ZnSe 나노분말 합성에 미치는 환원제와 첨가제의 영향
Influence of Reducing Agents and Additives on the Synthesis of ZnSe Nanoparticles
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Nano-sized ZnSe particles are successfully synthesized in an aqueous solution at room temperature using sodium borohydride (NaBH4) and thioglycolic acid (TGA) as the reducing agent and stabilizer, respectively. The effects of the mass ratio of the reducing agent to Se, stabilizer concentration, and stirring time on the synthesis of the ZnSe nanoparticles are evaluated. The light absorption/emission properties of the synthesized nanoparticles are characterized using ultraviolet-visible (UV-vis) spectroscopy, photoluminescence (PL) spectroscopy, and particle size analyzer (PSA) techniques. At least one mass ratio (NaBH4/Se) of the reducing agent should be added to produce ZnSe nanoparticles finer than 10 nm and to absorb UV–vis light shorter than the ZnSe bulk absorption wavelength of 460 nm. As the ratio of the reducing agent increases, the absorption wavelengths in the UV-vis curves are blue-shifted. Stirring in the atmosphere acts as a deterrent to the reduction reaction and formation of nanoparticles, but if not stirred in the atmosphere, the result is on par with synthesis in a nitrogen atmosphere. The stabilizer, TGA, has an impact on the Zn precursor synthesis. The fabricated nanoparticles exhibit excellent photo-absorption/discharge characteristics, suggesting that ZnSe nanoparticles can be alloyed without the need for organic solutions or high-temperature environments.
Abstract
Nano-sized ZnSe particles are successfully synthesized in an aqueous solution at room temperature using sodium borohydride (NaBH4) and thioglycolic acid (TGA) as the reducing agent and stabilizer, respectively. The effects of the mass ratio of the reducing agent to Se, stabilizer concentration, and stirring time on the synthesis of the ZnSe nanoparticles are evaluated. The light absorption/emission properties of the synthesized nanoparticles are characterized using ultraviolet-visible (UV-vis) spectroscopy, photoluminescence (PL) spectroscopy, and particle size analyzer (PSA) techniques. At least one mass ratio (NaBH4/Se) of the reducing agent should be added to produce ZnSe nanoparticles finer than 10 nm and to absorb UV–vis light shorter than the ZnSe bulk absorption wavelength of 460 nm. As the ratio of the reducing agent increases, the absorption wavelengths in the UV-vis curves are blue-shifted. Stirring in the atmosphere acts as a deterrent to the reduction reaction and formation of nanoparticles, but if not stirred in the atmosphere, the result is on par with synthesis in a nitrogen atmosphere. The stabilizer, TGA, has an impact on the Zn precursor synthesis. The fabricated nanoparticles exhibit excellent photo-absorption/discharge characteristics, suggesting that ZnSe nanoparticles can be alloyed without the need for organic solutions or high-temperature environments.
참고문헌 (29)
- 손민지, "온도에 따른 InZnP", ZnSe, 다중껍질) 양자점의 형광 특성 변화, pp.전기전자재료학회논문지, 2018[DOI]
- D. J. Norris, , Science, 319, pp.1776~ (2008)
- H. Hu, , Opt. Mater, 28, pp.536~ (2006)
- K. Senthilkumar, , J. Mater. Sci. Mater. Electron, 23, pp.2048~ (2012)
- Y. G. Kim, , Ceramist, 16, pp.42~ (2013)
- 김미소, "수열합성법에 의한 Zinc Selenide 나노 분말 합성 및 미세구조 특성 연구", 한국재료학회지, 27(9), pp.459~465 (2017), 한국재료학회
- H. S. Hong, , J. Crystal Growth, 535, pp.125523~ (2020)
- J. Zhu, , Chem. Mater, 12, pp.73~ (2000)
- L. S. Li, , Nano Lett, 4, pp.2261~ (2004)
- C. Mehta, , Appl. Surf. Sci, 256, pp.608~ (2009)
- Z. Chen, , J. Lumin, 145, pp.569~ (2014)
- N. N. Dlamini, , J. Nat. Prod, 12, pp.2645~ (2012)
- Y. Zheng, , Adv. Mater, 19, pp.1475~ (2007)
- C. Wang, , J. Mater. Chem, 19, pp.7016~ (2009)
- Z. Fang, , J. Phys. Chem. C, 113, pp.14145~ (2009)
- P. Shao, , J. Mater. Chem, 21, pp.151~ (2011)
- G. Xue, , J. Lumin, 131, pp.1300~ (2011)
- H. Qian, , J. Phys. Chem. B, 110, pp.9034~ (2006)
- J. Zhang, , Appl. Surf. Sci, 351, pp.655~ (2015)
- A. R. Khezripour, , Optik, 183, pp.294~ (2019)
- G. Y. Lan, , J. Mater. Chem, 17, pp.2661~ (2007)
- P. Reiss, , New J. Chem, 31, pp.1843~ (2007)
- A. P. Hagen, "Inorganic Reactions and Methods, The Formation of Bonds to Halogen (Part 1)", pp.204~ (2009), Wiley
- C. Zhao, , Electrochim. Acta, 273, pp.10~ (2018)
- 하성용, "전자 빔 조사를 이용한 CdSe", CdS 혼성 양자점의 수용성 합성, 2012, pp.62(7), 709~715[DOI]
- M. T. Dong, , Luminescence, 29, pp.818~ (2014)
- K. Saikia, "Facile synthesis of highly luminescent ZnSe(S) alloyed quantum dot for biomedical imaging", Current Applied Physics, 13(5), pp.925~930 (2013), 한국물리학회
- S. Zhang, "Nanostructured Thin Films and Coatings", pp.24~ (2010), CRC Press
- Y. Yu, , Colloids Surf. B, 95, pp.247~ (2012)