중간층 조건에 따른 Cr-Mo-N 막의 상형성 및 마찰마모 거동 연구
Tribology and Phase Evolution of Cr-Mo-N Coatings with Different Interlayer Condition
0
조회
0
다운로드
4
인용
0
참고문헌
키워드
초록
Phase evolution and tribological behavior of Cr-Mo-N multi compositional films with different interlayer were investigated. The films were deposited by hybrid PVD (Physical Vapor Deposition) system consisted of dc unbalanced magnetron (UBM) sputtering and arc ion plating (AIP) sources. A pure molybdenum (Mo)was used as sputtering target and also a pure Cr was used as AIP target to form the Cr-Mo-N films. Various growth planes were found, no textured surface, in all of the multi composition films. Maximum value of microhardness was measured in Cr-Mo-N film with Mo interlayer as 29 GPa. Composition film was mainly showed the aspect of the adhesive wear than CrN film. The friction coefficient was decreased from 0.6 for pure CrN coating to 0.35 for Cr-Mo-N film with Mo interlayer. This result may come from the formation of metal oxide tribo-layer which is known as solid lubricant during the wear test.
Abstract
Phase evolution and tribological behavior of Cr-Mo-N multi compositional films with different interlayer were investigated. The films were deposited by hybrid PVD (Physical Vapor Deposition) system consisted of dc unbalanced magnetron (UBM) sputtering and arc ion plating (AIP) sources. A pure molybdenum (Mo)was used as sputtering target and also a pure Cr was used as AIP target to form the Cr-Mo-N films. Various growth planes were found, no textured surface, in all of the multi composition films. Maximum value of microhardness was measured in Cr-Mo-N film with Mo interlayer as 29 GPa. Composition film was mainly showed the aspect of the adhesive wear than CrN film. The friction coefficient was decreased from 0.6 for pure CrN coating to 0.35 for Cr-Mo-N film with Mo interlayer. This result may come from the formation of metal oxide tribo-layer which is known as solid lubricant during the wear test.
참고문헌 (23)
- 이상율, "복합표면처리된 CrN박막의 밀착력에 미치는 스퍼터링 효과에 관한 연구", 한국표면공학회지, 39(1), pp.1~8 (2006), 한국표면공학회
- F. R. Lamastra, , Surf. Coat. Technol, 200, pp.6172~ (2006)
- B. Casas, , J. Mater. Sci, 41, pp.5123~ (2006)
- C. P. Mulligan, , Surf. Coat. Technol, 203, pp.584~ (2008)
- A. Thobor-Keck, , Surf. Coat. Technol, 200, pp.264~ (2005)
- S. H. Shin, , Surf. Coat. Technol, 202, pp.5613~ (2008)
- C. W. Zou, , J. Alloys and Compounds, 485, pp.236~ (2009)
- J. H. Jeon, , Surf. Coat. Technol, 200, pp.1635~ (2005)
- 정민재, "마그네트론 스퍼터링에 의하여 다양한 기판 위에 증착된 CrN 박막의 핵생성과 성장거동", 한국표면공학회지, 35(1), pp.33~38 (2002), 한국표면공학회
- S. Han, , Thin Soild Film, 436, pp.238~ (2003)
- C. H. Hsu, , Surf. Coat. Technol, 203, pp.868~ (2008)
- H. Y. Chen, , Mater. Lett, 58, pp.2924~ (2004)
- G. Li, , Tsinghua Sci. Technol, 10, pp.690~ (2005)
- Y. Zhang, , Mater. Sci. Eng. A, 438, pp.710~ (2006)
- Y. J. Kim, , Surf. Coat. Technol, 202, pp.5508~ (2008)
- J. Creus, , Surf. Coat. Technol, 107, pp.183~ (1998)
- S. Han, , Thin Solid Films, 377, pp.578~ (2000)
- S. Han, , Surf. Coat, 133, pp.460~ (2000)
- A. Conde, , Surf. Coat. Technol, 201, pp.2690~ (2006)
- P. Hones, , Thin Solid Films, 332, pp.240~ (1998)
- K. H. Kim, , Surf. Coat. Technol, 201, pp.4068~ (2006)
- E. Y. Choi, , J. Mater. Processing Technol, 187, pp.566~ (2007)
- Q. Yang, , Surf. Coat. Technol, 200, pp.1709~ (2005)