Purpose. To investigate the effect of sintering programs and surface treatments on surface properties, phase transformation and flexural strength of monolithic zirconia. Materials and Methods. Zirconia specimens were sintered using three distinct sintering programs [classic (C), speed (S), and superspeed (SS)] (n = 56, each). One sample from each group underwent scanning electron microscopy (SEM) and grain size analysis following sintering. Remaining samples were divided into five subgroups (n = 11) based on the surface treatments: control (CL), polish (P), glaze (G), grind + polish (GP), and grind + glaze (GG). One sample from each subgroup underwent SEM analysis. Remaining samples were thermally aged. Monoclinic phase volume, surface roughness, and three-point flexural strength were measured. Monoclinic phase volume and surface roughness were analyzed by Kruskal-Wallis and Dunn tests. Flexural strength was analyzed by two-way ANOVA and Weibull analysis. The relationships among the groups were analyzed using Spearman’s correlation analysis. Results. Sintering program, surface treatment, and sintering × surface treatment (P ≤ .010) affected the monoclinic phase volume, whereas the type of surface treatment and sintering × surface treatment affected the surface roughness (P < .001). Type of sintering program or surface treatment did not affect the flexural strength. Weibull analysis revealed no significant differences between the m and σo values. Monoclinic phase volume was positively correlated with surface roughness in the SGG and SSP groups. Conclusion. After sintering monolithic zirconia in each of the three sintering programs, each of the surface treatments can be used. However, for surface quality and aging resistance, G or GG can be recommended as a surface finishing method.
Abstract
Purpose. To investigate the effect of sintering programs and surface treatments on surface properties, phase transformation and flexural strength of monolithic zirconia. Materials and Methods. Zirconia specimens were sintered using three distinct sintering programs [classic (C), speed (S), and superspeed (SS)] (n = 56, each). One sample from each group underwent scanning electron microscopy (SEM) and grain size analysis following sintering. Remaining samples were divided into five subgroups (n = 11) based on the surface treatments: control (CL), polish (P), glaze (G), grind + polish (GP), and grind + glaze (GG). One sample from each subgroup underwent SEM analysis. Remaining samples were thermally aged. Monoclinic phase volume, surface roughness, and three-point flexural strength were measured. Monoclinic phase volume and surface roughness were analyzed by Kruskal-Wallis and Dunn tests. Flexural strength was analyzed by two-way ANOVA and Weibull analysis. The relationships among the groups were analyzed using Spearman’s correlation analysis. Results. Sintering program, surface treatment, and sintering × surface treatment (P ≤ .010) affected the monoclinic phase volume, whereas the type of surface treatment and sintering × surface treatment affected the surface roughness (P < .001). Type of sintering program or surface treatment did not affect the flexural strength. Weibull analysis revealed no significant differences between the m and σo values. Monoclinic phase volume was positively correlated with surface roughness in the SGG and SSP groups. Conclusion. After sintering monolithic zirconia in each of the three sintering programs, each of the surface treatments can be used. However, for surface quality and aging resistance, G or GG can be recommended as a surface finishing method.
참고문헌 (50)
- Manicone PF, "An overview of zirconia ceramics : basic properties and clinical applications", J Dent, 35, pp.819~826 (2007)
- Alao AR, "Surface quality of yttria-stabilized tetragonal zirconia polycrystal in CAD", CAM milling, sintering, polishing and sandblasting processes, 2017, pp.65, 102~116
- Preis V, "Wear performance of monolithic dental ceramics with different surface treatments", Quintessence Int, 44, pp.393~405 (2013)
- Caglar I, "The effect of various polishing systems on surface roughness and phase transformation of monolithic zirconia", J Adv Prosthodont, 10, pp.132~137 (2018)
- Denry I, "State of the art of zirconia for dental applications", Dent Mater, 24, pp.299~307 (2008)
- Işeri U, "Comparison of different grinding procedures on the flexural strength of zirconia", J Prosthet Dent, 107, pp.309~315 (2012)
- Kosmac T, "Strength and reliability of surface treated Y-TZP dental ceramics", J Biomed Mater Res, 53, pp.304~313 (2000)
- Cotes C, "Effects of aging procedures on the topographic surface, structural stability, and mechanical strength of a ZrO2-based dental ceramic", Dent Mater, 30, pp.e396~e404 (2014)
- Inokoshi M, "Aging resistance of surface-treated dental zirconia", Dent Mater, 31, pp.182~194 (2015)
- Muñoz EM, "The effects of mechanical and hydrothermal aging on microstructure and biaxial flexural strength of an anterior and a posterior monolithic zirconia", J Dent, 63, pp.94~102 (2017)
- Borchers L, "Influence of hydrothermal and mechanical conditions on the strength of zirconia", Acta Biomater, 6, pp.4547~4552 (2010)
- Souza RO, "Air-particle abrasion on zirconia ceramic using different protocols : effects on biaxial flexural strength after cyclic loading, phase transformation and surface topography", J Mech Behav Biomed Mater, 26, pp.155~163 (2013)
- Kosmac T, "The effect of surface grinding and sandblasting on flexural strength and reliability of Y-TZP zirconia ceramic", Dent Mater, 15, pp.426~433 (1999)
- Stawarczyk B, "The effect of zirconia sintering temperature on flexural strength, grain size, and contrast ratio", Clin Oral Investig, 17, pp.269~274 (2013)
- Mai HN, "Effects of different finishing", polishing protocols and systems for monolithic zirconia on surface topography, phase transformation, and biofilm formation, 2019, pp.11, 81~87
- Zucuni CP, "Fatigue strength of yttria-stabilized zirconia polycrystals : Effects of grinding, polishing, glazing, and heat treatment", J Mech Behav Biomed Mater, 75, pp.512~520 (2017)
- Zucuni CP, "Grinding, polishing and glazing of the occlusal surface do not affect the load-bearing capacity under fatigue and survival rates of bonded monolithic fully-stabilized zirconia simplified restorations", J Mech Behav Biomed Mater, 103, pp.103528~ (2020)
- DE Souza RH, "Flexural strength and crystalline stability of a monolithic translucent zirconia subjected to grinding, polishing and thermal challenges", Ceram Int, 46, pp.26168~26175 (2020)
- Mešić K, "The effect of aging on composition and surface of translucent zirconia ceramic", Acta Stomatol Croat, 54, pp.339~352 (2020)
- Vila-Nova TEL, "Effect of finishing", polishing techniques and low temperature degradation on the surface topography, phase transformation and flexural strength of ultra-translucent ZrO2 ceramic, 2020, pp.36, e126~e139
- Cardoso KV, "Effect of sintering temperature on microstructure, flexural strength, and optical properties of a fully stabilized monolithic zirconia", J Prosthet Dent, 124, pp.594~598 (2020)
- Grambow J, "Impact of changes in sintering temperatures on characteristics of 4YSZ and 5YSZ", J Mech Behav Biomed Mater, 120, pp.104586~ (2021)
- Juntavee N, "Flexural strength of different monolithic computer-assisted design and computer-assisted manufacturing ceramic materials upon different thermal tempering processes", Eur J Dent, 14, pp.566~574 (2020)
- Juntavee N, "Influence of thermal tempering processes on color characteristics of different monolithic computer-assisted design and computer-assisted manufacturing ceramic materials", J Clin Exp Dent, 11, pp.e614~e624 (2019)
- Kwon WC, "Evaluation of mechanical properties of dental zirconia in different milling conditions and sintering temperatures", J Prosthet Dent, 130, pp.909~916 (2023)
- Li L, "Super-speed sintered dental zirconia for chair-side one-visit application", Austin J Nutri Food Sci, 6, pp.1105~ (2018)
- Durkan R, "Biaxial flexural strength and phase transformation characteristics of dental monolithic zirconia ceramics with different sintering durations : An in vitro study", J Prosthet Dent, 128, pp.498~504 (2022)
- Kong MC, "Effect of sintering condition and low-temperature degradation on the flexural strength and phase transformation of zirconia", J Prosthet Dent, 126, pp.692~ (2021)
- Liu H, "Influence of high-speed sintering protocols on translucency, mechanical properties, microstructure, crystallography, and low-temperature degradation of highly translucent zirconia", Dent Mater, 38, pp.451~468 (2022)
- Oyar P, "Effects of sintering time and hydrothermal aging on the mechanical properties of monolithic zirconia ceramic systems", J Prosthet Dent, 126, pp.688~691 (2021)
- Hafezeqoran A, "Effect of sintering speed, aging processes, and different surface treatments on the optical and surface properties of monolithic zirconia restorations", J Prosthet Dent, 130, pp.917~926 (2023)
- inCoris TZI, "Translucent zirconia ceramic blocks and discs for CEREC and inLab Processing instructions:Restoration production for crowns and bridges", pp.1~22 (2016), Sirona Dental Systems GmbH
- Gale MS, "Thermal cycling procedures for laboratory testing of dental restorations", J Dent, 27, pp.89~99 (1999)
- Garvie RC, "Phase analysis in zirconia systems", J Am Ceram Soc, 55, pp.303~305 (1972)
- "ISO 6872. Dentistry-ceramic materials", International Standards Organization (ISO), ~ (2008)
- Fischer J, "Flexural strength of veneering ceramics for zirconia", J Dent, 36, pp.316~321 (2008)
- Bona AD, "Weibull analysis and flexural strength of hot-pressed core and veneered ceramic structures", Dent Mater, 19, pp.662~669 (2003)
- Asaad R, "Influence of different sintering protocols on translucency and fracture resistance of monolithic zirconia crowns", Egyptian Dent J, 66, pp.2649~2660 (2020)
- Amat NF, "Effect of sintering temperature on the aging resistance and mechanical properties of monolithic zirconia", J Mater Res Technol, 8, pp.1092~1101 (2019)
- Stawarczyk B, "Zirconia ceramics, their contrast ratio and grain size depending on sintering parameters", Dent Mater J, 33, pp.591~598 (2014)
- Hjerppe J, "Effect of sintering time on biaxial strength of zirconium dioxide", Dent Mater, 25, pp.166~171 (2009)
- Öztürk C, "Effect of sintering parameters on the mechanical properties of monolithic zirconia", J Dent Res Dent Clin Dent Prospects, 13, pp.247~252 (2019)
- Shen J, "Evaluation of the effect of low-temperature degradation on the translucency and mechanical properties of ultra-transparent 5Y-TZP ceramics", Ceram Int, 46, pp.553~559 (2019)
- Siarampi E, "Effect of in vitro aging on the flexural strength and probability to fracture of Y-TZP zirconia ceramics for all-ceramic restorations", Dent Mater, 30, pp.e306~e316 (2014)
- Ebeid K, "Effect of changes in sintering parameters on monolithic translucent zirconia", Dent Mater, 30, pp.e419~e424 (2014)
- Preis V, "Surface properties of monolithic zirconia after dental adjustment treatments and in vitro wear simulation", J Dent, 43, pp.133~139 (2015)
- De Souza GM, "Effect of accelerated aging on dental zirconia-based materials", J Mech Behav Biomed Mater, 65, pp.256~263 (2017)
- Flinn BD, "Influence of aging on flexural strength of translucent zirconia for monolithic restorations", J Prosthet Dent, 117, pp.303~309 (2017)
- Kohorst P, "Low-temperature degradation of different zirconia ceramics for dental applications", Acta Biomater, 8, pp.1213~1220 (2012)
- Nam MG, "Changes in the flexural strength of translucent zirconia due to glazing and low-temperature degradation", J Prosthet Dent, 120, pp.969~ (2018)