PURPOSE. The purpose of this study was to evaluate the properties of a porous zirconia scaffold coated with bioactive materials and compare the in vitro cellular behavior of MC3T3-E1 preosteoblastic cells to titanium and zirconia disks and porous zirconia scaffolds. MATERIALS AND METHODS. Titanium and zirconia disks were prepared. A porous zirconia scaffold was fabricated with an open cell polyurethane disk foam template. The porous zirconia scaffolds were coated with β-TCP, HA and a compound of β-TCP and HA (BCP). The characteristics of the specimens were evaluated using scanning electron microscopy (SEM), energy dispersive x-ray spectrometer (EDX), and x-ray diffractometry (XRD). The dissolution tests were analyzed by an inductively coupled plasma spectrometer (ICP). The osteogenic effect of MC3T3-E1 cells was assessed via cell counting and reverse transcriptase-polymerase chain reaction (RT-PCR). RESULTS. The EDX profiles showed the substrate of zirconia, which was surrounded by the Ca-P layer. In the dissolution test, dissolved Ca2+ ions were observed in the following decreasing order; β-TCP > BCP > HA (P<.05). In the cellular experiments, the cell proliferation on titanium disks appeared significantly lower in comparison to the other groups after 5 days (P<.05). The zirconia scaffolds had greater values than the zirconia disks (P<.05). The mRNA level of osteocalcin was highest on the non-coated zirconia scaffolds after 7 days. CONCLUSION. Zirconia had greater osteoblast cell activity than titanium. The interconnecting pores of the zirconia scaffolds showed enhanced proliferation and cell differentiation. The activity of osteoblast was more affected by microstructure than by coating materials.
Abstract
PURPOSE. The purpose of this study was to evaluate the properties of a porous zirconia scaffold coated with bioactive materials and compare the in vitro cellular behavior of MC3T3-E1 preosteoblastic cells to titanium and zirconia disks and porous zirconia scaffolds. MATERIALS AND METHODS. Titanium and zirconia disks were prepared. A porous zirconia scaffold was fabricated with an open cell polyurethane disk foam template. The porous zirconia scaffolds were coated with β-TCP, HA and a compound of β-TCP and HA (BCP). The characteristics of the specimens were evaluated using scanning electron microscopy (SEM), energy dispersive x-ray spectrometer (EDX), and x-ray diffractometry (XRD). The dissolution tests were analyzed by an inductively coupled plasma spectrometer (ICP). The osteogenic effect of MC3T3-E1 cells was assessed via cell counting and reverse transcriptase-polymerase chain reaction (RT-PCR). RESULTS. The EDX profiles showed the substrate of zirconia, which was surrounded by the Ca-P layer. In the dissolution test, dissolved Ca2+ ions were observed in the following decreasing order; β-TCP > BCP > HA (P<.05). In the cellular experiments, the cell proliferation on titanium disks appeared significantly lower in comparison to the other groups after 5 days (P<.05). The zirconia scaffolds had greater values than the zirconia disks (P<.05). The mRNA level of osteocalcin was highest on the non-coated zirconia scaffolds after 7 days. CONCLUSION. Zirconia had greater osteoblast cell activity than titanium. The interconnecting pores of the zirconia scaffolds showed enhanced proliferation and cell differentiation. The activity of osteoblast was more affected by microstructure than by coating materials.
참고문헌 (36)
- Hench LL., "Third-generation biomedical materials", Science, 295, pp.1014~1017 (2002)
- Fransson C., "Prevalence of subjects with progressive bone loss at implants", Clin Oral Implants Res, 16, pp.440~446 (2005)
- Klinge B., "Peri-implant marginal bone loss: an academic controversy or a clinical challenge?", Eur J Oral Implantol, 5, pp.S13~S19 (2012)
- Kim YK., "Autogenous teeth used for bone grafting: a comparison with traditional grafting materials", Oral Surg Oral Med Oral Pathol Oral Radiol, 117, pp.e39~e45 (2014)
- Bae JH., "Sinus bone graft using new alloplastic bone graft material (Osteon)-II: clinical evaluation", Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 109, pp.e14~e20 (2010)
- Dalkýz M., "Evaluation of the effects of different biomaterials on bone defects", Implant Dent, 9, pp.226~235 (2000)
- Carotenuto G., "Macroporous hydroxyapatite as alloplastic material for dental applications", J Mater Sci Mater Med, 10, pp.671~676 (1999)
- Lu J., "The biodegradation mechanism of calcium phosphate biomaterials in bone", J Biomed Mater Res, 63, pp.408~412 (2002)
- Chao SY., "Histologic study of tissue response to implanted hydroxylapatite in two patients", J Oral Maxillofac Surg, 45, pp.359~362 (1987)
- Frame JW., "Hydroxyapatite as a bone substitute in the jaws", Biomaterials, 2, pp.19~22 (1981)
- Daculsi G., "Transformation of biphasic calcium phosphate ceramics in vivo : ultrastructural and physicochemical characterization", J Biomed Mater Res, 23, pp.883~894 (1989)
- Nery EB., "Tissue response to biphasic calcium phosphate ceramic with different ratios of HA", beta TCP in periodontal osseous defects, 1992, pp.63, 729~735
- Gauthier O., "Macroporous biphasic calcium phosphate ceramics : influence of macropore diameter and macroporosity percentage on bone ingrowth", Biomaterials, 19, pp.133~139 (1998)
- Daculsi G., "Macroporous calcium phosphate ceramic for long bone surgery in humans and dogs. Clinical and histological study", J Biomed Mater Res, 24, pp.379~396 (1990)
- Jiang G., "Coating of hydroxyapatite on highly porous Al2O3 substrate for bone substitutes", J Biomed Mater Res, 43, pp.77~81 (1998)
- 배아란, "Cellular attachment and gene expression of osteoblast-like cells on zirconia ceramic surfaces", 대한치과보철학회지, 46(3), pp.227~237 (2008), 대한치과보철학회
- Guazzato M., "Influence of surface and heat treatments on the flexural strength of Y-TZP dental ceramic", J Dent, 33, pp.9~18 (2005)
- Piconi C., "Zirconia as a ceramic biomaterial", Biomaterials, 20, pp.1~25 (1999)
- Piconi C., "Y-TZP ceramics for artificial joint replacements", Biomaterials, 19, pp.1489~1494 (1998)
- Sollazzo V., "Zirconium oxide coating improves implant osseointegration in vivo", Dent Mater, 24, pp.357~361 (2008)
- Schultze-Mosgau S., "Osseointegration of endodontic endosseous cones : zirconium oxide vs titanium", Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 89, pp.91~98 (2000)
- Albrektsson T., "The long-term efficacy of currently used dental implants : a review and proposed criteria of success", Int J Oral Maxillofac Implants, 1, pp.11~25 (1986)
- Andreiotelli M., "Are ceramic implants a viable alternative to titanium implants? A systematic literature review", Clin Oral Implants Res, 20, pp.32~47 (2009)
- McKinney RV Jr., "The biologic response to the single-crystal sapphire endosteal dental implant : scanning electron microscopic observations", J Prosthet Dent, 51, pp.372~379 (1984)
- Vagkopoulou T., "Zirconia in dentistry : Part 1. Discovering the nature of an upcoming bioceramic", Eur J Esthet Dent, 4, pp.130~151 (2009)
- Wohlfahrt JC., "Porous titanium granules in the surgical treatment of peri-implant osseous defects : a randomized clinical trial", Int J Oral Maxillofac Implants, 27, pp.401~410 (2012)
- Steinemann SG., "Titanium--the material of choice?", Periodontol 2000, 17, pp.7~21 (1998)
- Langhoff JD., "Comparison of chemically and pharmaceutically modified titanium and zirconia implant surfaces in dentistry : a study in sheep", Int J Oral Maxillofac Surg, 37, pp.1125~1132 (2008)
- Itälä AI., "Pore diameter of more than 100 microm is not requisite for bone ingrowth in rabbits", J Biomed Mater Res, 58, pp.679~683 (2001)
- Aboushelib MN., "Influence of surface nano-roughness on osseointegration of zirconia implants in rabbit femur heads using selective infiltration etching technique", J Oral Implantol, 39, pp.583~590 (2013)
- Sudo H., "In vitro differentiation and calcification in a new clonal osteogenic cell line derived from newborn mouse calvaria", J Cell Biol, 96, pp.191~198 (1983)
- Wang D., "Isolation and characterization of MC3T3-E1 preosteoblast subclones with distinct in vitro and in vivo differentiation", mineralization potential, 1999, pp.14, 893~903
- Pae A., "Attachment and growth behaviour of human gingival fibroblasts on titanium and zirconia ceramic surfaces", Biomed Mater, 4, pp.025005~ (2009)
- Tai G., "Use of green fluorescent fusion protein to track activation of the transcription factor osterix during early osteoblast differentiation", Biochem Biophys Res Commun, 333, pp.1116~1122 (2005)
- Franceschi RT., "Regulation of the osteoblast-specific transcription factor, Runx2 : responsiveness to multiple signal transduction pathways", J Cell Biochem, 88, pp.446~454 (2003)
- Barrère F., "Osteogenecity of octacalcium phosphate coatings applied on porous metal implants", J Biomed Mater Res A, 66, pp.779~788 (2003)