Mechanical behavior and microstructural characterization of different zirconia polycrystals in different thicknesses
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
PURPOSE. To characterize the microstructure of three yttria partially stabilized zirconia ceramics and to compare their hardness, indentation fracture resistance (IFR), biaxial flexural strength (BFS), and fatigue flexural strength. MATERIALS AND METHODS. Disc-shaped specimens were obtained from 3Y-TZP (Vita YZ HT), 4Y-PSZ (Vita YZ ST) and 5Y-PSZ (Vita YZ XT), following the ISO 6872/2015 guidelines for BFS testing (final dimensions of 12 mm in diameter, 0.7 and 1.2 ± 0.1 mm in thicknesses). Energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD) and scanning electron microscopy (SEM) analyses were performed, and mechanical properties were assessed by Vickers hardness, IFR, quasi-static BFS and fatigue tests. RESULTS. All ceramics showed similar chemical compositions, but mainly differed in the amount of yttria, which was higher as the amount of cubic phase in the diffractogram (5Y-PSZ > 4Y-PSZ > 3Y-TZP). The 4Y- and 5Y-PSZ specimens showed surface defects under SEM, while 3Y-TZP exhibited greater grain uniformity on the surface. 5Y-PSZ and 3Y-TZP presented the highest hardness values, while 3Y-TZP was higher than 4Y- and 5Y-PSZ with regard to the IFR. The 5Y-PSZ specimen (0.7 and 1.2 mm) showed the worst mechanical performance (fatigue BFS and cycles until failure), while 3Y-TZP and 4Y-PSZ presented statistically similar values, higher than 5Y-PSZ for both thicknesses (0.7 and 1.2 mm). Moreover, 3Y-TZP showed the highest (1.2 mm group) and the lowest (0.7 mm group) degradation percentage, and 5Y-PSZ had higher strength degradation than 4Y-PSZ group. CONCLUSION. Despite the microstructural differences, 4Y-PSZ and 3Y-TZP had similar fatigue behavior regardless of thickness. 5Y-PSZ had the lowest mechanical performance.
Abstract
PURPOSE. To characterize the microstructure of three yttria partially stabilized zirconia ceramics and to compare their hardness, indentation fracture resistance (IFR), biaxial flexural strength (BFS), and fatigue flexural strength. MATERIALS AND METHODS. Disc-shaped specimens were obtained from 3Y-TZP (Vita YZ HT), 4Y-PSZ (Vita YZ ST) and 5Y-PSZ (Vita YZ XT), following the ISO 6872/2015 guidelines for BFS testing (final dimensions of 12 mm in diameter, 0.7 and 1.2 ± 0.1 mm in thicknesses). Energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD) and scanning electron microscopy (SEM) analyses were performed, and mechanical properties were assessed by Vickers hardness, IFR, quasi-static BFS and fatigue tests. RESULTS. All ceramics showed similar chemical compositions, but mainly differed in the amount of yttria, which was higher as the amount of cubic phase in the diffractogram (5Y-PSZ > 4Y-PSZ > 3Y-TZP). The 4Y- and 5Y-PSZ specimens showed surface defects under SEM, while 3Y-TZP exhibited greater grain uniformity on the surface. 5Y-PSZ and 3Y-TZP presented the highest hardness values, while 3Y-TZP was higher than 4Y- and 5Y-PSZ with regard to the IFR. The 5Y-PSZ specimen (0.7 and 1.2 mm) showed the worst mechanical performance (fatigue BFS and cycles until failure), while 3Y-TZP and 4Y-PSZ presented statistically similar values, higher than 5Y-PSZ for both thicknesses (0.7 and 1.2 mm). Moreover, 3Y-TZP showed the highest (1.2 mm group) and the lowest (0.7 mm group) degradation percentage, and 5Y-PSZ had higher strength degradation than 4Y-PSZ group. CONCLUSION. Despite the microstructural differences, 4Y-PSZ and 3Y-TZP had similar fatigue behavior regardless of thickness. 5Y-PSZ had the lowest mechanical performance.
참고문헌 (29)
- Denry I, "State of the art of zirconia for dental applications", Dent Mater, 24, pp.299~307 (2008)
- Zhang Y, "Making yttria-stabilized tetragonal zirconia translucent", Dent Mater, 30, pp.1195~1203 (2014)
- Husain Hatim Harianawala, "Comparative analysis of transmittance for different types of commercially available zirconia and lithium disilicate materials", The Journal of Advanced of Prosthodontics, 6(6), pp.456~461 (2014), 대한치과보철학회[DOI]
- Özkurt-Kayahan Z, "Monolithic zirconia : A review of the literature", Biomed Res, 27, pp.1427~1436 (2016)
- Kwon SJ, "Comparison of the mechanical properties of translucent zirconia and lithium disilicate", J Prosthet Dent, 120, pp.132~137 (2018)
- Zhang Y, "Novel zirconia materials in dentistry", J Dent Res, 97, pp.140~147 (2018)
- Ghodsi S, "A review on translucent zirconia", Eur J Prosthodont Restor Dent, 26, pp.62~74 (2018)
- Heffernan MJ, "Relative translucency of six all-ceramic systems. Part I: core materials", J Prosthet Dent, 88, pp.4~9 (2002)
- Vagkopoulou T, "Zirconia in dentistry: Part 1. Discovering the nature of an upcoming bioceramic", Eur J Esthet Dent, 4, pp.130~151 (2009)
- Nishioka G, "Fatigue strength of several dental ceramics indicated for CADCAM monolithic restorations", Braz Oral Res, 32, pp.e53~ (2018)
- Pereira GKR, "Low-temperature degradation of Y-TZP ceramics : A systematic review and meta-analysis", J Mech Behav Biomed Mater, 55, pp.151~163 (2015)
- Pereira GKR, "Mechanical reliability, fatigue strength and survival analysis of new polycrystalline translucent zirconia ceramics for monolithic restorations", J Mech Behav Biomed Mater, 85, pp.57~65 (2018)
- Kelly JR, "ADM guidance-ceramics : Fatigue principles and testing", Dent Mater, 33, pp.1192~1204 (2017)
- Suresh S, "Cambridge solid state science series" (1998), Series CSSS editor
- Yan J, "Load-bearing capacity of lithium disilicate and ultra-translucent zirconias", J Mech Behav Biomed Mater, 88, pp.170~175 (2018)
- Anstis GR, "A critical evaluation of indentation techniques for measuring fracture toughness: I, Direct crack measurements", J Am Ceram Soc, 64, pp.533~538 (1981)
- Belli R, "Mechanical fatigue degradation of ceramics versus resin composites for dental restorations", Dent Mater, 30, pp.424~432 (2014)
- Miyazaki T, "Current status of zirconia restoration", J Prosthodont Res, 57, pp.236~261 (2013)
- Jing Z, "Effect of multistep processing technique on the formation of micro-defects and residual stresses in zirconia dental restorations", J Prosthodont, 23, pp.206~212 (2014)
- Pecho OE, "Color and translucency of zirconia ceramics, human dentine and bovine dentine", J Dent, 40, pp.e34~e40 (2012)
- Kolakarnprasert N, "New multi-layered zirconias: Composition, microstructure and translucency", Dent Mater, 35, pp.797~806 (2019)
- Camposilvan E, "Aging resistance, mechanical properties and translucency of different yttria-stabilized zirconia ceramics for monolithic dental crown applications", Dent Mater, 34, pp.879~890 (2018)
- Sen N, "Microstructural, physical, and optical characterization of high-translucency zirconia ceramics", J Prosthet Dent, 123, pp.761~768 (2020)
- Arata A, "Quantitative phase analysis from X-ray diffraction in Y-TZP dental ceramics : a critical evaluation", J Dent, 42, pp.1487~1494 (2014)
- Chevalier J, "Critical effect of cubic phase on aging in 3 mol% yttria-stabilized zirconia ceramics for hip replacement prosthesis", Biomaterials, 25, pp.5539~5545 (2004)
- Inokoshi M, "Meta-analysis of bonding effectiveness to zirconia ceramics", J Dent Res, 93, pp.329~334 (2014)
- Johnson DL, "Microwave and plasma sintering of ceramics", Ceram Int, 17, pp.295~300 (1991)
- Tsukuma K, "Transparent 8mol% Y2O3-ZrO2(8Y)ceramics", J Am Ceram Soc, 91, pp.813~818 (2008)
- 김미진, "Effects of the sintering conditions of dental zirconia ceramics on the grain size and translucency", The Journal of Advanced of Prosthodontics, 5(2), pp.161~166 (2013), 대한치과보철학회[DOI]