Adhesion and Corrosion Resistance of Electrophoretic Paint on “Electroless” Paint Coated AZ31 Mg Alloy
2
조회
0
다운로드
0
인용
0
참고문헌
초록
The present study investigated the adhesion and corrosion resistance of subsequent electrophoretic paint (E-paint) on “electroless” paint coated AZ31 Mg alloy, which was formed by immersion of AZ31 Mg alloy in E-painting solution. It was found that with increasing immersion time of AZ31 in E-painting solution, the amount of paint deposited by electroless process increased but it decreased the electrochemical equivalent of E-painting process and the adhesion of the subsequent E-paint layer. The E-paint on electroless paint coated AZ31 contained pores with the highest pore density and the largest pore size was obtained on the samples with electroless times of 2 and 5 minutes, respectively. Results of the salt-spray test showed an accelerated growth of blisters over the entire surface of the sample immersed for less than 5 minutes whereas blisters were observed only in the vicinity of the scratch in case of samples treated for 15 and 30 minutes. The E-paint on AZ31 with shorter electroless immersion time in E-painting solution was found to have good adhesion and better corrosion resistance.
Abstract
The present study investigated the adhesion and corrosion resistance of subsequent electrophoretic paint (E-paint) on “electroless” paint coated AZ31 Mg alloy, which was formed by immersion of AZ31 Mg alloy in E-painting solution. It was found that with increasing immersion time of AZ31 in E-painting solution, the amount of paint deposited by electroless process increased but it decreased the electrochemical equivalent of E-painting process and the adhesion of the subsequent E-paint layer. The E-paint on electroless paint coated AZ31 contained pores with the highest pore density and the largest pore size was obtained on the samples with electroless times of 2 and 5 minutes, respectively. Results of the salt-spray test showed an accelerated growth of blisters over the entire surface of the sample immersed for less than 5 minutes whereas blisters were observed only in the vicinity of the scratch in case of samples treated for 15 and 30 minutes. The E-paint on AZ31 with shorter electroless immersion time in E-painting solution was found to have good adhesion and better corrosion resistance.
참고문헌 (30)
- H.E. Friedrich, "Magnesium technology" (2006), Springer
- M. Gupta, "Magnesium, magnesium alloys, and magnesium composites" (2011), John Wiley &Sons
- G.-L. Song, "Corrosion prevention of magnesium alloys" (2013), Elsevier
- G.L. Song, "Corrosion mechanisms of magnesium alloys", 1, pp.11~33 (1999)
- G. Song, "Understanding magnesium corrosion – a framework for improved alloy performance", Adv. Eng. Mater, 5, pp.837~858 (2003)
- J. Gray, "Protective coatings on magnesium and its alloys – a critical review", J. Alloys Compd., 336, pp.88~113 (2002)
- Nguyen Van Phuong, "Zinc Phosphate Conversion Coatings on Magnesium Alloys: A Review", Metals and Materials International, 19(2), pp.273~281 (2013), 대한금속·재료학회[DOI]
- X. Chen, "Corrosion-resistant electrochemical platings on magnesium alloys: a state-of-the-art review", Corrosion, 68, pp.518~535 (2012)
- L. Kouisni, "Phosphate coatings on magnesium alloy AM60 part 1: study of the formation and the growth of zinc phosphate films", Surf. Coat. Technol, 185, pp.58~67 (2004)
- Basit Raza Fazal, "Formation of Cerium Conversion Coatings on AZ31 Magnesium Alloy", 한국표면공학회지, 49(1), pp.1~13 (2016), 한국표면공학회[DOI]
- N. Birbilis, "Exploring corrosion protection of Mg via ionic liquid pretreatment", Surf. Coat. Technol, 201, pp.4496~4504 (2007)
- X. Chen, "Review of corrosion–resistant conversion coatings for magnesium and its alloy", Corrosion, 67, pp.035005-1~035005-16 (2011)
- N. Van Phuong, "Deposition and characterization of E-paint on magnesium alloys", Prog. Org. Coat., 89, pp.91~99 (2015)
- F. Czerwinski, "Magnesium alloys: corrosion and surface treatments" (2011), InTech
- L. Besra, "A review on fundamentals and applications of electrophoretic deposition (EPD)", Prog. Mater Sci., 52, pp.1~61 (2007)
- F. Beck, "Fundamental aspects of electrodeposition of paint", Prog. Org. Coat., 4, pp.1~60 (1976)
- R.-G. Hu, "Recent progress in corrosion protection of magnesium alloys by organic coatings", Prog. Org. Coat., 73, pp.129~141 (2012)
- J. Zhang, "Corrosion protection behavior of AZ31 magnesium alloy with cathodic electrophoretic coating pretreated by silane", Prog. Org. Coat, 66, pp.387~392 (2009)
- G.-L. Song, "“Electroless” E-coating: an innovative surface treatment for magnesium alloys", Electrochem. Solid-State Lett., 12, pp.D77~D79 (2009)
- G.-L. Song, "A dipping E-coating for Mg alloys", Prog. Org. Coat., 70, pp.252~258 (2011)
- G.-L. Song, "The effect of Mg alloy substrate on “electroless” E-coating performance", Corros. Sci., 53, pp.3500~3508 (2011)
- G.-L. Song, "The effect of surface pretreatment on the corrosion performance of electroless E-coating coated AZ31", Corros. Sci., 62, pp.61~72 (2012)
- G.-L. Song, "“Electroless” deposition of a pre-film of electrophoresis coating and its corrosion resistance on a Mg alloy", Electrochim. Acta, 55, pp.2258~2268 (2010)
- ASTM, "Standard Test Methods for Measuring Adhesion by Tape Test, D3359-02, Standard Test Methods for Measuring Adhesion by Tape Test", ASTM International, ~ (2002)
- ASTM, "Standard Practice for Operating Salt Spray (Fog) Apparatus, B117-03, Standard Practice for Operating Salt Spray (Fog) Apparatus", ASTM International, ~ (2003)
- R.C. Weast, "CRC handbook of chemistry and physics" (1988), CRC press
- N. Van Phuong, "Adhesion and corrosion studies of electrophoretic paint on AZ31 Mg alloy pretreated in cerium solution with and without addition of ethanol", Prog. Org. Coat, 102, pp.144~150 (2017)
- M. Taheri, "Analysis of the surface film formed on Mg by exposure to water using a FIB cross-section and STEM–EDS", Corros. Sci, 59, pp.222~228 (2012)
- Y. Luo, "Transition of interface oxide layer from porous Mg(OH)2 to dense MgO induced by polyaniline and corrosion resistance of Mg alloy therefrom", Appl. Surf. Sci., 328, pp.247~254 (2015)
- N. Aćamović, "Influence of substrate on the formation and growth kinetics of cathodic electrocoat paint", Prog. Org. Coat., 25, pp.293~307 (1995)