X-선 회절 및 격자 매개변수를 이용한 biphasic calcium phosphate 분말의 생분 해성 특성평가
Characterization of the biodegradable behavior for biphasic calcium phosphates using X-ray diffraction and lattice parameter
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
합성된 biphasic calcium phosphate(BCP) 분말의 나노크기 생분해성 거동은 X-선 회절 분석방법, 격자 매개변수및 전계방출형 주사전자현미경을 통해 특성평가 하였다. BCP 분말은 공침반응 및 하소과정을 통해 합성하였고, 합성된 분말은 행크 용액(pH = 7.4, 36.5oC)을 이용하여 3주 동안 in vitro 시험 하였다. 분해 시험(in vitro) 후, BCP 단위포의 매개변수는 a 및 c축의 불규칙한 변화와 비슷한 격자 왜곡 및 팽창 거동을 보였다.
Abstract
Nanoscale-biodegradable behaviors of synthesized biphasic calcium phosphates (BCP) powders were characterized using X-ray diffraction (XRD), lattice parameter, and field emission microscopy (FE-SEM). The calcined BCP powders in vitro tested in Hank’s balanced salt solution (pH = 7.4, 36.5oC) for 3 weeks. The calculated unit cell parameters for BCP have shown lattice distortion and expansion as irregular changes in the a and c-axis after in vitro.
참고문헌 (9)
- 박광범, "미세다공성 Biphasic calcium phosphate ceramics의 골이식 대체재로서의 기본특성에 대한 비교연구", Journal of Periodontal & Implant Science, 36(4), pp.797~808 (2006), 대한치주과학회
- R.W. Bucholz, "Hydroxyapatite and tricalcium phosphate bone graft substitutes", Orthop. Clic. North Am, 18, pp.323~ (1987)
- W. Suchanek, "Processing and properties of hydroxyapatite-based biomaterials for use as hard tissue replacement implants", J. Mater. Res, 13, pp.94~ (1998)
- Y. Ota, "Bone formation following implantation of fibrous compounds (β-Ca(PO3)2, CaCO3(aragonite)) into bone marrow", J. Mater. Sci, 12, pp.895~ (2002)
- J.H. Kim, "Microstructural develpment in synthetic hydroxyapatite", J. Kor. Ceram. Soc, 41, pp.289~ (2004)
- D.J. Baek, "Fabrication of hydroxyapatite whiskers by hydrolysis of α-TCP", J. Kor. Ceram. Soc, 40, pp.608~ (2003)
- S.H. Kwon, "Synthesis and dissolution behavior of β-TCP and HA", β- TCP composite powders, 2003, pp.23, 1039~
- R. Xin, "A comparative study of calcium phosphate formation on bioceramics in vitro and in vivo", Biomaterials, 26, pp.6477~ (2005)
- S.-H. Kwon, "Synthesis and dissolution behavior of β-TCP and HA", β-TCP composite powders, 2003, pp.23, 1039~