In vitro evaluation of the bond strength between various ceramics and cobalt-chromium alloy fabricated by selective laser sintering
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
PURPOSE. This study aimed to present the clinical applicability of restorations fabricated by a new method, by comparing the bond strength of between ceramic powder with different coefficient of thermal expansion and alloys fabricated by Selective laser sintering (SLS). MATERIALS AND METHODS. Fifty Co-Cr alloy specimens (25.0 × 3.0 × 0.5 mm) were prepared by SLS and fired with the ceramic (8.0 × 3.0 × 0.5 mm) (ISO 9693:1999). For comparison, ceramics with different coefficient of thermal expansion were used. The bond strength was measured by three-point bending testing and surfaces were observed with FE-SEM. Results were analyzed with a one-way ANOVA (α=.05). RESULTS. The mean values of Duceram Kiss (61.18 ± 6.86 MPa), Vita VM13 (60.30 ± 7.14 MPa), Ceramco 3 (58.87 ± 5.33 MPa), Noritake EX-3 (55.86 ± 7.53 MPa), and Vintage MP (55.15 ± 7.53 MPa) were found. No significant difference was observed between the bond strengths of the various metal-ceramics. The surfaces of the specimens possessed minute gaps between the additive manufactured layers. CONCLUSION. All the five powders have bond strengths higher than the required 25 MPa minimum (ISO 9693); therefore, various powders can be applied to metal structures fabricated by SLS.
Abstract
PURPOSE. This study aimed to present the clinical applicability of restorations fabricated by a new method, by comparing the bond strength of between ceramic powder with different coefficient of thermal expansion and alloys fabricated by Selective laser sintering (SLS). MATERIALS AND METHODS. Fifty Co-Cr alloy specimens (25.0 × 3.0 × 0.5 mm) were prepared by SLS and fired with the ceramic (8.0 × 3.0 × 0.5 mm) (ISO 9693:1999). For comparison, ceramics with different coefficient of thermal expansion were used. The bond strength was measured by three-point bending testing and surfaces were observed with FE-SEM. Results were analyzed with a one-way ANOVA (α=.05). RESULTS. The mean values of Duceram Kiss (61.18 ± 6.86 MPa), Vita VM13 (60.30 ± 7.14 MPa), Ceramco 3 (58.87 ± 5.33 MPa), Noritake EX-3 (55.86 ± 7.53 MPa), and Vintage MP (55.15 ± 7.53 MPa) were found. No significant difference was observed between the bond strengths of the various metal-ceramics. The surfaces of the specimens possessed minute gaps between the additive manufactured layers. CONCLUSION. All the five powders have bond strengths higher than the required 25 MPa minimum (ISO 9693); therefore, various powders can be applied to metal structures fabricated by SLS.
참고문헌 (25)
- van Noort R, "The future of dental devices is digital", Dent Mater, 28, pp.3~12 (2012)
- Moldovan O, "Threedimensional fit of CAD", CAM-made zirconia copings, 2011, pp.27, 1273~1278
- Wu L, "Evaluation of the mechanical properties and porcelain bond strength of cobalt-chromium dental alloy fabricated by selective laser melting", J Prosthet Dent, 111, pp.51~55 (2014)
- Deckard CR, "Method and apparatus for producing parts by selective sintering", United States Patent. US4863538 A, ~ (1989)
- Feygin M, "Apparatus and method for forming an integral object from laminations", United States Patent US5354414 A, ~ (1994)
- Nieva N, "Bonding strength evaluation on metal", ceramic interfaces in dental materials, 2012, pp.1, 475~482
- Donovan TE, "Porcelain-fused-to-metal (PFM) alternatives", J Esthet Restor Dent, 21, pp.4~6 (2009)
- Wataha JC, "Alloys for prosthodontic restorations", J Prosthet Dent, 87, pp.351~363 (2002)
- Zinelis S, "Thermal expansion and microstructural analysis of experimental metal-ceramic titanium alloys", J Prosthet Dent, 90, pp.332~338 (2003)
- Reyes MJ, "Titanium-porcelain system. Part III: effects of surface modification on bond strengths", Biomed Mater Eng, 11, pp.117~136 (2001)
- Steiner PJ, "Compatibility of ceramic-ceramic systems for fixed prosthodontics", Int J Prosthodont, 10, pp.375~380 (1997)
- Craig RG, "Restorative dental materials" (1997), Mosby
- Al Amri MD, "Shear bond strength of two forms of opaque porcelain to the metal substructure", King Saud Univ J Dent Sci, 3, pp.41~48 (2012)
- Barizon KT, "Ceramic materials for porcelain veneers:part II. Effect of material, shade, and thickness on translucency", J Prosthet Dent, 112, pp.864~870 (2014)
- Wang CH, "Fracture resistance of different metal substructure designs for implant-supported porcelain-fused-to-metal (PFM)crowns", J Dent Sci, 8, pp.314~320 (2013)
- Souza JC, "Mechanical and chemical analyses across dental porcelain fused to CP titanium or Ti6Al4V", Mater Sci Eng C Mater Biol Appl, 37, pp.76~83 (2014)
- "e-Manufacturing Solutions. Instructions for use: EOS Cobalt Chrome SP2" (2011)[URL]
- "ISO 9693. Metal-ceramic dental restorative systems", International Organization for Standardization, ~ (1999)
- Lei YC, "The influence of different thermal expansion coefficient (TEC) between ceramic and metal on thermal stability of porcelain-fused-to-metal (PFM) crown", Zhonghua Kou Qiang Yi Xue Za Zhi, 26, pp.329~332 (1991)
- Korkmaz T, "Comparative evaluation of bond strength of various metal-ceramic restorations", Mater Des, 30, pp.445~451 (2009)
- Joias RM, "Shear bond strength of a ceramic to Co-Cr alloys", J Prosthet Dent, 99, pp.54~59 (2008)
- Külünk T, "Effect of different air-abrasion particles on metal-ceramic bond strength", J Dent Sci, 6, pp.140~146 (2011)
- 배은정, "Bond and fracture strength of metalceramic restorations formed by selective laser sintering", The Journal of Advanced of Prosthodontics, 6(4), pp.266~271 (2014), 대한치과보철학회[DOI]
- Liu Y, "Evaluation of mechanical properties and porcelain bonded strength of nickel-chromium dental alloy fabricated by laser rapid forming", Lasers Med Sci, 25, pp.799~804 (2010)
- de Melo RM, "Shear bond strengths of a ceramic system to alternative metal alloys", J Prosthet Dent, 93, pp.64~69 (2005)