759~ (2002)
- W. U. Huynh, , Adv. Mater., 11, pp.923~ (1999)
- 정원근, "CdSe 나노입자 형광층 구조에 따른 백색 LED 발광 특성 연구", Korean Chemical Engineering Research(HWAHAK KONGHAK), 49(3), pp.320~324 (2011), 한국화학공학회
- M. Kumar, , Thin solid films, 312, pp.139~ (1998)
- 엄누시아, "Injection 온도 및 합성시간에 따른 CdSe 양자점 합성 및 특성", 한국재료학회지, 22(3), pp.140~144 (2012), 한국재료학회
- Z. A. Peng, , J. Am. Chem. Soc., 123, pp.183~ (2001)
- L. Qu, , Nano Lett, 1, pp.333~ (2001)
- Y. A. Yang, , Angew. Chem. Int. Ed, 44, pp.6712~ (2005)
- C. Zhai, , Nanoscale Res Lett, 6, pp.31~ (2011)