내부 도핑 법에 의한 Cu 도핑 Cu:ZnSe 양자점의 수계 합성 및 발광 특성
Aqueous Synthesis and Luminescent Characteristics of Cu:ZnSe Quantum Dots by Internal Doping Method
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Cu-doped ZnSe quantum dots were successfully synthesized in an aqueous solution using an internal doping method. The effects of ligand type, CuSe synthesis temperature, and heating time on Cu-doped ZnSe synthesis were systematically investigated. Of MPA, GSH, TGA, and NAC used as ligands, MPA was the optimal ligand as determined by PL spectrum analysis. In addition, the emission wavelength was found to depend on the synthesis temperature of the internal doping core of CuSe. As the temperature increased, the doping of Cu2+ was enhanced, and the emission wavelength band was redshifted; accordingly, the emission peaks moved from blue to green (up to 550 nm). Thus, the synthesis of Cu:ZnSe using internal doping in aqueous solutions is a potential method for ecomanufacturing of colortuned ZnSe quantum dots for display applications.
Abstract
Cu-doped ZnSe quantum dots were successfully synthesized in an aqueous solution using an internal doping method. The effects of ligand type, CuSe synthesis temperature, and heating time on Cu-doped ZnSe synthesis were systematically investigated. Of MPA, GSH, TGA, and NAC used as ligands, MPA was the optimal ligand as determined by PL spectrum analysis. In addition, the emission wavelength was found to depend on the synthesis temperature of the internal doping core of CuSe. As the temperature increased, the doping of Cu2+ was enhanced, and the emission wavelength band was redshifted; accordingly, the emission peaks moved from blue to green (up to 550 nm). Thus, the synthesis of Cu:ZnSe using internal doping in aqueous solutions is a potential method for ecomanufacturing of colortuned ZnSe quantum dots for display applications.
참고문헌 (25)
- F. Mirnajafizadeh, , Mater. Sci. Eng. C, 64, pp.167~ (2016)
- G. Xue, , J. Lumin, 131, pp.1300~ (2011)
- R. Hernández, , Mater. Lett, 159, pp.229~ (2015)
- G. Y. Lan, , J. Mater. Chem, 17, pp.2661~ (2007)
- Z. Chen, , J. Lumin, 145, pp.569~ (2014)
- Y. G. Kim, , Ceramist, 16, pp.42~ (2013)
- H. Shen, , Dalton Trans, 47, pp.10534~ (2009)
- A. Aboulaich, , Inorg. Chem, 49, pp.10940~ (2010)
- Y. Wu, , J. Mater. Sci. Mater. Electron, 30, pp.21406~ (2019)
- J. Mazher, , Physica E, 16, pp.209~ (2003)
- J. F. Suyver, , Appl. Phys. Lett, 79, pp.4222~ (2001)
- S. Xu, , Nanotechnology, 22, pp.275605~ (2011)
- S. Jana, , Chem. Commun, 46, pp.2853~ (2010)
- G. Xue, , J. Lumin, 131, pp.1300~ (2011)
- C. Wang, , Nanotechnology, 26, pp.305601~ (2015)
- C. Wang, , J. Phys. Chem. C, 115, pp.18486~ (2011)
- N. Pradhan, , J. Am. Chem. Soc, 129, pp.3339~ (2007)
- S. W. Kim, , Polymer Science and Technology, 23, pp.493~ (2012)
- S. Xu, , Nanotechnology, 22, pp.275605~ (2011)
- Z. Deng, , Langmuir, 25, pp.434~ (2009)
- L. Sun, , Mater. Express, 5, pp.219~ (2015)
- 백금지, "글루타티온이 캡핑된 ZnSe 나노 입자 발광 특성에 미치는 합성 조건의 영향", 한국분말재료학회지, 28(1), pp.44~50 (2021), 한국분말재료학회
- H. S. Hong, , J. Crystal Growth, 535, pp.125523~ (2020)
- N. Pradhan, , J. Am. Chem. Soc, 127, pp.17586~ (2005)
- Y. Wu, , J. Mater. Sci. Mater. Electron, 30, pp.21406~ (2019)