Effects of 3 different light-curing units on the physico-mechanical properties of bleach-shade resin composites
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Objectives: This study investigated the microhardness, flexural strength, and color stability of bleach-shade resin composites cured with 3 different light-curing units. Materials and methods: In this in vitro experimental study, 270 samples were fabricated of bleach and A2 shades of 3 commercial resin composites (Point 4, G-aenial Anterior, and Estelite Sigma Quick). Samples (n = 5 for each trial) were cured with Bluephase N, Woodpecker LED.D, and Optilux 501 units and underwent Vickers microhardness and flexural strength tests. The samples were tested after 24 hours of storage in distilled water. Color was assessed using a spectrophotometer immediately after preparation and 24 hours after curing. Data were analyzed using 3-way analysis of variance and the Tukey test (p ≤ 0.001). Results: Samples cured with Optilux exhibited the highest and those cured with LED.D exhibited the lowest microhardness (p = 0.023). The bleach shade of Point 4 composite cured with Optilux displayed the highest flexural strength, while the same composite and shade cured with Sigma Quick exhibited the lowest (p ≤ 0.001). The color change after 24 hours was greatest for the bleach shade of G-aenial cured with Bluephase N and least for the A2 shade of Sigma Quick cured with Optilux (p ≤ 0.001). Conclusions: Light curing with polywave light-emitting diode (LED) yielded results between or statistically similar to those of quartz-tungsten-halogen and monowave LED in the microhardness and flexural strength of both A2 and bleach shades of resin composites. However, the brands of light-curing devices showed significant differences in color stability.
Abstract
Objectives: This study investigated the microhardness, flexural strength, and color stability of bleach-shade resin composites cured with 3 different light-curing units. Materials and methods: In this in vitro experimental study, 270 samples were fabricated of bleach and A2 shades of 3 commercial resin composites (Point 4, G-aenial Anterior, and Estelite Sigma Quick). Samples (n = 5 for each trial) were cured with Bluephase N, Woodpecker LED.D, and Optilux 501 units and underwent Vickers microhardness and flexural strength tests. The samples were tested after 24 hours of storage in distilled water. Color was assessed using a spectrophotometer immediately after preparation and 24 hours after curing. Data were analyzed using 3-way analysis of variance and the Tukey test (p ≤ 0.001). Results: Samples cured with Optilux exhibited the highest and those cured with LED.D exhibited the lowest microhardness (p = 0.023). The bleach shade of Point 4 composite cured with Optilux displayed the highest flexural strength, while the same composite and shade cured with Sigma Quick exhibited the lowest (p ≤ 0.001). The color change after 24 hours was greatest for the bleach shade of G-aenial cured with Bluephase N and least for the A2 shade of Sigma Quick cured with Optilux (p ≤ 0.001). Conclusions: Light curing with polywave light-emitting diode (LED) yielded results between or statistically similar to those of quartz-tungsten-halogen and monowave LED in the microhardness and flexural strength of both A2 and bleach shades of resin composites. However, the brands of light-curing devices showed significant differences in color stability.
참고문헌 (35)
- Gomes GM, "Hardness of a bleaching-shade resin composite polymerized with different light-curing sources", Braz Oral Res, 20, pp.337~341 (2006)
- Alaghemand H, "Vickers hardness of composite resins cured with LED and QTH units", J Dent Biomater, 3, pp.192~198 (2016)
- Pahlevan A, "Effect of LED and argon laser on degree of conversion and temperature rise of hybrid and low shrinkage composite resins", Open Dent J, 10, pp.538~545 (2016)
- Pratap B, "Resin based restorative dental materials: characteristics and future perspectives", Jpn Dent Sci Rev, 55, pp.126~138 (2019)
- Manojlovic D, "Effect of resin and photoinitiator on color, translucency and color stability of conventional and low-shrinkage model composites", Dent Mater, 32, pp.183~191 (2016)
- Temel G, "Photopolymerization and photophysical properties of amine linked benzophenone photoinitiator for free radical polymerization", J Photochem Photobiol Chem, 219, pp.26~31 (2011)
- Lalevée J, "Photopolymerisation initiating systems" (2018), Royal Society of Chemistry
- de Oliveira DC, "Effect of different photoinitiators and reducing agents on cure efficiency and color stability of resin-based composites using different LED wavelengths", J Dent, 43, pp.1565~1572 (2015)
- Meereis CT, "BAPO as an alternative photoinitiator for the radical polymerization of dental resins", Dent Mater, 30, pp.945~953 (2014)
- Lima AF, "Increased rates of photopolymerisation by ternary type II photoinitiator systems in dental resins", J Mech Behav Biomed Mater, 98, pp.71~78 (2019)
- Hadis MA, "Competitive light absorbers in photoactive dental resin-based materials", Dent Mater, 28, pp.831~841 (2012)
- Lucey SM, "Degree of conversion of resin-based materials cured with dual-peak or single-peak LED light-curing units", Int J Paediatr Dent, 25, pp.93~102 (2015)
- Alpöz AR, "Effects of light curing method and exposure time on mechanical properties of resin based dental materials", Eur J Dent, 2, pp.37~42 (2008)
- Franco EB, "The effect of different light-curing units on tensile strength and microhardness of a composite resin", J Appl Oral Sci, 15, pp.470~474 (2007)
- Hubbezoğlu I, "Microhardness evaluation of resin composites polymerized by three different light sources", Dent Mater J, 26, pp.845~853 (2007)
- Domingos PA, "Composite resin color stability: influence of light sources and immersion media", J Appl Oral Sci, 19, pp.204~211 (2011)
- Yazici AR, "The effect of curing units and staining solutions on the color stability of resin composites", Oper Dent, 32, pp.616~622 (2007)
- Albuquerque PP, "Degree of conversion, depth of cure, and color stability of experimental dental composite formulated with camphorquinone and phenanthrenequinone photoinitiators", J Esthet Restor Dent, 27(Suppl 1), pp.S49~S57 (2015)
- Salgado VE, "Influence of photoinitiator system and nanofiller size on the optical properties and cure efficiency of model composites", Dent Mater, 30, pp.e264~e271 (2014)
- Salgado VE, "Effect of photoinitiator combinations on hardness, depth of cure, and color of model resin composites", J Esthet Restor Dent, 27(Suppl 1), pp.S41~S48 (2015)
- Price RB, "Knoop hardness of five composites cured with single-peak and polywave LED curing lights", Quintessence Int, 41, pp.e181~e191 (2010)
- Uhl A, "Photoinitiator dependent composite depth of cure and Knoop hardness with halogen and LED light curing units", Biomaterials, 24, pp.1787~1795 (2003)
- Miletic V, "Micro-Raman spectroscopic analysis of the degree of conversion of composite resins containing different initiators cured by polywave or monowave LED units", J Dent, 40, pp.106~113 (2012)
- Santini A, "Degree of conversion of resin-based orthodontic bonding materials cured with single-wave or dual-wave LED light-curing units", J Orthod, 41, pp.292~298 (2014)
- Santini A, "Degree of conversion and microhardness of TPO-containing resin-based composites cured by polywave and monowave LED units", J Dent, 40, pp.577~584 (2012)
- Sim JS, "Interaction of LED light with coinitiatorcontaining composite resins: effect of dual peaks", J Dent, 40, pp.836~842 (2012)
- "Ivoclar Vivadent" (2022)[URL]
- "Standard I" (2009)[URL]
- Brandt WC, "Influence of light-curing units on the flexural strength and flexural modulus of different resin composites", Braz J Oral Sci, 7, pp.1555~1558 (2008)
- Esmaeili B, "Hardness evaluation of composite resins cured with QTH and LED", J Dent Res Dent Clin Dent Prospect, 8, pp.40~44 (2014)
- Conte G, "Curing effectiveness of single-peak and multi-peak led light curing units on tpo-containing resin composites with different chromatic characteristics", Oral Implantol (Rome), 10, pp.140~150 (2017)
- Stahl F, "Light-emitting diode (LED) polymerisation of dental composites: flexural properties and polymerisation potential", Biomaterials, 21, pp.1379~1385 (2000)
- Massotti TG, "Analysis of flexural strength of composite resins polymerized by 2nd and 3rd generation leds", Braz Dent Sci, 18, pp.67~74 (2015)
- Sabatini C, "Color stability of ten resin-based restorative materials", J Esthet Restor Dent, 24, pp.185~199 (2012)
- de Almeida Souza MB, "Influence of different types of light curing units and photoinitiators in microhardness and color of composite resins after immersion in wine", Braz Dent Sci, 22, pp.371~377 (2019)