Biaxial flexural strength and phase transformation of Ce-TZP/Al2O3 and Y-TZP core materials after thermocycling and mechanical loading
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
PURPOSE. The purpose of the present study was to evaluate the effect of thermocycling and mechanical loading on the biaxial flexural strength and the phase transformation of one Ce-TZP/Al2O3 and two Y-TZP core materials. MATERIALS AND METHODS. Thirty disc-shaped specimens were obtained from each material. The specimens were randomly divided into three groups (control, thermocycled, and mechanically loaded). Thermocycling was subjected in distilled water for 10000 cycles. Mechanical loading was subjected with 200 N loads at a frequency of 2 Hz for 100000 times. The mean biaxial flexural strength and phase transformation of the specimens were tested. The Weibull modulus, characteristic strength, 10%, 5% and 1% probabilities of failure were calculated using the biaxial flexural strength data. RESULTS. The characteristic strengths of Ce-TZP/Al2O3 specimens were significantly higher in all groups compared with the other tested materials (P<.001). Statistical results of X-ray diffraction showed that thermocycling and mechanical loading did not affect the monoclinic phase content of the materials. According to Raman spectroscopy results, at the same point and the same material, mechanical loading significantly affected the phase fraction of all materials (P<.05). CONCLUSION. It was concluded that thermocycling and mechanical loading did not show negative effect on the mean biaxial strength of the tested materials.
Abstract
PURPOSE. The purpose of the present study was to evaluate the effect of thermocycling and mechanical loading on the biaxial flexural strength and the phase transformation of one Ce-TZP/Al2O3 and two Y-TZP core materials. MATERIALS AND METHODS. Thirty disc-shaped specimens were obtained from each material. The specimens were randomly divided into three groups (control, thermocycled, and mechanically loaded). Thermocycling was subjected in distilled water for 10000 cycles. Mechanical loading was subjected with 200 N loads at a frequency of 2 Hz for 100000 times. The mean biaxial flexural strength and phase transformation of the specimens were tested. The Weibull modulus, characteristic strength, 10%, 5% and 1% probabilities of failure were calculated using the biaxial flexural strength data. RESULTS. The characteristic strengths of Ce-TZP/Al2O3 specimens were significantly higher in all groups compared with the other tested materials (P<.001). Statistical results of X-ray diffraction showed that thermocycling and mechanical loading did not affect the monoclinic phase content of the materials. According to Raman spectroscopy results, at the same point and the same material, mechanical loading significantly affected the phase fraction of all materials (P<.05). CONCLUSION. It was concluded that thermocycling and mechanical loading did not show negative effect on the mean biaxial strength of the tested materials.
참고문헌 (32)
- Cattani-Lorente M., "Low temperature degradation of a Y-TZP dental ceramic", Acta Biomater, 7, pp.858~865 (2011)
- Yilmaz H., "Effect of fatigue on biaxial flexural strength of bilayered porcelain", zirconia(Y-TZP)dental ceramics, 2011, pp.27, 786~795
- Piconi C., "Zirconia as a ceramic biomaterial", Biomaterials, 20, pp.1~25 (1999)
- Kohorst P., "Low-temperature degradation of different zirconia ceramics for dental applications", Acta Biomater, 8, pp.1213~1220 (2012)
- Yang G., "Investigation on strengthening and toughening mechanisms of Ce-TZP", Al2O3 nanocomposites, 2006, pp.37, 1969~1975
- Mangalaraja RV., "Effect of ceria on the physical, mechanical and thermal properties of yttria stabilized zirconia toughened alumina", Mater Sci Eng A, 343, pp.71~75 (2003)
- Nawa M., "Tough and strong Ce-TZP", Alumina nanocomposites doped with titania, 1998, pp.24, 497~506
- Ban S., "Reliability and properties of core materials for all-ceramic dental restorations", Jpn Dent Sci Rev, 44, pp.3~21 (2008)
- Tanaka K., "Phase stability after aging and its influence on pin-on-disk wear properties of Ce-TZP", Al2 O3 nanocomposite and conventional Y-TZP, 2003, pp.67, 200~207
- Nawa M., "The effect of TiO2 addition on strengthening and toughening in intragranular type of 12Ce-TZP", Al2 O3 nanocomposites, 1998, pp.18, 209~219
- Ban S., "Biaxial flexure strength and low temperature degradation of Ce-TZP", Al2 O3 nanocomposite and Y-TZP as dental restoratives, 2008, pp.87, 492~498
- Hirano M., "Fracture toughness, strength and Vickers hardness of yttria-ceria-doped tetragonal zirconia", alumina composites fabricated by hot isostatic pressing, 1992, pp.27, 3511~3518
- Fischer J., "Compatibility of machined Ce-TZP", Al2 O3 nanocomposite and a veneering ceramic, 2007, pp.23, 1500~1505
- Borchers L., "Influence of hydrothermal and mechanical conditions on the strength of zirconia", Acta Biomater, 6, pp.4547~4552 (2010)
- Perdigão J., "Degradation of dental ZrO2-based materials after hydrothermal fatigue. Part I : XRD, XRF, and FESEM analyses", Dent Mater J, 31, pp.256~265 (2012)
- Pittayachawan P., "The biaxial flexural strength and fatigue property of Lava Y-TZP dental ceramic", Dent Mater, 23, pp.1018~1029 (2007)
- Ban S., "Fracture toughness of dental zirconia before and after autoclaving", J Ceram Soc Jpn, 118, pp.406~409 (2010)
- Sato H., "Mechanical properties of dental zirconia ceramics changed with sandblasting and heat treatment", Dent Mater J, 27, pp.408~414 (2008)
- Nakamura T., "Mechanical properties of zirconia", alumina nano-composite after soaking in various water-based conditions, 2006, pp.309-11, 1219~1222
- Takano T., "Fatigue strength of Ce-TZP", Al2 O3 nanocomposite with different surfaces, 2012, pp.91, 800~804
- Gale MS., "Thermal cycling procedures for laboratory testing of dental restorations", J Dent, 27, pp.89~99 (1999)
- Fontijn-Tekamp FA., "Biting and chewing in overdentures, full dentures, and natural dentitions", J Dent Res, 79, pp.1519~1524 (2000)
- "ISO 6872. Dentistry-ceramic materials", International Organization for Standardization, ~ (2008)
- Garvie RC., "Phase analysis in zirconia systems", J Am Ceram Soc, 55, pp.303~305 (1972)
- Kim BK., "Quantitative phase analysis in tetragonal-rich tetragonal", monoclinic two phase zirconia by Raman spectroscopy, 1997, pp.16, 669~671
- Bona AD., "Weibull analysis and flexural strength of hot-pressed core and veneered ceramic structures", Dent Mater, 19, pp.662~669 (2003)
- Studart AR., "Fatigue of zirconia under cyclic loading in water and its implications for the design of dental bridges", Dent Mater, 23, pp.106~114 (2007)
- Karakoca S., "Influence of surface treatments on surface roughness, phase transformation, and biaxial flexural strength of Y-TZP ceramics", J Biomed Mater Res B Appl Biomater, 91, pp.930~937 (2009)
- Gupta TK., "Effect of stress-induced phase transformation on the properties of polycrystalline zirconia containing metastable tetragonal phase", J Mater Sci, 13, pp.1464~1470 (1978)
- Kailer A., "Raman microspectroscopy of nanocrystalline and amorphous phases in hardness indentations", J Raman Spectrosc, 30, pp.939~946 (1999)
- Behrens G., "On the isothermal martensitic transformation in 3Y-TZP", J Am Ceram Soc, 76, pp.1025~1030 (1993)
- Nemli SK, "Effect of fatigue on fracture toughness and phase transformation of Y-TZP ceramics by X-ray diffraction and Raman spectroscopy", J Biomed Mater Res B Appl Biomater (2011)