Sintering behavior and mechanical properties of zirconia compacts fabricated by uniaxial press forming
2
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
PURPOSE. The purpose of this study was to compare the linear sintering behavior of presintered zirconia blocks of various densities. The mechanical properties of the resulting sintered zirconia blocks were then analyzed. MATERIALS AND METHODS. Three experimental groups of dental zirconia blocks, with a different presintering density each, were designed in the present study. Kavo Everest(R). ZS blanks (Kavo, Biberach, Germany) were used as a control group. The experimental group blocks were fabricated from commercial yttria-stabilized tetragonal zirconia powder (KZ-3YF (SD) Type A, KCM. Corporation, Nagoya, Japan). The biaxial flexural strengths, microhardnesses, and microstructures of the sintered blocks were then investigated. The linear sintering shrinkages of blocks were calculated and compared. RESULTS. Despite their different presintered densities, the sintered blocks of the control and experimental groups showed similar mechanical properties. However, the sintered block had different linear sintering shrinkage rate depending on the density of the presintered block. As the density of the presintered block increased, the linear sintering shrinkage decreased. In the experimental blocks, the three sectioned pieces of each block showed the different linear shrinkage depending on the area. The tops of the experimental blocks showed the lowest linear sintering shrinkage, whereas the bottoms of the experimental blocks showed the highest linear sintering shrinkage. CONCLUSION. Within the limitations of this study, the density difference of the presintered zirconia block did not affect the mechanical properties of the sintered zirconia block, but affected the linear sintering shrinkage of the zirconia block.
Abstract
PURPOSE. The purpose of this study was to compare the linear sintering behavior of presintered zirconia blocks of various densities. The mechanical properties of the resulting sintered zirconia blocks were then analyzed. MATERIALS AND METHODS. Three experimental groups of dental zirconia blocks, with a different presintering density each, were designed in the present study. Kavo Everest(R). ZS blanks (Kavo, Biberach, Germany) were used as a control group. The experimental group blocks were fabricated from commercial yttria-stabilized tetragonal zirconia powder (KZ-3YF (SD) Type A, KCM. Corporation, Nagoya, Japan). The biaxial flexural strengths, microhardnesses, and microstructures of the sintered blocks were then investigated. The linear sintering shrinkages of blocks were calculated and compared. RESULTS. Despite their different presintered densities, the sintered blocks of the control and experimental groups showed similar mechanical properties. However, the sintered block had different linear sintering shrinkage rate depending on the density of the presintered block. As the density of the presintered block increased, the linear sintering shrinkage decreased. In the experimental blocks, the three sectioned pieces of each block showed the different linear shrinkage depending on the area. The tops of the experimental blocks showed the lowest linear sintering shrinkage, whereas the bottoms of the experimental blocks showed the highest linear sintering shrinkage. CONCLUSION. Within the limitations of this study, the density difference of the presintered zirconia block did not affect the mechanical properties of the sintered zirconia block, but affected the linear sintering shrinkage of the zirconia block.
참고문헌 (28)
- Lehner CR, "All-ceramic crowns", Curr Opin Dent, 2, pp.45~52 (1992)
- Bindl A, "An up to 5-year clinical evaluation of posterior in-ceram CAD", CAM core crowns, 2002, pp.15, 451~456
- Mo¨rmann WH, "All-ceramic,chair-side computeraided design", computer-aided machining restorations, 2002, pp.46, 405~426
- Pera P, "In vitro marginal adaptation of alumina porcelain ceramic crowns", J Prosthet Dent, 72, pp.585~590 (1994)
- Rinke S, "Marginal accuracy and fracture strength of conventional and copy-milled all-ceramic crowns", Int J Prosthodont, 8, pp.303~310 (1995)
- Sulaiman F, "A comparison of the marginal fit of In-Ceram,IPS Empress,and Procera crowns", Int J Prosthodont, 10, pp.478~484 (1997)
- Marquardt P, "Survival rates of IPS empress 2 all-ceramic crowns and fixed partial dentures:results of a 5-year prospective clinical study", Quintessence Int, 37, pp.253~259 (2006)
- Sorensen JA, "In-Ceram fixed partial dentures:three-year clinical trial results", J Calif Dent Assoc, 26, pp.207~214 (1998)
- Sorensen JA, "A clinical investigation on three-unit fixed partial dentures fabricated with a lithium disilicate glass-ceramic", Pract Periodontics Aesthet Dent, 11, pp.95~106 (1999)
- Tinschert J, "Fracture resistance of lithium disilicate-,alumina-,and zirconiabased three-unit fixed partial dentures:a laboratory study", Int J Prosthodont, 14, pp.231~238 (2001)
- Guazzato M, "Strength,fracture toughness and microstructure of a selection of all-ceramic materials.Part II.Zirconia-based dental ceramics", Dent Mater, 20, pp.449~456 (2004)
- Tinschert J, "Structural reliability of alumina-,feldspar-,leucite-,mica-and zirconia-based ceramics", J Dent, 28, pp.529~535 (2000)
- Porter DL, "Mechanisms of toughening partially stabilized zirconia(PSZ)", J Am Ceram Soc, 60, pp.183~184 (1977)
- Cales B, "Colored zirconia ceramics for dental applications", Bioceramics, 11, pp.591~594 (1998)
- Kosmac T, "The effect of surface grinding and sandblasting on flexural strength and reliability of Y-TZP zirconia ceramic", Dent Mater, 15, pp.426~433 (1999)
- Garvie RC, "Ceramic steel?", Nature, 258, pp.703~704 (1975)
- Kitazaki H, "Effect of amount of grinding on flexural strength of dental ceramics", J Med Dent Sci, 48, pp.7~13 (2001)
- Chevalier J, "Low-temperature aging of YTZP ceramics", J Am Ceram Soc, 82, pp.2150~2154 (1999)
- Piconi C, "Zirconia as a ceramic biomaterial", Biomaterials, 20, pp.1~25 (1999)
- Duke ES, "The status of CAD", CAM in restorative dentistry, 2001, pp.22, 968~972
- Suttor D, "LAVA-the system for all-ceramic ZrO2 crown and bridge frameworks", Int J Comput Dent, 4, pp.195~206 (2001)
- Heydecke G, "Material characteristics of a novel shrinkage-free ZrSiO4 ceramic for the fabrication of posterior crowns", Dent Mater, 23, pp.785~791 (2007)
- ISO 6872, "International standard for dental ceramic. 2nd ed" (1995)
- Callister WD, "Failure. In: Fundamental of materials science and engineering. An integrated approach. 2nd ed", pp.282~356 (2005), John Wiley & Sons Inc
- Fre′chette V, "Failure analysis of brittle materials. Advances in ceramics , American Ceramic Society" (1990), Westerville, OH
- Ban S, "Influence of test method on failure stress of brittle dental materials", J Dent Res, 69, pp.1791~1799 (1990)
- Giordano R, "Materials for chairside CAD", CAM-produced restorations, 2006, pp.137, 14S~21S
- "Zirconia-Physical and mechanical property comparison of the different types of zirconias"[URL]