SM45C재의 PVD코팅과 필름에 의한 트라이볼러지 특성
Variations in Tribological Characteristics of SM45C by PVD Coating and Thin Films
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In order to accumulate data to lower the friction coefficient of a press mold, tribological tests were performed before and after coating SM45C with a PVC/PO film and plasma coating (CrN, concept). The ultrasonic nanocrystal surface modification (UNSM)-treated material had a nano-size surface texture, high surface hardness, and large and deep compressive residual stress formation. Even when the load was doubled, the small amount of abrasion, small weight of the abrasion, and width and depth of the abrasion did not increase as much as those of untreated materials. A comparison of the weight change before and after the tribological test with the CrN and the concept coating material and that of the untreated material showed that the wear loss of the concept coating material and P-UNSM treated material (that is, the UNSM treated material treated with the concept coating) showed a tendency to decrease by approximately 55–75%. Concept 100N had a lower friction coefficient of about 0.6, and P-UNSM-30-100N showed almost the same curve as concept 100N and had a low coefficient of friction of about 0.6. The concept multilayer coating had a thickness of 5.32 μm. In the beginning, the coefficient of friction decreased because of the plasma coating, but it started to increase from about 250–300 s. After about 350 s, the coefficient of friction tended to approach the friction coefficient of the SM45C base metal. The SGV-280F film-attached test specimen was slightly pushed back and forth, but the SM45C base material was not exposed due to abrasion. The friction coefficient was 0.22, which was the lowest, and the tribological property was the best in this study.
Abstract
In order to accumulate data to lower the friction coefficient of a press mold, tribological tests were performed before and after coating SM45C with a PVC/PO film and plasma coating (CrN, concept). The ultrasonic nanocrystal surface modification (UNSM)-treated material had a nano-size surface texture, high surface hardness, and large and deep compressive residual stress formation. Even when the load was doubled, the small amount of abrasion, small weight of the abrasion, and width and depth of the abrasion did not increase as much as those of untreated materials. A comparison of the weight change before and after the tribological test with the CrN and the concept coating material and that of the untreated material showed that the wear loss of the concept coating material and P-UNSM treated material (that is, the UNSM treated material treated with the concept coating) showed a tendency to decrease by approximately 55–75%. Concept 100N had a lower friction coefficient of about 0.6, and P-UNSM-30-100N showed almost the same curve as concept 100N and had a low coefficient of friction of about 0.6. The concept multilayer coating had a thickness of 5.32 μm. In the beginning, the coefficient of friction decreased because of the plasma coating, but it started to increase from about 250–300 s. After about 350 s, the coefficient of friction tended to approach the friction coefficient of the SM45C base metal. The SGV-280F film-attached test specimen was slightly pushed back and forth, but the SM45C base material was not exposed due to abrasion. The friction coefficient was 0.22, which was the lowest, and the tribological property was the best in this study.
참고문헌 (13)
- Amanov, A., "Micro-dimpled Surface by Ultrasonic Nanocrystal Surface Modification and Its Tribological Effects", Wear, 286, pp.136~144 (2012)
- Amanov, A., "The Influence of DLC Coating on the Mechanical and Frictional Properties of Unpeened and Peened Cu-based Bimetal under Dry Sliding Conditions", Materials Chemistry and Physics, 143, pp.814~824 (2014)
- Chun, M. S., "Experimental Investigation on the Impact Behavior of Membrane Type LNG Carrier Insulation System", Journal of Loss Prevention in the Process Industries, 22(6), pp.901~907 (2009)
- Gim, J. S., "Introduction to PVD", PACVD Coating, 2007, pp.24(5), 7~13
- 전용준, "마모특성 및 유한요소해석을 이용한 프레스금형 손상 간접예측", 소성∙가공, 23(1), pp.29~34 (2014), 한국소성∙가공학회
- Kim, B. C., "Pressure Resistance of the Corrugated Stainless Steel Membranes of LNG Carriers", Ocean Engineering, 38, pp.592~608 (2011)
- Kim, H. S., "A Comparative Evaluation of Fatigue and Fracture Characteristics of Structural Components of Liquefied Natural Gas Carrier Insulation System", Journal of Pressure Vessel Technology, 135(2), pp.021405~ (2013)
- Kim, M. H., "Fatigue Strength Assessment of MARK-III Type LNG Cargo Containment System", Ocean Engineering, 37, pp.1243~1252 (2010)
- 이승철, "UNSM 기술을 이용한 초경의 기계적 특성변화", 한국트라이볼로지학회지, 31(4), pp.157~162 (2015), 한국트라이볼로지학회[DOI]
- Pyun, Y. S., "Fatigue Characteristics of SAE52100 Steel via Ultrasonic Nanocrystal Surface Modification Technology", Journal of Nanoscience and Nanotechnology, 12, pp.6089~6095 (2012)
- 서창민, "수소취화된 인코넬 718의 VHCF(Very High Cycle Fatigue) 피로특성에 관한 연구", 대한기계학회논문집 A, 40(7), pp.637~646 (2016), 대한기계학회
- Suh, C. M., "Fatigue and Mechanical Characteristics of Nanostructured Tool Steel by Ultrasonic Cold Forging Technology", Materials Science and Engineering: A, 443(1-2), pp.101~106 (2007)
- Yu, Y. H., "Cryogenic Reliability of the Sandwich Insulation Board for LNG Ship", Composite Structures, 95, pp.547~556 (2013)