Electrodeposition of Copper on AZ91 Mg Alloy in Cyanide Solution
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Copper electrodeposition on AZ91 Mg alloy was studied in views of preferential deposition on α- or β- phases and how to achieve uniform deposition over the entire surface on α- and β-phases in a cyanide solution. The inhomogeneous microstructure of AZ91 Mg alloy, particularly α- and β-phases, was found to result in non-uniform deposition of zincate layer, preferential deposition of zincate on β-phases, which leads to nonuniform growth of copper layer during the following electrodeposition process. The preferential depositions of zincate can be attributed to higher cathodic polarizations on the β-phases. Pin-hole defects in the copper electrodeposit were observed at the center of large size β-phase particles which is ascribed to gas bubbles formed at the β-phases. The activation of AZ91 Mg alloy in hydrofluoric acid solution was used to obtain uniform growth of zincate layer on both the α- and β-phases. By choosing an optimum activation time, a uniform zincate layer was obtained on the AZ91 Mg alloy surface and thereby uniform growth of copper was obtained in a cyanide copper electroplating solution.
Abstract
Copper electrodeposition on AZ91 Mg alloy was studied in views of preferential deposition on α- or β- phases and how to achieve uniform deposition over the entire surface on α- and β-phases in a cyanide solution. The inhomogeneous microstructure of AZ91 Mg alloy, particularly α- and β-phases, was found to result in non-uniform deposition of zincate layer, preferential deposition of zincate on β-phases, which leads to nonuniform growth of copper layer during the following electrodeposition process. The preferential depositions of zincate can be attributed to higher cathodic polarizations on the β-phases. Pin-hole defects in the copper electrodeposit were observed at the center of large size β-phase particles which is ascribed to gas bubbles formed at the β-phases. The activation of AZ91 Mg alloy in hydrofluoric acid solution was used to obtain uniform growth of zincate layer on both the α- and β-phases. By choosing an optimum activation time, a uniform zincate layer was obtained on the AZ91 Mg alloy surface and thereby uniform growth of copper was obtained in a cyanide copper electroplating solution.
참고문헌 (24)
- Y. Kojima, "Project of platform of science and technology for advanced magnesium alloys", Mater. Trans, 42, pp.1154~1159 (2001)
- G. L. Song, "Corrosion prevention of magnesium alloys" (2013), Woodhead Publishing Limited
- Nguyen Van Phuong, "Zinc Phosphate Conversion Coatings on Magnesium Alloys: A Review", Metals and Materials International, 19(2), pp.273~281 (2013), 대한금속·재료학회[DOI]
- J. E. Gray, "Protective coatings on magnesium and its alloys – a critical review", J. Alloy Compd, 336, pp.88~113 (2002)
- A. Atrens, "Review of recent developments in the field of magnesium corrosion", Adv. Eng. Mater, 17, pp.400~453 (2015)
- Basit Raza Fazal, "Formation of Cerium Conversion Coatings on AZ31 Magnesium Alloy", 한국표면공학회지, 49(1), pp.1~13 (2016), 한국표면공학회[DOI]
- X. B. Chen, "Corrosion-resistance electrochemical platings on magnesium alloys : A stateof-the-art review", Corrosion, 68, pp.518~535 (2011)
- X. P. Lei, "Successful cyanide free plating protocols on magnesium alloys", T. I. Met. Finish, 88, pp.75~80 (2010)
- F. Czerwinski, "Magnesium alloys – Corrosion and surface treatments", pp.153~184 (2011), InTech
- L. P. Wu, "Progress of electroplating and electroless plating on magnesium alloy", Trans. Nonferrous Met. Soc. China, 20, pp.630~637 (2010)
- C. A. Huang, "A pretreatment with galvanostatic etching for copper electrodeposition on pure magnesium and magnesium alloys in an alkaline copper-sulfate bath", Electrochim. Acta, 53, pp.7235~7241 (2008)
- P. Zhu, "Copper coating electrodeposited directly onto AZ31magnesium alloy", Anti-Corros. Method. M, 60, pp.127~133 (2013)
- J. Tang, "Effect of copper pretreatment on the zincate process and subsequent copper electrodeposition of AZ31 magnesium alloy", J. Electrochem. Soc, 158, pp.D535~D540 (2011)
- P. Zhu, "Electrodeposition of copper coating on AZ31magnesium alloy", Surf. Eng, 28, pp.796~799 (2012)
- J. C. Ballesteros, "Electrodeposition of copper from noncyanide alkaline solution containing tartrate", Int. J. Electrochem. Sci, 6, pp.2632~2651 (2011)
- J. Tang, "Influence of zincate pretreatment on adhesion strength of a copper electroplating layer on AZ91 D magnesium alloy", Surf. Coat. Tech, 205, pp.3050~3057 (2011)
- C. A. Huang, "Copper electrodeposition on a magnesium alloy(AZ80)with a U-Shaped surface", Materials, 7, pp.7366~7378 (2014)
- J. Lee, "Direct nickel electrodeposition on magnesium alloy in pyrophosphate electrolyte", Surf. Coat. Tech, 205, pp.4018~4023 (2011)
- Mordechay Schlesinger, "Modern electroplating", pp.33~78 (2010), A John Wiley & Sons, Inc.
- O. Radovici, "Some aspects of copper electrodeposition from pyrophosphate electrolytes", Electrodepos. Surface Treat, 2, pp.263~273 (1974)
- 이정훈, "불화칼륨이 첨가된 피로인산구리 도금욕에서 마그네슘합금의 전기도금", 대한금속·재료학회지, 48(3), pp.218~224 (2010), 대한금속·재료학회
- J. Kato, "Magnesium based alloys article and a method thereof", US Patent No: 6,068,938, ~
- "ASTM standard D3359-02", ASTM International, ~ (2004)
- Tohru Watanabe, "Nano-plating: Microstructure control theory of plated film and data base of plated film microstructure" (2004), Elsevier