Sn-Sb-Cu-Ni-Cd whitemetal에서 Cu와 Sb가 미세조직과 기계적 특성에 미치는 영향
The effect of Cu and Sb on the microstructure and mechanical properties in Sn-Sb-Cu-Ni-Cd whitemetal
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The effects of Cu and Sb on the microstructure and mechanical properties of Sn-Sb-Cu-Ni-Cd whitemetal were investigated. Any compound phase was not observed in the whitemetal with 0.05 wt% Cu, while as the Cu content was increased, star- or needle-like Cu6Sn5 phases were found. The tensile strength gradually increased with Cu up to 5 % and then remained almost constant with Cu content above 5 %, while the hardness continuously increased with Cu content because of the increased hard Cu6Sn5 phases. As the Sb content increased, SbSn cuboids were present as well as Cu6Sn5. The tensile strength and hardness continuously increased and the elongation decreased with Sb content.
Abstract
The effects of Cu and Sb on the microstructure and mechanical properties of Sn-Sb-Cu-Ni-Cd whitemetal were investigated. Any compound phase was not observed in the whitemetal with 0.05 wt% Cu, while as the Cu content was increased, star- or needle-like Cu6Sn5 phases were found. The tensile strength gradually increased with Cu up to 5 % and then remained almost constant with Cu content above 5 %, while the hardness continuously increased with Cu content because of the increased hard Cu6Sn5 phases. As the Sb content increased, SbSn cuboids were present as well as Cu6Sn5. The tensile strength and hardness continuously increased and the elongation decreased with Sb content.
참고문헌 (7)
- K. Lepper, "Sliding behavior of selected aluminum alloys", Wear, 203-204, pp.46~ (1997)
- E. Booser, "Applied tribology bearing design and lubrication" (2001), Wiley
- H. Iliev, "Failure analysis of hydro-generator thrust bearing", Wear, 225-229, pp.913~ (1999)
- K. Tamura, "Effect of cyclic load and sliding speed on sliding wear characteristics of a bearing lined with WJ7 white metal", Proc. Inst. Mech. Eng. Part J J. Eng. Tribol, 218, pp.23~ (2004)
- M.J. Neale, "Bearings: a tribology handbook", pp.1993, Scotland, Butterworth
- C.J. Thwaites, "Tin and Tin Alloys", ASM Handbook ASM International, 9, pp.449~ (1985)
- T.B. Massalski, "Binary Alloy Phase Diagrams, 2", e, 1990, ~