The comparisons of layers and the effect of additional firings on flexural strength and translucency of 5Y-ZP
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Purpose: The purpose of this in vitro study was to investigate the flexural strength and translucency of three layers in 5Y-ZP and to assess the effect of additional firings on these properties. Materials and Methods: Sintered zirconia blocks were sectioned according to three layers : incisal, transition, and body. Disc-shaped specimens were fabricated from each layer. The diameter of specimens was 15.0 mm and each thickness of specimens for biaxial flexural strength test and translucency was 1.2 mm and 1.0 mm. The specimens were classified into subgroups according to the number of firing (0, 1, and 3 times; n = 10/subgroup) and the additional firings were performed under 900°C using a furnace. Biaxial flexural strength and translucency was measured using universal testing machine and uv-vis spectrophotometer. X-ray diffraction (XRD) analysis was used for measurement of the phase identification. Oneway ANOVA, Tukey HSD test were performed (α = 0.05). Results: There was no significant difference in flexural strength between the three layers (P > 0.05), while there was significant difference in translucency between different layers (P < 0.05). The flexural strength of incisal and transition layer was decreased by the single additional firing, and the three additional firings significantly decreased the flexural strength of three layers. The translucency of layer was decreased by additional firings except the body layer. The XRD patterns of all groups were similar. Conclusion: Three layers of 5Y-ZP were different only in translucency. Additional firings affected the flexural strength and translucency differently depending on the layers but crystalline phases were not changed.
Abstract
Purpose: The purpose of this in vitro study was to investigate the flexural strength and translucency of three layers in 5Y-ZP and to assess the effect of additional firings on these properties. Materials and Methods: Sintered zirconia blocks were sectioned according to three layers : incisal, transition, and body. Disc-shaped specimens were fabricated from each layer. The diameter of specimens was 15.0 mm and each thickness of specimens for biaxial flexural strength test and translucency was 1.2 mm and 1.0 mm. The specimens were classified into subgroups according to the number of firing (0, 1, and 3 times; n = 10/subgroup) and the additional firings were performed under 900°C using a furnace. Biaxial flexural strength and translucency was measured using universal testing machine and uv-vis spectrophotometer. X-ray diffraction (XRD) analysis was used for measurement of the phase identification. Oneway ANOVA, Tukey HSD test were performed (α = 0.05). Results: There was no significant difference in flexural strength between the three layers (P > 0.05), while there was significant difference in translucency between different layers (P < 0.05). The flexural strength of incisal and transition layer was decreased by the single additional firing, and the three additional firings significantly decreased the flexural strength of three layers. The translucency of layer was decreased by additional firings except the body layer. The XRD patterns of all groups were similar. Conclusion: Three layers of 5Y-ZP were different only in translucency. Additional firings affected the flexural strength and translucency differently depending on the layers but crystalline phases were not changed.
참고문헌 (44)
- Bagby M, "Metal ceramic compatibility : a review of the literature", J Prosthet Dent, 63, pp.21~25 (1990)
- Isgrò G, "The influence of the veneering porcelain and different surface treatments on the biaxial flexural strength of a heat-pressed ceramic", J Prosthet Dent, 90, pp.465~473 (2003)
- 김희경, "Effect of the amount of thickness reduction on color and translucency of dental monolithic zirconia ceramics", The Journal of Advanced of Prosthodontics, 8(1), pp.37~42 (2016), 대한치과보철학회[DOI]
- Christel P, "Mechanical properties and short-term in-vivo evaluation of yttrium-oxide-partially-stabilized zirconia", J Biomed Mater Res, 23, pp.45~61 (1989)
- Teichmann M, "Ten-year survival and chipping rates and clinical quality grading of zirconia-based fixed dental prostheses", Clin Oral Investig, 22, pp.2905~2915 (2018)
- Stefanescu C, "Survival Rates and Complications for Zirconia-Based Fixed Dental Prostheses in a Period up to 10 Years : A Systematic Review", Eur J Prosthodont Restor Dent, 26, pp.54~61 (2018)
- Christensen GJ, "The all-ceramic restoration dilemma : where are we", J Am Dent Assoc, 142, pp.668~671 (2011)
- Marchack BW, "Complete and partial contour zirconia designs for crowns and fixed dental prostheses : a clinical report", J Prosthet Dent, 106, pp.145~152 (2011)
- Thalji GN, "Implant-supported fixed dental rehabilitation with monolithic zirconia : a clinical case report", J Esthet Restor Dent, 26, pp.88~96 (2014)
- Malkondu O, "Influence of type of cement on the color and translucency of monolithic zirconia", J Prosthet Dent, 116, pp.902~908 (2016)
- da Silva LH, "Dental ceramics : a review of new materials and processing methods", Braz Oral Res, 31(Suppl 1), pp.e58~ (2017)
- da Silva LH, "Monolithic Zirconia for Prosthetic Reconstructions : Advantages and Limitations", Curr Oral Health Rep, 4, pp.197~200 (2017)
- Zhang F, "Strength, toughness and aging stability of highly-translucent Y-TZP ceramics for dental restorations", Dent Mater, 32, pp.e327~e337 (2016)
- Kwon SJ, "Comparison of the mechanical properties of translucent zirconia and lithium disilicate", J Prosthet Dent, 120, pp.132~137 (2018)
- Zhang Y, "Novel Zirconia Materials in Dentistry", J Dent Res, 97, pp.140~147 (2018)
- Ueda K, "Light transmittance by a multi-coloured zirconia material", Dent Mater J, 34, pp.310~314 (2015)
- Baldissara P, "Translucency of zirconia copings made with different CAD", CAM systems, 2010, pp.104, 6~12
- Sato H, "Mechanical properties of dental zirconia ceramics changed with sandblasting and heat treatment", Dent Mater J, 27, pp.408~414 (2008)
- Zhang Y, "Making yttria-stabilized tetragonal zirconia translucent", Dent Mater, 30, pp.1195~1203 (2014)
- Nakamura K, "Effect of low-temperature degradation on the mechanical and microstructural properties of tooth-colored 3Y-TZP ceramics", J Mech Behav Biomed Mater, 53, pp.301~311 (2016)
- Shamseddine L, "Relative Translucency of a Multilayered Ultratranslucent Zirconia Material", J Contemp Dent Pract, 18, pp.1099~1106 (2017)
- Kolakarnprasert N, "New multi-layered zirconias: Composition, microstructure and translucency", Dent Mater, 35, pp.797~806 (2019)
- "ISO 6872:2015 Dentistry - ceramic materials" (2021)[URL]
- ASTM International, "ASTM F394-78, Test Method for Biaxial Flexure Strength (Modulus of Rupture) of Ceramic Substrates (Withdrawn 2001)", ~ (1996)
- "CIE S 017-2011. International lighting vocabulary" (2015)[URL]
- "JIS Z 8113-1998. Lighting vocabulary" (2015)[URL]
- 서덕규, "광중합형 레진의 3점 굴곡 강도와 이축 굴곡 강도 측정 방법에 대한 상대적 신뢰도의 비교", Restorative Dentistry and Endodontics, 31(1), pp.58~65 (2006), 대한치과보존학회
- Anusavice KJ, "Which mechanical and physical testing methods are relevant for predicting the clinical performance of ceramicbased dental prostheses", Clin Oral Implants Res, 18, pp.218~231 (2007)
- Wille S, "Low temperature degradation of single layers of multilayered zirconia in comparison to conventional unshaded zirconia: Phase transformation and flexural strength", J Mech Behav Biomed Mater, 77, pp.171~175 (2018)
- Xie H, "Effects of multiple firings on the low-temperature degradation of dental yttria-stabilized tetragonal zirconia", J Prosthet Dent, 115, pp.495~500 (2016)
- Nakamura K, "Influence of grain size and veneer firing process on the flexural strength of zirconia ceramics", Eur J Oral Sci, 120, pp.249~254 (2012)
- Chevalier J, "What future for zirconia as a biomaterial?", Biomaterials, 27, pp.535~543 (2006)
- Brodbelt RH, "Translucency of dental porcelains", J Dent Res, 59, pp.70~75 (1980)
- Johnston WM, "Color and translucency changes during and after curing of esthetic restorative materials", Dent Mater, 13, pp.89~97 (1997)
- Wang F, "Translucency of dental ceramics with different thicknesses", J Prosthet Dent, 110, pp.14~20 (2013)
- Awad D, "Translucency of esthetic dental restorative CAD", CAM materials and composite resins with respect to thickness and surface roughness, 2015, pp.113, 534~540
- Harada K, "A comparative evaluation of the translucency of zirconias and lithium disilicate for monolithic restorations", J Prosthet Dent, 116, pp.257~263 (2016)
- Spink LS, "Comparison of an absolute and surrogate measure of relative translucency in dental ceramics", Dent Mater, 29, pp.702~707 (2013)
- Nassary Zadeh P, "Flexural strength, fracture toughness, and translucency of cubic", tetragonal zirconia materials, 2018, pp.120, 948~954
- Camposilvan E, "Aging resistance, mechanical properties and translucency of different yttria-stabilized zirconia ceramics for monolithic dental crown applications", Dent Mater, 34, pp.879~890 (2018)
- Inokoshi M, "Crystallographic and morphological analysis of sandblasted highly translucent dental zirconia", Dent Mater, 34, pp.508~518 (2018)
- Cho MS, "Changes in optical properties of enamel porcelain after repeated external staining", J Prosthet Dent, 95, pp.437~443 (2006)
- Lai X, "Effects of small-grit grinding and glazing on mechanical behaviors and ageing resistance of a supertranslucent dental zirconia", J Dent, 66, pp.23~31 (2017)
- Sulaiman TA, "The effect of staining and vacuum sintering on optical and mechanical properties of partially and fully stabilized monolithic zirconia", Dent Mater J, 34, pp.605~610 (2015)