표면개질 기술에 의한 Cu 기반 바이메탈의 인장강도,스크래치 저항성 및 트라이볼로지 성능 향상
Improvement in Tensile Strength, Scratch Resistance and Tribological Performance of Cu-based Bimetals by Surface Modification Technology
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
In this study, an ultrasonic nanocrystal surface modification (UNSM) was used to improve the mechanical properties, scratch resistance and tribological performance of Cu-based bimetals, which are usually used to manufacture sliding bearings and bushings for internal combustion engines (ICEs). Two different Cu-based bimetals, namely CuPb10Sn10 and CuSn10Bi7, were sintered onto a low carbon steel substrate. The mechanical properties and dry tribological performance using a tensile tester and micro-tribo tester were evaluated, respectively. The scratch resistance was assessed using a micro-scratch tester at an incremental load. The tensile test results showed that the yield strength (YS) and ultimate tensile strength (UTS) of both Cu-based bimetals increased after UNSM. Furthermore, the scratch and tribological tests results revealed that the scratch resistance and tribological performance of both Cu-based bimetals were improved by the application of UNSM. These improvements were mainly attributed to the eliminated pores, increased hardness and reduced roughness after UNSM. CuSn10Bi7 demonstrated better mechanical properties, scratch resistance and tribological performance than CuPb10Sn10. It was found that the presence of Bi in CuSn10Bi7 formed a Cu11Bi7 intermetallic phase, which is harder than Cu3Sn. Hence, CuSn10Bi7 demonstrated higher strength and wear resistance than CuPb10Sn10. In addition, a CuSn10Bi7 formed both SnO2 and Bi2O3 that prevented adhesion and improved the tribological performance. It can be expected that under dry tribological conditions, ICEs can utilize UNSM bearings and bushings made of CuSn10Bi7 instead of CuPb10Sn10 under oil-lubricated conditions.
Abstract
In this study, an ultrasonic nanocrystal surface modification (UNSM) was used to improve the mechanical properties, scratch resistance and tribological performance of Cu-based bimetals, which are usually used to manufacture sliding bearings and bushings for internal combustion engines (ICEs). Two different Cu-based bimetals, namely CuPb10Sn10 and CuSn10Bi7, were sintered onto a low carbon steel substrate. The mechanical properties and dry tribological performance using a tensile tester and micro-tribo tester were evaluated, respectively. The scratch resistance was assessed using a micro-scratch tester at an incremental load. The tensile test results showed that the yield strength (YS) and ultimate tensile strength (UTS) of both Cu-based bimetals increased after UNSM. Furthermore, the scratch and tribological tests results revealed that the scratch resistance and tribological performance of both Cu-based bimetals were improved by the application of UNSM. These improvements were mainly attributed to the eliminated pores, increased hardness and reduced roughness after UNSM. CuSn10Bi7 demonstrated better mechanical properties, scratch resistance and tribological performance than CuPb10Sn10. It was found that the presence of Bi in CuSn10Bi7 formed a Cu11Bi7 intermetallic phase, which is harder than Cu3Sn. Hence, CuSn10Bi7 demonstrated higher strength and wear resistance than CuPb10Sn10. In addition, a CuSn10Bi7 formed both SnO2 and Bi2O3 that prevented adhesion and improved the tribological performance. It can be expected that under dry tribological conditions, ICEs can utilize UNSM bearings and bushings made of CuSn10Bi7 instead of CuPb10Sn10 under oil-lubricated conditions.
참고문헌 (12)
- Roy, R., "Detailed Cost Estimating in the Automotive Industry : Data and Information Requirements", Int. J. Prod. Econom (2011)[DOI]
- Xiong, X., "Friction and Wear Behaviors and Mechanisms of Fe and SiO2 in Cu-based P", M Friction Materials, 2007, ~
- Amanov, A., "Effects of Ultrasonic Nanocrystalline Srface Modification(UNSM)Technique on the Tribological Behavior of Sintered Cu-based Alloy", Tribol. Int (2014)[DOI]
- Arifvianto, B., "Effects of Surface Mechanical Attrition Treatment(SMAT)on a Rough Surface of AISI 316L Stainless Steel", Appl. Surf. Sci (2012)[DOI]
- Bagherifard, S., "On the Shot Peening Surface Coverage and Its Assessment by Means of Finite Element Simulation : A Critical Review and Some Original Developments", Appl. Surf. Sci (2012)[DOI]
- 노준석, "초음파나노표면개질기술로 제작된 마이크로 그루브가미끄럼 마찰 특성에 주는 영향", 한국트라이볼로지학회지, 37(1), pp.25~30 (2021), 한국트라이볼로지학회[DOI]
- 산성충호, "Selective Laser Melting 방식으로 적층가공된 Ti-6Al-4V 합금의 내마모성 특성에 미치는 고온 UNSM 처리 영향에 대한 연구", 한국트라이볼로지학회지, 36(1), pp.47~54 (2020), 한국트라이볼로지학회[DOI]
- Oliver, W. C., "An Improved Technique for Determining Hardness and Elastic Modulus using Load and Displacement Sensing Indentation Experiments", J. Mater. Res (1992)[DOI]
- Walsh, J. P. S., "High-pressure Synthesis : A New Frontier in the Search for Next-Generation Intermetallic Compound", Acc. Chem. Res (2018)[DOI]
- Amsler, M., "Dense Superconducting Phases of Copper-bismuth at High Pressure", Phys. Rev. Mater (2017)[DOI]
- Amanov, A., "Effect of Local Treatment Temperature of Ultrasonic Nanocrystalline Surface Modification on Tribological Behavior and Corrosion Resistance of Stainless Steel 316L Produced by Selective Laser Melting", Surf. Coat. Technol (2020)[DOI]
- Gencer, G. M., "Effect of the Surface Nanocrystallization on Tribological Behavior of the Cu based Bimetallic Materials(CuPbSn)", Mater. Res. Exp (2019)[DOI]